The systematic transfer of solvent-free, additive flame retardant (FR) formulations from epoxy resins to glass fiber-reinforced epoxy composites (GFRECs) through prepregs is difficult. Additionally, obtaining data on their post-fire mechanics is often challenging. Utilizing melamine polyphosphate (MPP), ammonium polyphosphate (APP), and silane-coated ammonium polyphosphate (SiAPP) FRs with low-melting inorganic silicates (InSi) in an 8:2 proportion and 10% loading by weight in a diglycidyl ether of bisphenol A (DGEBA) resin, a systematic investigation of the processing properties, room-temperature mechanics, and temperature-based mechanics of the systems was performed. The resin was cured with a dicyandiamide hardener (DICY) and a urone accelerator. The results revealed no substantial impact of these FRs at the current loading on the resin's glass transition temperature or processability. However, the fire residues from cone calorimetry tests of the composites containing FRs were found to be only 15-20% of the thickness of the resins, implying a suppression of intumescence upon transfer. At room temperature, the decrease in the flexural modulus for the composites containing FRs was negligible. Exposure of the composites in a furnace at 400°C as a preliminary study before ignition tests was shown to cause significant flexural moduli reductions after 2.5 min of exposure and complete delamination after 3 min making further testing unviable. This study emphasizes the need for future research on recovering modes of action upon transfer of FR formulations from resins to composites. Based on the challenges outlined in this investigation, sample adaptation methods for post-fire analysis will be developed in a future study.
The transfer of flame-retardant epoxy resin formulations to composites for structural and lightweight applications in the energy and transport sector can be complex and requires systematic investigation. Here, uncoated and silane-coated ammonium polyphosphate (APP, Si-APP) intumescent compounds are transferred to prepregs using a Bisphenol A diglycidyl ether (DGEBA) resin matrix to 0/90o bidirectional glass fibers with an aerial weight of 600 g/m2. Inorganic silicates (InSi) are added to improve the fire residues of the composites after combustion and the total amount of flame retardants in the resin formulations was 10% by weight. The prepregs' fiber volume content (FVC) is corroborated using in-process measurements and thermogravimetric analysis. This was found to be approximately 60% for the composites containing APP, which is ideal for load-bearing applications with high mechanical strength. However, the Si-APP containing prepregs showed an inconsistent FVC potentially due to interactions with the commercial sizing of the glass fibers. The composites subsequently prepared are analysed for potential filtration effects of the additives via SEM after immobilization in a cured resin and platinum sputtering. The inter-laminar shear strength and the mechanical strength of the composites are compared via three-point bending tests. Additionally, the fire performance of the composites is analysed using cone calorimetry. It was found there was minimal impact of the loading of the flame retardants on the delamination of the composites and the flexural strength. However, the high density of the glass fibers possibly results in a suppression of the mode of action of the flame retardants in the composites. Therefore, the fire residues of the composites are further compared using SEM, and the flame-retardant modes of action upon transfer are investigated.
The residual post-fire mechanical properties of fiber-reinforced epoxy composites are influenced by their fire residues after burning. This study uses intumescent/low-melting glass flame retardants to tailor fire residues in epoxy resin. Processibility of prepregs and their quality are analysed for transfer of the flame-retardant epoxy resins to layered glass-fiber reinforced composites. Minimal effects were found on the pre-fire flexural strengths of the composites due to low loading of the flame retardants. However, when transferred to glass-fiber reinforced composites, the fire residues diminish significantly. Further studies are required to improve theoretical and experimental estimations of the post-fire mechanics of the composites.
The residual post-fire mechanical properties of fiber-reinforced epoxy composites are influenced by their fire residues after burning. This study uses intumescent/low-melting glass flame retardants to tailor fire residues in epoxy resin. Processibility of prepregs and their quality are analysed for transfer of the flame-retardant epoxy resins to layered glass-fiber reinforced composites. Minimal effects were found on the pre-fire flexural strengths of the composites due to low loading of the flame retardants. However, when transferred to glass-fiber reinforced composites, the fire residues diminish significantly. Further studies are required to improve theoretical and experimental estimations of the post-fire mechanics of the composites.