A thorough characterization of base materials is the prereq- uisite for further research. In this paper, the characterization data of the reference materials (CEM I 42.5 R, limestone pow- der, calcined clay and a mixture of these three components) used in the second funding phase of the priority program 2005 of the German Research Foundation (DFG SPP 2005) are presented under the aspects of chemical and min- eralogical composition as well as physical and chemical properties. The data were collected based on tests performed by up to eleven research groups involved in this cooperative program.
Moiré fringes for misfit measurements at incoherent y/y'-interfaces of nickel-base superalloys
(1998)
α(1 0 0) Dislocations are observed in nickel-base superalloys after creep deformation at high temperatures and low stresses. They are formed in the γ/γ´ interfaces by a three step mechanism. First, primary dislocations with Burgers vector α/2(1 0 1) and 60° character are left behind in the interfaces when dislocation loops glide through the γ channels. The 60° dislocations move into edge orientation and react forming secondary dislocations α/2(1 1 0). In the third step, new primary dislocations are knit into the already existing meshes of primary and secondary dislocations, which results in hexagonal misfit dislocation networks consisting of secondary dislocations α/2(1 1 0) and tertiary dislocations α(1 0 0), both of edge type. This self-organisation process is explained by dislocation theory and crystallography.
Creep deformation accelerates when the α(1 0 0) interfacial dislocations enter the γ´ phase. During their climb towards the opposite interface, they attain a characteristic rectangular shape. This shape and the importance of the α(1 0 0) super dislocations for creep deformation are discussed.