Aluminas with Fe2O3 particles finely divided in the Al2O3 matrix were prepared via a crystalline precursor derived from ammonium dawsonite and its calcination. The precursors with Fe content between 1 and 10 wt% were synthesized by reaction of ammonium hydrogen carbonate with mixtures containing aluminium ammonium sulfate and ferric ammonium sulfate. The characterization of the as-synthesized and calcined products by chemical analysis, XRD, EPR, Mössbauer, TEM and adsorption measurements shows that all the Fe3+ ions are incorporated into the structure of dawsonite when the Fe content is low and that the calcined materials with micropores and mesopores (maximum 3040 Å) also contain very small Fe2O3 particles (<10 nm) at higher Fe contents.
Improved large mesoporous ordered molecular sieves - Stabilization and acid/base functionalization
(2010)
The preparation of nanoporous materials with enhanced stability using an improved synthesis route using reactive inorganic silica and alumina species is reported. This way improved mesoporous molecular sieves were obtained. The synthesized aluminum substituted mesoporous molecular materials (Al-MMS) contain very large pores of 50200 Å size combined with an improved pore wall thickness. Increased wall thickness and Al substitution lead to an improved chemical stability against alkaline solution. The textural, structural and acid properties are investigated by physico-chemical methods. The catalytic performance acidic materials was tested in the benzoylation reaction; amino functionalized materials were studied in the base catalyzed Michael addition.