A set of compound refractive lenses (CRLs), mounted on a silicon wafer, was obtained from the Institut für Mikrostrukturtechnik Karlsruhe. The CRLs were characterized at the BAMline at the synchrotron BESSYII in Berlin. It could be demonstrated that beam diameters below 1 µm can be obtained. The beam size accepted by the lenses is (140 × 140) µm2, thus the intensity gain in the micrometer spot, including absorption, is about 15,000. It is possible to switch between different beam energies within a few minutes. First results of scans and the application of the lenses for MicroXANES (X-ray absorption near-edge structure) measurements are presented in this paper. Also, the possibility of MicroEXAFS (extended X-ray absorption fine structure) measurements is discussed.
Fire-gilding is a historic technique for the application of golden layers on a number of different base materials utilizing a gold amalgam. This technique leaves a significant amount of Hg in the golden layer, giving archeometrists a reliable indicator to identify firegildings.
Recent findings on presumably fire-gilded objects have shown in several cases significantly lower Hg content than previously studied objects. This prompted a synchrotron-based X-ray fluorescence investigation into the Hg distribution along the material–gilding interface, as well as a series of measurements regarding the Hg content development in fire-gilded samples during artificial aging. This work presents findings on laboratory-prepared fire-gildings, indicating an Hg enrichment at the interface of firegilded silver samples. Notably, such an enrichment is missing in fire-gilded copper samples. Further, it is confirmed that fire-gilded layers typically do not undercut an Hg bulk content of 5%. In this light, it seems improbable that ancient samples that contain <5% Hg are fire-gilded. The results presented in this study might lead to a non-destructive method to identify the Hg enrichment at the interface. This might be obtained by a combination of different non-destructive measurements and might also work unambiguously in samples in which the gold top layer is altered.
Fire-gilding or amalgam gilding is a historical technique for the gilding of objects. The object to be gilded is coated with an amalgam (a solution of gold (Au) in mercury (Hg)). By heating, the largest part of the Hg is subsequently evaporated and there remains a gold layer, containing still detectable amounts of Hg.
The information on the used gilding technique might be crucial for the conservation and preservation of archaeological objects. Therefore, the main objective of this work is the detailed understanding of the behaviour of Hg under conditions of fire gilding. I.e. the understanding of the diffusion and evaporating behaviour of Hg, depending on parameters like substrate material (silver, copper, bronze, brass...), heating temperature and duration, and the resulting Hg depth profiles under these conditions. Secondary objective is the establishment of a measurement protocol for the unambiguous identification of different types of gilding, based solely on non-destructive methods, which can be applied to historical samples.
In a first step, fire-gilded samples have been prepared on Cu and Ag sheet metal, respectively. Some of the gildings were produced by a professional goldsmith; another set of samples was produced under laboratory conditions. These samples have been examined with NAA (neutron activation analysis) and SR-XRF (synchrotron radiation induced X-ray fluorescence). First results of these measurements will be presented and discussed.