Underwater plasma and glow discharge electrolysis are interesting new methods for polymer surface functionalization. The achievable content of O-containing functional groups exceeds that of oxygen glow discharge gas plasmas by a factor of two (up to ca. 56 O/100 C). The percentage of OH groups among all O-containing groups can reach 25 to 40%, whereas it is about 10% in the gas plasmas. Addition of hydrogen peroxide increases the fraction of OH groups to at most 70% (27 OH/100 C). The liquid plasma systems are also able to polymerize acrylic acid and deposit the polymer as very thin film on substrate surfaces or membranes, thereby retaining about 80% of all COOH functional groups (27 COOH/100 C).
Thin metal-filled polyterafluoroethylene films with various metal concentration were produced by co-deposition in vacuum. Metal nanocluster size increased with metal concentration. Films were heated up to 300 degrees C, their optical spectra were recorded during heating. The changes in plasmon band shape and wavelength of the nanocluster ensemble during heating are not linearly related with metal concentration and heating temperature. This is caused by different thermal behavior of the complex processes, which are taking place in each of the two materials present in the film. The metal cluster size and optical properties of the whole ensemble can be purposefully formed by varying metal nature, its concentration and annealing temperature of the film. Nano- and micro-domains with properties different from original film were generated by focused excimer laser or electron beam. Gold-filled PTFE nano-structured films were used as substrate for surface enhanced Raman scattering measurements of ultrathin film of Rhodamine 6G dye.
Polyolefins are chemically inert and do not adhere well to metals, polymers or inorganics. To overcome this problem, polyolefin surfaces were modified thermally, plasmachemically, or by flame treatment with different oxygen-containing groups, however, unfortunately, such treatments were accompanied by undesired, adhesion lowering polymer degradation. To solve this dilemma, solutions of synthetic polymers and copolymers were prepared, sprayed into the barrier discharge or electrosprayed without discharge and deposited as thin adhesion-promoting layers. The deposited polymer layers from poly(vinylamine), poly(ethylene glycol)-poly(vinyl alcohol) copolymers and poly(acrylic acid) were endowed with monotype functional groups. Using the aerosol - dielectric barrier discharge only a fraction of functional groups survived the deposition process in contrast to the electrospray in which all functional groups were retained.
Nebulizing of polymer solutions, in a high-voltage field under atmospheric conditions by electrospray ionization (ESI), is a comfortable way to deposit ultra-thin layers of polar or ionic polymers onto any conductive substrate materials. The substrate is grounded and the polymer solution is sprayed through a powered capillary. The formed charged droplets shrink by solvent evaporation during their way to the grounded substrate, the charges close ranks and the droplets collapse consecutively by charge repulsion, thus forming finally charged single macromolecules. After their discharging at the grounded substrate, an ultrathin ‘quasi-monomolecular’ polymer layer is formed. It could be shown by imaging of scratches through the polymer layer by atomic force microscopy that the deposited polymer layers are dense at a thickness of about 10 nm. Carbon fibre bundles were coated with poly (allylamine) (PAAm) or poly(acrylic acid) (PAA) as potential adhesion-promoting layers in fibre–polymer composites. The polymer deposition is self-inhibiting after formation of a continuous coverage of about 200 nm for PAAm and 30 nm for PAA as result of surface charging. Continuous deposition onto such isolating layers or polymers without charging can be achieved by using current of alternating polarity. The film formation is self-healing because of the electrophoretic effect, i.e. the ion discharging occurs preferentially at noncoated areas. This electrophoretic effect of ESI was demonstrated by completely enwrapping all the carbon fibres of the roving within a distance of about 100 μm far from its outside and also at the backside of the fibre bundle with about 80% of the topside coverage, as measured by X-ray photoelectron spectroscopy and visualized using scanning electron microscopy.
Polymer deposition morphology by electrospray deposition - Modifications through distance variation
(2014)
Electrospray deposition (ESD) of highly diluted polymers was examined with regard to the deposited surface structure. Only the flight distance (flight time) onto the resulting deposited surface was varied from 20 to 200 mm.
An apparatus without any additional heating or gas flows was used. Polyacrylic acid (PAA) and polyallylamine (PAAm) in methanol were deposited on Si wafers. The polymer layers were characterized by scanning electron microscopy, X-ray photoelectron spectroscopy, derivatization reactions and Fourier transform infrared spectroscopy using a grazing incidence unit.
SEM images illustrated the changing structures of PAA and PAAm. For PAA the deposited structure changed from a smooth film (20 mm) to a film with individual droplets on the coated surface (100 mm and 200 mm), while for PAAm individual droplets can be seen at all distances. The ESD process with cascades of splitting droplets slows down for PAA after distances greater than 40 mm. In contrast, the ESD process for PAAm is nearly stopped within the first flight distance of 20 mm. Residual solvent analysis showed that most of the solvent evaporated within the first 20 mm capillary-sample distance.
Die Elektrospray-Ionisations (ESI)-Vernebelung von Polymerlösungen wird analytisch zur massenspektrometrischen Bestimmung der Molmassen von Makromolekülen genutzt. Dabei werden die Polymermoleküle nach einem speziellen Mechanismus im Hochspannungsfeld unter Normaldruckbedingungen vereinzelt und in das Massenspektrometer überführt. Dieser Prozeß kann auch zur flächigen Abscheidung einzelner Polymermoleküle genutzt werden. Die Struktur und Zusammensetzung sowie die Molmassenverteilung der Polymere bleiben dabei erhalten. Schichten polarer oder ionischer Polymere der Dicke einer Quasi-Monolage bis hin zu mehreren 100 Nanometern können abgeschieden werden. Erwähnenswert ist, daß der ESI-Prozeß zu den elektrophoretischen Verfahren gehört, was die Ausbildung lochfreier Schichten auf elektrisch leitenden Substraten nicht nur auf der der Spraydüse zugewandten Seite ermöglicht, sondern auch auf der abgeschatteten Rückseite. Dieses Verhalten wurde zur vollständigen ESI-Umhüllung von dichtgepackten Kohlenstoff-Faser-Bündeln mit haftvermittelnden Polymerschichten ausgenutzt.