Platinum does not form any adherent oxides and can be easily wetted by tin-based solders. Platinum is also an available metallization in semiconductor laboratories. Therefore we investigated the diffusion of platinum thin-film metallizations into eutectic tin–lead solder by using a high-resolution secondary ion mass spectroscopy (SIMS) profiling from the back side. It is shown that an intermetallic phase (PtSn4) is formed during soldering, which controls the consumption of platinum during soldering and in operation. The consumption of platinum follows the well-known parabolic diffusion law. The activation energy of this process is 0.63 eV. Even at extended heating cycles of 2 min at 250°C, 190 nm from the original 300 nm of the platinum film remain undissolved. This high stability makes platinum a very attractive thin-film metallization for flip-chip (FC) bonding of new microsystems.
Iridium oxide is the catalytic material with the highest stability in the oxygen evolution reaction (OER) performed under acidic conditions. However, its high cost and limited availability demand that IrO2 is utilized as efficiently as possible. We report the synthesis and OER performance of highly active mesoporous IrO2 catalysts with optimized surface area, intrinsic activity, and pore accessibility. Catalytic layers with controlled pore size were obtained by soft-templating with micelles formed from amphiphilic block copolymers poly(ethylene oxide)-b-poly(butadiene)-b-poly(ethylene oxide). A systematic study on the influence of the calcination temperature and film thickness on the morphology, phase composition, accessible surface area, and OER activity reveals that the catalytic performance is controlled by at least two independent factors, that is, accessible surface area and intrinsic activity per accessible site. Catalysts with lower crystallinity show higher intrinsic activity. The catalyst surface area increases linearly with film thickness. As a result of the templated mesopores, the pore surface remains fully active and accessible even for thick IrO2 films. Even the most active multilayer catalyst does not show signs of transport limitations at current densities as high as 75 mA cm-2.