Filtern
Dokumenttyp
- Vortrag (35)
- Posterpräsentation (16)
- Beitrag zu einem Tagungsband (13)
- Zeitschriftenartikel (3)
- Dissertation (1)
- Forschungsbericht (1)
Referierte Publikation
- nein (69) (entfernen)
Schlagworte
- KorroPad (34)
- Korrosion (32)
- Nichtrostender Stahl (31)
- EPR (21)
- Wärmebehandlung (20)
- Corrosion resistance (17)
- Korrosionsbeständigkeit (16)
- Lochkorrosion (16)
- Heat treatment (15)
- Stainless steel (12)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (35)
The copper alloyed stainless steel 1.4542 (X5CrNiCuNb16-4) is used in different areas due to its good mechanical properties and corrosion resistance. Strength and corrosion resistance can be adjusted by the heat treatment, which is of importance for the application of this alloy. The mechanical properties (strength and hardness) are attributed to the dispersive precipitation of the copper rich ε–Phase. The additional precipitation of chromium carbides can reduce the corrosion resistance. Different ageing states were produced to investigate the precipitation behaviour with various methods. Furthermore, the influence of cold-rolling on the precipitation behaviour was studied in comparison to a solution annealed state without deformation. The microstructure was studied by SEM and the variations of hardness and magnetic proportion were characterised. The electrochemical potentiodynamic reactivation (EPR) was used to determine the corrosion resistance and detect chromium depletion in all heat-treated states. The results show that a work hardening accelerates the precipitation rate, while ageing at 600 °C reduces the corrosion resistance due to chromium depletion.
The copper alloyed stainless steel 1.4542 (X5CrNiCuNb16-4) is used in different areas due to its good mechanical properties and corrosion resistance. Strength and corrosion resistance can be adjusted by the heat treatment, which is of importance for the application of this alloy. The mechanical properties (strength and hardness) are attributed to the dispersive precipitation of the copper rich ε–Phase. The additional precipitation of chromi-um carbides can reduce the corrosion resistance. Different ageing states were produced to investigate the precipitation behaviour with various methods. Furthermore, the influence of cold-rolling on the precipitation behaviour was studied in comparison to a solution annealed state without deformation. The microstructure was studied by SEM and the variations of hardness and magnetic proportion were characterised. The electrochemical potentiodynamic reactivation (EPR) was used to determine the corrosion resistance and detect chromium depletion in all heat-treated states. The results show that a work hard-ening accelerates the precipitation rate, while ageing at 600 °C reduces the corrosion resistance due to chromium depletion.
The copper alloyed stainless steel 1.4542 (X5CrNiCuNb16-4) is used in different areas due to its good mechanical properties and corrosion resistance. Strength and corrosion resistance can be adjusted by the heat treatment, which is of importance for the application of this alloy. The mechanical properties (strength and hardness) are attributed to the dispersive precipitation of the copper rich ε–Phase. The additional precipitation of chromi-um carbides can reduce the corrosion resistance. Different ageing states were produced to investigate the precipitation behaviour with various methods. Furthermore, the influence of cold-rolling on the precipitation behaviour was studied in comparison to a solution annealed state without deformation. The microstructure was studied by SEM and the variations of hardness and magnetic proportion were characterised. The electrochemical potentiodynamic reactivation (EPR) was used to determine the corrosion resistance and detect chromium depletion in all heat-treated states. The results show that a work hard-ening accelerates the precipitation rate, while ageing at 600 °C reduces the corrosion resistance due to chromium depletion.
The copper alloyed stainless steel 1.4542 (X5CrNiCuNb16-4) is used in different areas due to its good mechanical properties and corrosion resistance. Strength and corrosion re-sistance can be adjusted by the heat treatment, which is of importance for the application of this alloy. The mechanical properties (strength and hardness) are attributed to the dispersive precipitation of the copper rich ε–Phase. The additional precipitation of chromium carbides can reduce the corrosion resistance. Different ageing states were produced to investigate the precipitation behaviour with various methods. Furthermore, the influence of cold-rolling on the precipitation behaviour was studied in comparison to a solution annealed state without deformation. The microstructure was studied by SEM and the variations of hardness and magnetic proportion were characterised. The electrochemical potentiodynamic reactivation (EPR) was used to determine the corrosion resistance and detect chromium depletion in all heat-treated states. The results show that a work hardening accelerates the precipitation rate, while ageing at 600 °C reduces the corrosion re-sistance due to chromium depletion.
Der nichtrostende, aushärtbare Stahl 1.4542 (X5CrNiCuNb16-4) wird aufgrund der guten mechanischen Eigenschaften und der hohen Korrosionsbeständigkeit in einer Vielzahl von technischen Anwendungen eingesetzt. Das Verhältnis zwischen den mechanischen Eigenschaften und der Korrosionsbeständigkeit wird durch eine gezielte Wärmebehandlung eingestellt. Härte und Festigkeit werden durch die Bildung von fein verteilten Kupferausscheidungen bei der Warmauslagerung erreicht. Werden dabei auch Chromkarbide gebildet, reduziert sich gleichzeitig die Korrosionsbeständigkeit. Um den Einfluss der Warmauslagerung auf die Eigenschaften zu charakterisieren, wurden verschiedene Alterungszustände erzeugt und vergleichend untersucht. Dabei wurde außerdem der Einfluss einer starken Kaltumformung auf das Alterungsverhalten und die Korrosionsbeständigkeit untersucht. Zur Charakterisierung der Veränderungen wurden die Gefüge im REM untersucht und der magnetisierbare Anteil sowie die Vickershärte ermittelt. Zum Nachweis korrosionsanfälliger Zustände wurde die elektrochemisch potentiodynamische Reaktivierung (EPR) genutzt. Die Ergebnisse zeigen, dass die Kaltverfestigung die Ausscheidungskinetik beschleunigt und die Korrosionsbeständigkeit durch die Warmauslagerung bei 600 °C deutlich reduziert wird.
The double loop electrochemical potentiodynamic reactivation (EPR) method is a standardised procedure for detecting and quantifying sensitisation on austenitic, ferritic and ferritic-austenitic stainless-steel grades. This sensitisation is caused by microstructural alternations, as the formation of chromium carbides, nitrides or sigma-phases, which generate local chromium depleted zones nearby. The latter strongly influence the corrosion resistance and the electrochemical response of a stainless steel during electrochemical potentiodynamic reactivation, providing important information on the degree of chromium depletion. In case of martensitic stainless steels, which are used for cutlery and surgical instruments, the heat treatment has a strong impact on the microstructure, the material properties and especially on the corrosion resistance. To study this interaction, the EPR method was modified for the application on martensitic stainless steels with about 13 wt.-% chromium. Different H2SO4 concentrations and EPR-parameters were tested and compared on two standard martensitic stainless-steel grades (AISI 420 A / X20Cr13 and AISI 420 C / X46Cr13) to define applicable parameters. Afterwards, these parameters were used to study the effect of austenitisation time and cooling rate on the corrosion resistance of both martensitic stainless steels. The response of both alloys was different due to the different carbon levels, which will be explained by microstructural investigations in detail. All results allow postulating a process window, in which chromium depletion is suppressed and an optimised corrosion resistance is guaranteed. Based on this research, the modified EPR-test is now used to control the heat treatment and its impact on the corrosion resistance of martensitic stainless steels in the cutlery industry. The EPR-test is thus an interesting alternative for manufacturers, processors, users and researchers to the time-consuming exposition test normally used to characterise the corrosion resistance of martensitic stainless steels.
The corrosion resistance of stainless-steels grades is of high importance for the technical safety in different environmental conditions. Processing and surface finish influences the corrosion resistance of ferritic stainless steels, which may be considered for some application in marine environment. Three ferritic stainless steel alloys (X2CrNi12, X2CrTiNb18 and X2CrMoTi18-2) were exposed in four different surface finishes (rolled, dry grinding, glass beaded and electro polished) for five years in marine environment to obtain reliable information about the corrosion resistance. All samples were assessed after 22 and 60 months according to DIN EN ISO 10289 in validation degrees from 1 to 10. Complementary investigation using accelerated chamber test (salt spray test followed by four weeks storage at 30 °C / 80 % relative humidity) and short-term electrochemical methods (electrochemical potentiodynamic reactivation, pitting potentials and the KorroPad method) were conducted to compare their results. The presentation gives an overview on all methods and the generated results, which show benefits and restrictions of long-term, accelerated and short-term corrosion tests.
Die Legierungselemente (Chrom und Kohlenstoff) und die Wärmebehandlung bestimmen Korrosionsbeständigkeit und Härte martensitischer nichtrostender Stähle. Verschiedene wissenschaftliche Arbeiten haben bereits gezeigt, dass die Korrosionsbeständigkeit sehr stark vom Anteil an Chromkarbiden im Gefüge bestimmt wird. Der kombinierte Einfluss von Kohlenstoffgehalt und der Abkühlgeschwindigkeit beim Härten wurde mit Fokus auf die Korrosionsbeständigkeit bisher nur unzureichend untersucht. Die Literatur liefert außerdem gegensätzliche Aussagen über den Einfluss der Abkühlgeschwindigkeit, was möglicherweise auf unterschiedliche Kohlenstoffgehalte zurückgeführt werden kann. In dieser Arbeit wird daher systematisch untersucht, ab welcher Abkühlgeschwindigkeit es bei den Werkstoffen X20Cr13 und X46Cr13 zu Karbidbildung und Chromverarmung kommt. Die Variation der Abkühlgeschwindigkeit erfolgte für die industriell relevante Härtetemperatur von 1050 °C mit dem Stirnabschreckversuch. In Abhängigkeit von der Abkühlgeschwindigkeit wurden an den Stirnabschreckproben Gefüge, Härte und Korrosionsbeständigkeit (EPR, kritische Lochkorrosionspotentiale) untersucht und die Ergebnisse mit thermodynamischen Berechnungen (ThermoCalc) korreliert. Aus den Ergebnissen wird abgeleitet, unter welchen Bedingungen die Abkühlgeschwindigkeit die Korrosionsbeständigkeit beeinflusst.
Der nichtrostende Duplexstahl 1.4062 (X2CrNiN22-2) hat sich im Bauwesen als Werkstoffalternative zu den nichtrostenden Austeniten etabliert. Die Korrosionsbeständigkeit von Schweißverbindungen aus 1.4062 wird, neben dem Grundwerkstoff, dem Schweißzusatzwerkstoff und dem Schweißverfahren, auch sehr stark von der Oberflächennachbehandlung der Schweißnaht beeinflusst. Je nach zukünftigem Anwendungsbereich und geforderter Korrosionsbeständigkeit wird die Schweißnaht geschliffen, gebeizt, elektropoliert oder gestrahlt, um die beim Schweißen entstandenen Anlauffarben zu entfernen. Gestrahlte Oberfläche sind in der industriellen Praxis häufig anzutreffen, da sie deutlich einfacher und kostengünstiger herzustellen sind als gebeizte oder elektropolierte Oberflächen. Die Auswahl des Strahlmittels bestimmt auch die Prozesskosten, wobei das Strahlen mit Korund effektiver als das Strahlen mit Glasperlen ist. In den letzten Jahren wurden korrosionsanfällige Oberflächen bei nichtrostenden Stählen beobachtet, wenn diese mit Korund geschliffen wurden. Daher wird nun auch beim Strahlen kritisch hinterfragt, ob Korund als Strahlmittel die Korrosionsbeständigkeit verändert. Diese Fragestellung wird im Vortrag beantwortet indem geschliffene, gebeizte, mit Korund gestrahlte und mit Glasperlen gestrahlte Schweißverbindungen vergleichend untersucht werden. Die Ergebnisse der Untersuchungen von den Strahlmitteln und den gestrahlten Oberflächen werden mit den Ergebnissen der Salzsprühnebelprüfung, den kritischen Lochkorrosionspotentialen und der KorroPad-Prüfung korreliert.
Die Korrosionsbeständigkeit geschweißter Konstruktionen aus nichtrostenden Duplexstählen wird von den Schweißparametern und der Nachbehandlung der Oberflächen bestimmt. Eine etablierte Methode der Schweißnahtnachbehandlung ist das Strahlen der Oberfläche mit Glasperlen. Diese Methode soll aus wirtschaftlichen Gründen durch das Strahlen mit Korund ersetzt werden, welches deutliche Zeit- und Kostenvorteile bietet. Besonders bei der Lochkorrosionsbeständigkeit hat sich das Schleifen mit Korund bereits als nachteilig erwiesen, weshalb diese Umstellung auch beim Stahlen kritisch hinterfragt wird. Daher wurden Probeschweißungen bei der Firma Modersohn hergestellt und mit verschiedenen Oberflächenbearbeitungsmethoden (Glasperlenstrahlen, Korundstrahlen, Beizen, Elektropolieren, Schleifen) nachbehandelt. Diese verschiedenen Oberflächenzustände wurden analytisch (REM, Rauheit) charakterisiert und hinsichtlich ihrer Lochkorrosionsbeständigkeit vergleichend untersucht werden, um die Eignung des Strahlens mit Korund zu beurteilen.