Flexible organic crystals (elastic and plastic) are important materials for optical waveguides, tunable optoelectronic devices, and photonic integrated circuits. Here, we present highly elastic organic crystals of a Schiff base, 1-((E)-(2,5-dichlorophenylimino)methyl)naphthalen-2-ol (1), and an azine molecule, 2,4-dibromo-6-((E)-((E)-(2,6-dichlorobenzylidene)hydrazono)methyl)phenol (2). These microcrystals are highly flexible under external mechanical force, both in the macroscopic and the microscopic regimes. The mechanical flexibility of these crystals arises as a result of weak and dispersive C−H⋅⋅⋅Cl, Cl⋅⋅⋅Cl, Br⋅⋅⋅Br, and π⋅⋅⋅π stacking interactions. Singly and doubly-bent geometries were achieved from their straight shape by a micromechanical approach using the AFM cantilever tip. Crystals of molecules 1 and 2 display a bright-green and red fluorescence (FL), respectively, and selective reabsorption of a part of their FL band. Crystals 1 and 2 exhibit optical-path-dependent low loss emissions at the termini of crystal in their straight and even in extremely bent geometries. Interestingly, the excitation position-dependent optical modes appear in both linear and bent waveguides of crystals 1 and 2, confirming their light-trapping ability.
Mechanically dual-responsive molecular crystals have gained ubstantial interest among researchers due to their significant applications in various fields. However, incorporation of disparate mechanical responses in the same crystalline material is still a challenging issue and is continuously being explored. Here, we report long acicular crystals derived from 4-bromobenzhydrazide and 9-anthraldehyde exhibit both stressinduced mechanical bending and blue-light induced photomechanical bending. Furthermore, the crystals show thermal back isomerization upon gradual heating. These two distinct mechanical responses in the crystalline phase have been studied and their structure–property correlation have been established.