Filtern
Dokumenttyp
- Beitrag zu einem Tagungsband (18)
- Zeitschriftenartikel (4)
- Vortrag (3)
- Corrigendum (2)
- Forschungsbericht (2)
- Beitrag zu einem Sammelband (1)
Referierte Publikation
- nein (30) (entfernen)
Schlagworte
- Wasserstoff (9)
- Schweißen (6)
- Fügetechnik (4)
- Hochfester Feinkornbaustahl (4)
- WEZ-Erweichung (4)
- Forschung (3)
- Thermodynamische Simulation (3)
- UP-Schweißen (3)
- Welding (3)
- Diffusion (2)
Organisationseinheit der BAM
Paper des Monats
- ja (1)
Eingeladener Vortrag
- nein (3)
Effect of cooling rate on microstructure and properties of microalloyed HSLA steel weld metals
(2015)
Two high strength Nb/Ti microalloyed S690QL steels were welded with identical filler material, varying welding parameters to obtain three cooling rates: slow, medium and fast cooling. As cooling rate increased, the predominantly acicular ferrite in Nb weld metal (WM) is substituted by bainite, with a consequence of obvious hardness increase, but in Ti WM, no great variation of acicular ferrite at all cooling rates contributed to little increment of hardness. The transition between bainite and acicular ferrite has been analysed from the point view of inclusions characteristics, chemical composition and cooling rate. Excellent Charpy toughness at 233 K was obtained with acicular ferrite as predominantly microstructure. Even with bainite weld of high hardness, the toughness was nearly enough to fulfill the minimal requirements. WM for Ti steel showed to be markedly less sensitive to the variations of cooling rate than that for Nb steel.
Wasserstoff kann eine Rissbildung u.U. auch noch nach Tagen in der Schweißnaht bewirken. Dabei stellen höherfeste Stähle etablierte Kaltrissprüftests vor Herausforderungen. Generell nimmt die zur Rissvermeidung tolerierbare Wasserstoffkonzentration mit zunehmender Festigkeit der Werkstoffe ab. Zudem verändern weiterentwickelte Schweißverfahren die Nahtgeometrie und Wärmeeinbringung und die Ausbildung risskritischer Mikrostrukturen (z.B. Wärmeeinflusszone). Am Beispiel des Implant- und Tekken-Tests werden die Einsatz- u. Anwendungsgrenzen bewertet. Zu berücksichtigen ist, dass beim Schweißen eine äußere mechan. Beanspruchung durch bauteilspezifische Steifigkeitsverhältnisse wirksam ist. Zusätzlich werden weiterführende Prüfverfahren zur Bestimmung der Wasserstoffkonzentration und -diffusion in Schweißnähten vorgestellt, wie die Trägergasheißextraktion (TGHE) für die Ermittlung der Wasserstoffkonzentration (ISO 3690) oder Hochtemperaturdiffusionskoeffizienten.
Diese Werte sind für die schweißtechnische Praxis von großer Bedeutung, um Haltezeiten z.B. für das Wasserstoffarmglühen abzuleiten.
The article "Influence of welding stresses on relief cracking during heat treatment of a creep-resistant 13CrMoV steel: Part I - Effect of heat control on welding stresses and stress relief cracking" was originally published in the journal "Welding in the world" Online First without Open Access. After publication in volume 64, issue 5, page 807-817 the authors decided to opt for Open Choice and to make the article an Open Access publication. Therefore, the copyright of the article has been changed to The Author(s) 2020 and the article is forthwith distributed under the terms of the Creative Commons Attribution Attribution 4. 0 International License.
The article "Influence of welding stresses on relief cracking during heat treatment of a creep-resistant 13CrMoV steel: Part II - Mechanisms of stress relief cracking during post weld heat treatment" was originally published in the journal "Welding in the world" Online First without Open Access. After publication in volume 64, issue 5, page 819-829 the authors decided to opt for Open Choice and to make the article an Open Access publication. Therefore, the copyright of the article has been changed to The Author(s) 2020 and the article is forthwith distributed under the terms of the Creative Commons Attribution Attribution 4. 0 International License.
Für eine nachhaltige und ressourceneffiziente Fertigung von Windkraftanlagen ist der Einsatz moderner hochfester Feinkornbaustähle vielfach notwendig. Bei der Montage hochfester Stahlkonstruktionen kommt es trotz anforderungsgerechter schweißtechnischer Fertigung vereinzelt zur Detektion von unzulässigen Unregelmäßigkeiten im Schweißbereich. Derzeitige Normen und Verarbeitungsrichtlinien geben hierbei kaum Informationen zu adäquaten Reparaturkonzepten, insbesondere für hochfeste Stähle. Vor diesem Hintergrund werden an der Bundesanstalt für Materialforschung und -prüfung (BAM) bauteilrelevante Untersuchungen zu den schweißbedingten Beanspruchungen und Gefügeveränderungen bei der schweißtechnischen Reparatur durch lokales thermisches Ausfugen und erneutes Schweißen durchgeführt.
Hierzu werden einige wesentliche Ergebnisse an Beispielen des Ingenieurbaus, mit Blick auf die mechanisch-technologischen Eigenschaften und Eigenspannungen erörtert. In einem aktuellen Vorhaben (FOSTA P1311, IGF 20162N) sind darauf aufbauend die Einflüsse durch die Schrumpfbehinderung und Wärmeführung beim Reparaturschweißen hochfester Feinkornbaustähle (S500MLO, S960QL) sowie die Reparaturzyklenanzahl Fokus systematischer Untersuchungen. Mittels strukturmechanischer Berechnungen ließen sich hierzu selbstbeanspruchende Probenformen identifizieren, die unterschiedliche definierte Steifigkeitsverhältnisse von Reparaturschweißnähten realer Bauteile abbilden. Schweißnähte an diesen bauteilähnlichen Proben weisen signifikant erhöhte schweißbedingte Beanspruchungen mit zunehmenden (Biege-)Einspanngraden auf. Im Vergleich mit bisherigen Erkenntnissen wird gezeigt, dass eine sichere Reparatur solcher Schweißnähte nur mittels optimaler Reparaturkonzepte und Wärmeführung gelingt, um diesen hohen Beanspruchungen und auch den speziellen Gefügen hochfester Stähle Rechnung zu tragen.
Ziel der Untersuchungen ist es letztlich, Empfehlungen für beanspruchungs- und werkstoffgerechte Reparaturkonzepte gerade für KMU abzuleiten, um Schäden und zumeist teure Nacharbeiten zu vermeiden.
High-strength low-alloyed (HSLA) steels with yield strength ≥ 690 MPa have increasing importance in steel construction and civil engineering. However, weld processing of those steels is a major challenge. The susceptibility for degradation of mechanical properties of weld joints significantly increases in presence of hydrogen and can result in hydrogen assisted cracking (HAC). Generally, risk for HAC increases with increasing yield strength of HSLA steels. To minimize the incidence of HAC, it is essential to gain knowledge about both the (1) absorbed hydrogen amount and its distribution in the weld seam and (2) options to lower
the amount of introduced hydrogen. Existing standards recommend heat treatment procedures (interpass temperature or post weld heat treatment) to reduce the diffusible hydrogen concentration in weldments. In this context, different weld seam geometries should be considered. For HSLA steel fabrication weld processing with seam opening angles of 45° to 60° is typical. Modern weld technologies allow welding with seam opening angles of 30° - reduced welding time and costs. In the present study, the hydrogen distribution in multi-layer welds of a 960 MPa HSLA steel was analysed. Influence of different seam opening angles as well as heat input, interpass temperature and post weld heat treatments were investigated. The welded samples were quenched in ice water immediately after welding and subsequently stored in liquid nitrogen. After defined warming up, small specimens were machined from the weld seam by water jet cutting. The diffusible hydrogen concentration was measured by carrier gas hot extraction with coupled mass spectrometer. The results showed, that low heat input and post weld heat treatment procedures can lower hydrogen concentrations in welds. Furthermore, a gradient of the hydrogen concentration was
identified with increasing weld pool depth. By varying the seam opening angles different hydrogen concentrations were
measured.
In-situ analysis of solid state phase transformation in TRIP-aided steels by synchrotron diffraction
(2011)
Energy dispersive synchrotron diffraction (EDXRD) analysis and 3 dimensional digital image correlations were conducted to investigate the stress and strain effected transformation behavior during tensile loading of low alloyed TRansformation Induced Plasticity (TRIP) steel. This technique allowed for phase specific stress measurement during certain tensile load steps in the elastic and also plastic regime. Additionally the simultaneous determination of the load dependent phase content was realized. The results show that the martensite transformation starts only after exceeding the overall yield point and is finished before reaching the uniform elongation, whereas a large portion of the austenite remains unchanged in the structure. Furthermore, the martensite transformation related to the stress in the γ-phase and α-phase was analyzed and quantified.
Offshore wind turbines are an important goal in national energy strategies worldwide. Foundation structures are manufactured from submerged arc welded (SAW) plates with thicknesses up to 200 mm. In that connection, high-strength steels like the S420G2+M are more and more applied offering the possibility for increased stability and load-bearing capacity of the foundations. These offshore steel grades can show a susceptibility for delayed hydrogen assisted cold cracking of the weld joints. For that purpose, a minimum waiting time (MWT) of up to 48 h (dependent on applied standards) is recommended before non-destructive testing is allowed and conducted. But this concept is based on older steel grades that have been used for three or more decades. Nowadays, the metallurgical improvements (clean steels, proper rolling, and heat treatment) of base materials and well as welding consumables must be anticipated. Hence, the MWT concept should be critically discussed as it is assumed to be very conservative. For that reason, the focus of this study was to investigate the diffusion behavior in S420G2+M steel and its multi-layer SAW joint. Electrochemical permeation experiments were carried at room temperature. Boundary conditions were anticipated in terms of using different sample thicknesses. From the experimental data, hydrogen diffusion coefficients and absorbed diffusible hydrogen concentrations had been calculated. It was shown that hydrogen diffusion in the base material is increased compared to the weld metal. In addition, the sample thickness had a significant on the calculated diffusion coefficients. The minimum and maximum diffusion coefficients had been used for numerical modelling of the hydrogen diffusion in the welding joint. It became clear that a MWT must be always regarded together with a critical initial diffusible hydrogen concentration for the evaluation of a possible delayed cracking as diffusion times were mostly > 48 h due to the thick plates.
Für eine signifikante Festigkeitssteigerung von vergüteten, hochfesten Feinkornbaustählen mit einer Nominalstreckgrenze ≥ 690 MPa, ist die Zugabe von Mikrolegierungselementen, wie Nb und Ti, unerlässlich. Die Normvorgaben zur chemischen Zusammensetzung dieser Stähle (bspw. in DIN EN 10025-6) geben zur Erzielung der vorgeschriebenen Eigenschaften dabei oft nur Grenzgehalte für die Hersteller vor. Die Wirkung der Legierungselemente in der WEZ ist teilweise komplett konträr. Somit wird eine adäquate Vorhersage der Chargenabhängigkeit hinsichtlich der Schweißeignung und des Tragverhaltens der Schweißverbindung erschwert. Neben metallographischen Untersuchungen einzelner WEZ-Bereiche wurden unter Variation der chemischen Zusammensetzung, thermodynamische Phasenberechnungen mittels ThermoCalc durchgeführt. Hierdurch wird ein Verständnis zur Phasentransformation, Ausscheidungswachstum und -auflösung während des Schweißens in Abhängigkeit von Temperatur und Abkühlbedingungen geschaffen.