Modified Yoldas sols can be used to prepare crack-free well adherent layers on different substrate materials such as sodalime glass, corundum and metal (IN-718). These layers having thicknesses of 0.6 µm are strain tolerant and withstand thermal cycling between 810 °C and room temperature. Introducing alpha-Al2O3 filler particles into modified Yoldas sols allows the preparation of thicker layers of 1.6 µm, which as well can be thermally cycled without noticeable delaminations. Chemical bonding seems to be the predominant layer bonding mechanism.
Influence of polyvinylpyrrolidone (PVP) on alumina sols prepared by a modified Yoldas procedure
(2008)
Al13 polycations containing alumina sols, prepared by a modified Yoldas procedure were mixed with polyvinylpyrrolidone (PVP). Although Al speciation in freshly prepared sols was not affected by PVP addition the decay rate of Al13 polycations was slightly decreased in PVP-containing sols. PVP does not show any influence on particle size and particle growth. The influence of PVP addition on viscosity and flow behavior of modified Yoldas sols depends on their solids content and NO3-/Al molar ratio.
Alumina coatings with differing phase compositions were deposited on Inconel-718 (IN-718) Ni-base
superalloy substrates using solgel processing. Mass gain measurements served for studying the oxidation
behavior of coated metal surfaces if exposed to 800°C and 900°C for up to 4000 h in static air. Itwas found, that
alumina coatings significantly reduce the oxidation related mass gain of IN-718 even after heating to 900°C
for 4000 h. Transmission electron microscopy (TEM) studies revealed diffusion of elements from the metal
substrate (IN-718) into the alumina coatings and to a much lower degree from the coating into the
substrate. These diffusion processes are greatly influenced by the phase composition of the coatings, especially
by the presence of alpha-alumina.