Filtern
Dokumenttyp
- Forschungsdatensatz (2)
- Beitrag zu einem Tagungsband (1)
- Vortrag (1)
Sprache
- Englisch (4)
Referierte Publikation
- nein (4)
Schlagworte
- Bridge (2)
- Civil engineering (2)
- Corrosion (2)
- Durability assessment (2)
- Nondestructive testing (2)
- Compressive Concrete Strength (1)
- Compressive concrete strength (1)
- Interlaboratory comparison (1)
- Non-destructive testing (1)
- Rebound Hammer (1)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (4) (entfernen)
Eingeladener Vortrag
- nein (1)
Corrosion of concrete reinforcement is one of the major damage mechanisms affecting both the load-bearing capacity and the serviceability of re-inforced concrete structures significantly. When externally discernible damages are observed during visual inspections on the structure, the extent of the damage inside the concrete is often already significant. Corrosion caused by carbonation often leads to severe discoloration of the surface or even large-area spalling of the concrete cover. In contrast, chloride-induced corrosion is usually difficult to observe visually but can cause much more serious damage in less time. The effect occurs locally and can lead to weakening of the cross-section of the reinforce-ment. This, in turn, can cause sudden structural collapses without prior notice.
In the meanwhile, various non-destructive and minimally invasive testing methods are available to evaluate the resistance to penetration of corrosion-pro-moting pollutants and to detect active corrosion. In this paper, a bridge crossing the river Regen is used as a case-study to demonstrate how the information ob-tained applying different testing methods can be combined and evaluated in the context of structural reassessments. Both the results of the permeability testing and the electrical resistance measurement are considered, as well as active corro-sion areas are localized using the half-cell potential mapping combined with the concrete cover measurement with the eddy current method and ground penetrat-ing radar. The results are evaluated using drill cores and in addition laser-induced breakdown spectroscopy was applied to obtain information about possible chlo-ride ion transport into the concrete.
Corrosion of concrete reinforcement is one of the major damage mechanisms affecting both the load-bearing capacity and the serviceability of reinforced concrete structures significantly. The challenge of detecting corrosion is that the corrosion process in its various forms is not immediately visible, especially in the corrosion initiation phase inside the concrete. When externally discernible damages are observed during visual inspections on the structure, the extent of the damage inside the concrete is often already significant. Corrosion caused by carbonation often leads to severe discoloration of the surface or even large-area spalling of the concrete cover. In contrast, chloride-induced corrosion is usually difficult to observe visually, but can cause much more serious damage in less time. The effect occurs locally and can lead to weakening of the cross-section of the reinforcement. This, in turn, can cause sudden structural collapses without prior notice. Therefore, it is important to investigate whether there is protection against corrosion of the reinforcement in the concrete and to detect active corrosion in the structure at an early stage.
In the meanwhile, various non-destructive and minimally invasive testing methods are available to evaluate the resistance to penetration of corrosion-promoting pollutants and to detect active corrosion. In this paper, a bridge crossing the river Regen (Germany) is used as a case-study to demonstrate how the information obtained applying different testing methods can be combined and evaluated in the context of structural reassessments. Both the results of the permeability testing (Torrent tester) and the electrical resistance measurement (Wenner probe) are considered, as well as active corrosion areas are localized using the half-cell potential mapping combined with the concrete cover measurement with the eddy current method and ground penetrating radar (GPR). The results are evaluated using drill cores and in addition laser-induced breakdown spectroscopy (LIBS) was applied to obtain information about possible ion transport in the concrete.
This data set contains three different data types obtained from concrete specimens. For each specimen, the rebound numbers, ultrasonic data (ultrasonic velocity, time of flight), and destructive concrete strength are given. Two kind of specimen geometries were tested: cubes and drilled cores. The files are labeled according to the specimen geometry as "cube" or "core" and the type of measurement data as "compressive_strength", "rn_R" and "rn_Q" for rebound numbers as well as "us" for ultrasonic data. The ultrasonic data were generated by six independent laboratories, the rebound numbers by five independent laboratories and the destructive tests by one laboratory. The designation of each specimen establishes the relationship between the different data types.
"This data set contains three different data types obtained from concrete specimens. For each specimen, the rebound numbers, ultrasonic data (ultrasonic velocity, time of flight), and destructive concrete strength are given. Two kind of specimen geometries were tested: cubes and drilled cores. The files are labeled according to the specimen geometry as "cube" or "core" and the type of measurement data as "compressive_strength", "rn_R" and "rn_Q" for rebound numbers as well as "us" for ultrasonic data. The ultrasonic data were generated by six independent laboratories, the rebound numbers by five independent laboratories and the destructive tests by one laboratory. The designation of each specimen establishes the relationship between the different data types."