Effect of cooling rate on microstructure and properties of microalloyed HSLA steel weld metals
(2015)
Two high strength Nb/Ti microalloyed S690QL steels were welded with identical filler material, varying welding parameters to obtain three cooling rates: slow, medium and fast cooling. As cooling rate increased, the predominantly acicular ferrite in Nb weld metal (WM) is substituted by bainite, with a consequence of obvious hardness increase, but in Ti WM, no great variation of acicular ferrite at all cooling rates contributed to little increment of hardness. The transition between bainite and acicular ferrite has been analysed from the point view of inclusions characteristics, chemical composition and cooling rate. Excellent Charpy toughness at 233 K was obtained with acicular ferrite as predominantly microstructure. Even with bainite weld of high hardness, the toughness was nearly enough to fulfill the minimal requirements. WM for Ti steel showed to be markedly less sensitive to the variations of cooling rate than that for Nb steel.
Carrier gas hot extraction (CGHE) technique was used for measurement of hydrogen in press-hardened (and as delivered) condition of 22MnB5 steel primarily coated with a thin layer of Al–Si. The CGHE technique was applied using different temperature programs: isothermal heating, temperature step, and linear heating in solid state. The effusing hydrogen was measured using thermal conductivity device (TCD) and high resolution mass spectroscopy (MS). Single isothermal heating at 400 and 900 °C allowed determining absolute value of effusing hydrogen. The linear heating, also known as thermal desorption analysis (TDA), revealed temperature dependent hydrogen effusion peaks. The deconvolution of the TDA spectra by peak fitting allowed the calculation of hydrogen desorption energies for each peak. The results showed good agreement between hydrogen concentrations measured with MS and TCD. In addition, the as-received ferrite-perlite microstructure showed only hydrogen effusion above 400 °C. The subsequent press hardening process leads to hydrogen uptake in the microstructure. In general, the press-hardened 22MnB5 revealed a hydrogen concentration of 0.4 to 0.5 ppm. The biggest concentration was released at isothermal holding at 400 °C indicating reversibly trapped hydrogen. TDA results with different heating rates confirmed mostly diffusible and reversible trapped hydrogen due to calculated activation energies in the range from 4 to 20 kJ mol-1; it was ascertained that nearly 90 % of the hydrogen left the specimens below 400 °C. Melt extraction (ME) was performed to measure the total hydrogen amount (including the diffusible and trapped hydrogen) and showed that above 900 °C up to 1 ppm hydrogen is trapped.