Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (33) (entfernen)
Sprache
- Englisch (33)
Referierte Publikation
- ja (33) (entfernen)
Schlagworte
- Plasma polymerization (5)
- Surface functionalization (4)
- Fluorescence spectroscopy (3)
- Surface modification (3)
- Allyl alcohol (2)
- Aluminium (2)
- Dielectric properties (2)
- Dielectric relaxation (2)
- Peel strength (2)
- Plasma modification (2)
Monotype functionalizations with different types of functional groups (OH, NH2, COOH) on polypropylene and poly(tetrafluoroethylene) surfaces were synthesized using pulsed plasma-initiated homo- or copolymerization of functional group-carrying monomers. The maximum concentrations of functional groups were 31 OH, 18 NH2 or 24 COOH groups per 100 C atoms using allyl alcohol, allylamine or acrylic acid respectively as the monomer. The measured peel strengths of aluminium deposits increased linearly with the concentration of functional groups. Near the maximum concentration of OH (>27 OH/100 C atoms) or at moderate concentrations of COOH groups (>10 COOH/100 C atoms), constant (maximum) peel strengths were measured due to the mechanical collapse of one component in the composite (cohesive failure). Interface failures in Al-PP composites were found with COOH, NH2 and OH groups and cohesive failures were seen when higher concentrations of COOH groups were applied (>10 COOH/100 C atoms).
The peel strength of aluminium to polypropylene and poly(tetrafluoroethylene) was determined in dependence on the type and the concentration of functional groups on the polymer surface. For this purpose the polymer surface was equipped with monotype functional groups. The first method to produce monotype functionalized surfaces was an introduction of O functional groups using an oxygen plasma treatment and converting these groups to OH groups applying a wet chemical reduction. In result of this two-step treatment the hydroxyl group concentration at the polymer surface could be increased from 34 to 1014 OH groups/100 C atoms. The second method consists in the deposition of a 150 nm adhesion-promoting layer of plasmapolymers or copolymers onto the polymer surface using the pulsed plasma technique. For that purpose functional groups carrying monomers as allyl alcohol, allylamine and acrylic acid were used. Applying the plasma-initiated copolymerization and using neutral monomers like ethylene or butadiene the concentration of the functional groups was varied.
A correlation of peel strength with the ability of forming chemical interactions between Al atoms and functional groups was found: COOH > OH >> NH2 > H(CH2CH2).
A new concept for molecular interface design in metal-polymer systems is presented. The main features of this concept are the replacement of weak physical interactions by strong covalent bonds, the flexibilization of the interface for compensating different thermal expansions of materials by using long-chain flexible and covalently bonded spacers between the metal and the polymer as well as its design as a moisture-repellent structure for hindering diffusion of water molecules into the interface and hydrolysis of chemical bonds.
For this purpose, the main task was to develop plasmachemical and chemical techniques for equipping polymer surfaces with monotype functional groups of adjustable concentration. The establishing of monotype functional groups allows grafting the functional groups by spacer molecules by applying usual wet-chemical reactions. Four processes were favoured for production of monotype functional groups by highly selective reactions: the plasma bromination, the plasma deposition of plasma polymers, the post-plasma chemical reduction of O-functionalities to OH-groups, and the chemical replacement of bromine groups by NH2-groups. The grafting of flexible organic molecules as spacers between the metal layer and polymer improved the peel strength of the metal. To obtain maximal peel strength of aluminium coatings to polypropylene films and occurrence of cohesive failure in the polypropylene substrate, about 27 OH groups per 100 C-atoms or 6 COOH groups per 100 C-atoms were needed. Introducing C6-11-aliphatic spacers 1 OH or COOH group per 100 C-atoms contributed about 60% of the maximal peel strength of the Al-PP system, i.e. 2 or 3 spacer molecules per 100 C-atoms were sufficient for maximal peel strength.
The production of chemically-defined plasma polymers and the introduction of monotype functional groups onto polymer surfaces are described. One method is to lower the energetic level of low-pressure plasmas. Pressure- and plasma-pulsed plasmas were successfully tested for the production of chemically-defined plasma polymers by increasing the monomer supply during the plasma-off period. Well-defined ultra-thin polymer films with regular structure were deposited from atmospheric plasmas by electrospray techniques. Post-plasma wet-chemical processing was also applied, as were gas/liquid-based aerosols and underwater plasmas.
A straightforward strategy toward the sensitive fluorometric detection of primary amino groups on plasma-chemically modified polypropylene supports is presented, exploiting the transformation of the sterically nonhindered pyrylium dye Py-1 into its pyridinium counterpart. The reaction-induced blue-shifted absorption and emission bands and an increased fluorescence quantum yield provide the basis for the spectroscopic distinction between covalently bound and free, that is, nonspecifically adsorbed label molecules. With this label, for the first time, plasma-chemically introduced amino functionalities could be monitored on the surface of a polymer film employing fluorescence spectroscopy and confocal laser scanning microscopy.
Copolymers of acrylic acid and styrene (AA/S) were prepared by pulsed plasma deposition technique. Their structure–property relationships were studied in dependence on the comonomer ratio. Both, the regularity of the structure and the composition of the thin copolymer films were investigated by bulk-sensitive (dielectric spectroscopy, FTIR, and differential scanning calorimetry) as well as surface-sensitive methods such as X-ray photoelectron spectroscopy (XPS). For an unambiguous identification of the functionality of the deposited films the COOH groups were estimated by derivatization with trifluoroethanol and subsequent XPS measurement as well as by the quantitative analysis of the FTIR data. As a result, the concentration of COOH groups on the surface and in the bulk is increasing with the fraction of AA in precursor mixture in a non-monotonous way but similar to the dependence obtained by conventional free radical polymerization.
A first inter-laboratory comparison was conducted to demonstrate and document the capability of interested laboratories to measure the fraction of C—OH species on a plasma oxidised poly(propylene) sample by using a chemical derivatisation XPS approach. This report presents the results from that inter-laboratory comparison and includes the data received for the measured values and their associated standard deviations of laboratory means, at a 95% confidence level. The measurements were guided by a protocol developed within the group before and summarised shortly in the paper. Standard deviations that may characterise the state-of-the-art for the nominally simple and rather often practised case of TFAA chemical derivatisation XPS of C—OH species on a plasma oxidised polyolefin surface are calculated following ISO 5725-2:1994. The main conclusion is that the associated degree of equivalence reached by the participating laboratories in this comparison is still low. Further research to improve chemical derivatisation XPS protocols is mandatory.
Response of linear, branched or crosslinked polyethylene structures on the attack of oxygen plasma
(2014)
Linear, branched and crosslinked polyethylenes (PE) were exposed to the low-pressure oxygen plasma for 2–120 s. In the following the samples were washed with solvents to remove low-molecular weight oxidized material and to excavate the subjacent polymer structure for microscopic characterization. X-ray photoelectron spectroscopy (XPS) measurements provided information about changes in elemental composition and chemical structure of PE after plasma exposure and washing. The calculation of the concentration of tertiary C atoms using XPS data was a measure of branches and crosslinking in the polymer before and after exposure to oxygen plasma. Linear PE was most sensitive towards oxygen plasma and showed the highest concentration in tertiary C atoms after plasma exposure. On the other hand branched PE types, which possess originally more tertiary carbon atoms, have lost two-third of them after 2 s oxygen plasma exposure. Branched PE show also topological changes at their surface as detected by atomic force microscopy. Differential scanning calorimetry measurements confirmed strong changes in crystallinity and molecular orientation of linear PE already after 120 s exposure to the oxygen plasma interpreted as amorphization. These effects should be interpreted as result of crosslinking caused by the recombination of dangling bond sites.