A new method for the evaluation of the low temperature properties of rubber materials is presented. The method emulates the standardized compression set measurement, which is frequently used for sealing materials, but can be performed within a considerably shorter time. The results are compared with the standard test and found to be qualitatively the same. Slight differences are discussed on the basis of the differences in the measurement procedures. Further data evaluation is done by fitting functions to describe the material behaviour.
Partial discharges may cause damage to electrical insulation of high voltage equipment. They initiate elastic waves in the insulating material, e.g. in the stress cone of an outdoor termination. Localisation of the origin of such elastic waves can help to predict serious damaging processes in the electrical insulation. In order to measure and evaluate the wave propagation effects in typical multilayered elastomeric structures, knowledge of the material properties is required. The propagating velocity and the attenuation of longitudinal waves are important parameters. Values for these quantities found in the literature were not appropriate. Therefore, for cross-linked polyethylene (XLPE) and cured liquid silicone rubber (LSR), the longitudinal wave velocity and the attenuation were evaluated in the temperature interval from -20°C to 50°C and in the frequency range from 200 kHz to 600 kHz using a two-sample ultrasound technique. The loss factor was determined from these measured quantities. Additionally, low frequency Dynamic Mechanical Thermal Analysis (DMTA) was applied to investigate LSR and XLPE in a temperature interval between -100 and 50°C and to check qualitatively the ultrasound data.
The investigation of low temperature properties of elastomeric sealing materials by means of thermo-analytical methods is a sound way to get information about the glass transition process.
The breakdown temperature of the sealing function of O-ring seals was measured in a component test setup depending on material and degree of compression.
An in depth explanation of the observed component tests behaviour is currently in preparation. It requires the results of thermo-analytical methods and measurements as the compression set (not shown here). With that, a model was developed to describe the correlation between physical material parameters and observed component behaviour.
Carbon fibre prepregs have found widespread application in lightweight constructions. They are based on a carbon-fibre fabric impregnated with reactive epoxy resin. DMA measurements under temperature conditions similar to an autoclave programme were carried out using commercially available prepreg material with a high glass transition temperature. The characteristic of the temperature programme was a dynamic heating segment at 1.5 K/min followed by a longer isothermal segment at 180 °C. The courses of the storage modulus E', loss modulus E'' and tanδ were recorded. The measuring frequency was varied between 1 Hz and 33.3 Hz. Gelation and vitrification are assigned. The influence of the measuring frequency on the time to vitrification and the correlation with DSC are discussed. The reaction does not end even after 10 h curing at 180 °C, which is interpreted as the slow cessation of the reaction caused by vitrification.
Rubbers are often used for seal applications due to their special material properties and easy use. In many applications the material is exposed to low temperatures during Operation. Therefore it is important to know the material behavior at low temperatures to determine the temperature ränge that allows a Safe Operation of the seal, e.g. in storage and transport Containers for radioactive materials.
The seal function of an elastomer is limited in temperature by the rubber-glass transition during which the material properties change from rubber-like to stiff and glass-like. For a given application this correlation is not trivial and therefore needs an in-depth investigation under consideration of the physical properties and the
application conditions.
In this work different analytical methods are used to characterize the material behavior at low temperature in the ränge of the glass-rubber-transition and are compared with the quality of Operation of a component which is here defined by the detected leakage rate.
The method for the determination of compression set values with a Dynamic Mechanical Analysis (DMA) setup at low temperatures, which was presented previously, allows a much faster and readily automated procedure than the standardized compression set test according to ISO 815-2. This method is applied to a series of different elastomeric materials that are commonly used for sealing applications. The results of the compression set test are compared with results from thermal analysis to allow an in depth comparison of the material behaviour at low temperatures.
Furthermore, a comparison between two EPDM materials is presented. These materials show very similar properties determined by thermo analytical methods such as Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Analysis (DMA) but differ clearly in their compression set behaviour. This comparison shows the importance and value of information of the compression set test in addition to thermal analysis to judge the behaviour of sealing materials and confirms the relevance of the new compression set test method for the investigation of low temperature properties of elastomers.
Carbon-fibre prepregs have found widespread use in lightweight applications. They are based on a carbon-fibre fabric impregnated with reactive epoxy resin. Prepreg materials are generally pre-cured so that they have a higher molecular weight than typical resins in order to reduce resin flow, which facilitates storage and later processing properties.
The measurements were carried out using commercially available materials and follow the published DMA investigations of the same material. TMDSC was used to find the correlation between curing conditions, the degree of cure and glass transition temperature. TMDSC has the advantage over standard DSC that it enables better determination of the glass transition temperature, which is often accompanied by an exothermic curing reaction, and thus overshadowed. The influence of the amplitude of temperature modulation was tested in preliminary experiments. For non-cured material a glass transition temperature of approximately 0 °C was determined; whereas for the totally cured material it was approximately 230 °C. The changes in degree of cure, temperature of actual glass transition and post-reaction are given as a function of curing time at 180 °C. The correlation between actual glass transition temperature and degree of cure is derived.
Für Elastomenwerkstoffe im Allgemeinen und im Bereich der Dichtungstechnik im Besonderen ist der Druckverformungsrest eine wichtige Kenngröße zur Beurteilung der Eignung eines Werkstoffs bzw. der Funktion eines Bauteils. Er ermöglicht eine Einschätzung des zeitabhängigen Rückstellverhaltens eines Werkstoffs nach Deformation. Dieses ist für Dichtungen von besonderer Bedeutung, da der Test deren Einbauzustand nachstellt.
Oft wird er, bei der Prüfung unter erhöhten Temperaturen, zur Beurteilung des Alterungsverhaltens verwendet und kann anhand eines definierten Versagenskriteriums zur Lebensdauerabschätzung eingesetzt werden. Bei tiefen Temperaturen dient er dazu, die limitierende Einsatztemperatur zu bestimmen. Dabei spielt eine Alterung im eigentlichen Sinne nur eine untergeordnete Rolle, wohl aber physikalische Effekte wie Tieftemperaturkristallisation und Glasübergang. Diese Effekte sind weit weniger durch lange Lagerzeiten beeinflusst als die eigentliche Alterung.
Die Versuchsdurchführung unterscheidet sich je nach angewandter Norm und kann einen deutlichen Einfluss auf den Druckverformungsrest haben. Alle standardisierten Methoden sind aufgrund der langen Lagerzeiten relativ langwierig und erfordern das regelmäßige Eingreifen durch den Prüfer. Zusätzlich sehen einige Methoden nur die Bestimmung eines einzelnen Wertes nach einer definierten Zeit vor.
Um die Messungen zu beschleunigen wurde eine Methode entwickelt, die automatisch die erforderlichen Messungen bei mehreren Temperaturen durchführt.
Dazu wird ein Prüfgerät der Dynamisch Mechanischen Analyse verwendet, das kontinuierlich die Deformation während eines frei programmierbaren Temperaturzyklus misst, wodurch eine sehr große Datenmenge verfügbar ist.
Ein Vergleich der neuen Methode mit den Ergebnissen des nach ISO 815 genormten Messprinzips ergibt eine gute Übereinstimmung. Ergebnisse der neuen Methode werden vorgestellt und die Vorzüge der kontinuierlichen Datenerfassung, z.B. für die Materialauswahl, diskutiert.
Die vorgestellten Ergebnisse beziehen sich zum großen Teil auf die in beschriebenen Untersuchungen und Ergebnisse.
Der Druckverformungsrest (DVR) stellt insbesondere für Dichtungsanwendungen eine wichtige Kenngröße zur Beurteilung der Eignung eines Elastomers dar. Er ermöglicht die Einschätzung des zeitabhängigen Rückstellverhaltens eines Werkstoffs nach Deformation. Neben der Prüfung bei erhöhten Temperaturen, zur Beurteilung des Alterungsverhaltens, lässt sich bei der Durchführung bei tiefen Temperaturen die limitierende Einsatztemperatur bestimmen. Die Versuchsdurchführung unterscheidet sich je nach angewandter Norm und kann einen deutlichen Einfluss auf den DVR-Wert haben. Um bei tiefen Temperaturen eine schnelle Aussage zu gestatten, ist eine im Vergleich zu genormten Methoden deutlich schneller durchzuführende, automatisierte Methode entwickelt und mit Standardmethoden verglichen worden. Durch kontinuierliche Messung des Druckverformungsrests kann die Kinetik der Materialrückstellung betrachtet und dadurch ein effizienter Materialvergleich und eine effiziente Materialauswahl ermöglicht werden. Compression set (CS) is especially for sealing applications an important parameter for material selection. It allows an assessment of the time dependent recovery after deformation.
In addition to testing at elevated temperatures which aims at the evaluation of the ageing behaviour, testing at low temperatures permits the determination of the low working temperature limit. The test procedure varies depending on the applied standard and can show a significant effect on the CS value. In order to allow a quick statement regarding low temperatures an automated procedure being significantly faster realisable in relation to the standardised methods has been developed and compared with standard procedures. Continuous measurement of the compression set allows evaluating the recovery kinetics and therefore an efficient comparison and selection of materials.
Epoxy carbon-fibre prepreg, Hexcel Type 6376 HTS, was investigated using Dynamic Mechanical Analysis (DMA). The DMA characteristic parameters are storage modulus E', loss modulus E' and loss factor tanδ. These parameters are ideally suited to observe the vitrification, referred to as glass transition, resulting from the cross-linking reaction. Detection of the cure state may also be achieved by determining the momentary glass transition temperature of partially cured samples. The consequent use of a multi-frequency measuring regime was used to derive the apparent activation energy for the glass transition process. Different temperature programs were also applied to monitor the curing process directly, as well as to investigate the different states of incomplete cure reached in preceding curing steps. The intention was to provide better understanding of the consequences of an interrupted autoclave curing process and to use DMA to detect the cure state achieved. With DMA, the continuation of an incomplete curing process also can be monitored. DMA measurements up to 300 °C showed, furthermore, that the final glass transition temperature was reduced by thermal degradation at high temperatures.