In the rapidly expanding composite industry, novel inspection methods have been developed in recent years. Particularly promising for air-coupled testing are cellular polypropylene transducers which offer better impedance matching to air than piezoelectric transducers. Furthermore, broadband transmitters (laser-induced ultrasound and thermoacoustic emitters) and receivers (optical microphones) have opened a completely new chapter for advanced contact-free ultra-sound inspection. X-ray dark-field radiography offers a different approach to detect porosity and microcracks, employing small angle X-ray scattering. These innovative ultrasonic and radiographic alternatives were evaluated in comparison with well-established inspection techniques. We applied thirteen different non-destructive methods to inspect the same specimen (a carbon fiber-reinforced polymer laminate with induced impact damage): air-coupled ultrasound testing (using piezoelectric transducers, broadband optical microphones, cellular polypropylene transducers, and a thermoa-
coustic emitter), laser-induced ultrasound testing, ultrasonic immersion testing, phased array ultrasonic testing, optically excited lock-in thermography, and X-ray radiography (projectional absorption and dark-field, tomosynthesis, and micro-computed tomography). The inspection methods were qualitatively characterized by comparing the scan results. The conclusions are advantageous for a decision on the optimal method for certain testing constraints.
Air-coupled ultrasound was used for assessing natural defects in wood boards by through-transmission scanning measurements. Gas matrix piezoelectric (GMP) and ferroelectret (FE) transducers were studied. The study also included tests with additional bias voltage with the ferroelectret receivers. Signal analyses, analyses of the measurement dynamics and statistical analyses of the signal parameters were conducted. After the measurement series, the samples were cut from the measurement regions and the defects were analyzed visually from the cross sections. The ultrasound responses were compared with the results of the visual examination of the cross sections. With the additional bias voltage, the ferroelectret measurement showed increased signal-to-noise ratio, which is especially important for air-coupled measurement of high-attenuation materials like wood. When comparing the defect response of GMP and FE sensors, it was found that FE sensors had more sensitive dynamic range, resulting from better s/n ratio and short response pulse. Classification test was made to test the possibility of detecting defects in sound wood. Machine learning methods including decision trees, k-nearest neighbor and support vector machine were used. The classification accuracy varied between 72 and 77% in the tests. All the tested machine learning methods could be used efficiently for the classification.
Luftultraschall
(2020)
Imaging wood defects using air coupled ferroelectret ultrasonic transducers in reflection mode
(2020)
Air-coupled ultrasound (ACU) is used to detect defects in wood panels without physically contacting the sample and with a quick scanning rate. Transducers made of cellular polypropylene (PP) with a high signal-to-noise ratio are quite suitable for ACU testing of wood. The extremely low modulus of elasticity and low density of PP transducers results in a small difference in acoustic impedance for the Transmission of ultrasonic waves between the transducer and air, allowing new areas of application to become possible.
To demonstrate the suitability of the reflection technique, measurements are shown on the three samples Multiplex, LVL, and MDF and compared with transmission measurements. Due to this acoustic barrier and the use of cellular PP transducers, an exact detection of delamination and cavities is possible in wood panels up to 40 mm thick. If only one side of an object is accessible and the depth of the defect is of interest, the reflection technique is preferred at the expense of a reduced measuring accuracy and Penetration depth.