Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (13)
- Beitrag zu einem Sammelband (11)
- Beitrag zu einem Tagungsband (11)
- Forschungsbericht (3)
- Buchkapitel (1)
- Corrigendum (1)
Referierte Publikation
- nein (40) (entfernen)
Schlagworte
- BAM-Zulassung (5)
- Deponieverordnung (5)
- Geokunststoffe (5)
- POD (4)
- Reliability (4)
- CE-Kennzeichnung (2)
- Deponieabdichtungssysteme (2)
- Drop test (2)
- Glas (2)
- 3-Punkt-Biege-Großprobe (1)
Organisationseinheit der BAM
In accident scenarios of transport packages or hypothetical crashes of containers in a storage facility or repository, the materials resistance against dynamic failure of the involved components is a deciding factor for package and container integrity during the handling, transport and storage for each type of radioactive material. For example, different dynamic impact tests on containers and components like lid sealing systems and specimens made of ductile cast iron and shock-absorbing materials are carried out by BAM. In order to perform dynamic impact tests with packages and its parts BAM operates two free-fall drop test facilities with maximum capacities of 200 t and 55 t, and a test bench for guided drop tests. This latter drop test machine enables a clearly specified component loading by a precisely positioned test object or drop weight and has been used recently for numerous investigations. The paper gives an overview of the wide range of experimental testing methods carried out within guided Impact and bending tests. Examples of methodological challenges are presented, especially such experimental analysis of dynamic impact conditions. In addition to known applied methods of dynamic, non-contact displacement measurements like high-speed 3-D surface deformation a recently patented 2-D tracking method is presented. By means of in-situ determination of fracture parameters with relevance to the materials stress intensity factor, the method has been successfully applied for a typical specimen geometry. Also shown are the possibility of detecting in-situ He-leakage rates on laterally impact loaded lid sealing systems as well as a method of acceleration sensor-temperature control under test conditions in the low temperature range.
Mechanisms of degradation of concrete by external sufate ions under laboratory and field conditions
(2011)
The durability of concrete is a major challenge for the construction, which devotes one third to one half of its annual investment to building maintenance. The lack of fieid data regarding concrete durability, especially in the case of exposure to Sulfate ions (“sulfate attack”) makes it dijficult to determine the appropriate fest methods andperformance criteria. Additionally, the increased use of sustainable blends (cement with mineral admixtures, typically slag from the iron industiy) suffers from a lack of experience regarding their long-term performance. Most results for sulfate resistance are derived from accelerated laboratoiy tests xvhere performance criteria are based only on macroscopic properties, especially expansion. To fill this gap and better widerstand the mechanisms of sulfate attack under real conditions, a parallel study of laboratoiy micro-concrete and fieid concrete samples under sulfate exposure was undertaken, focussing on microstructural changes in addition to the conventional macroscopic characterisation.
Four exposure regimes were designed in the laboratoiy: full immersion (ponding), pH-control, semi-immersion and wet/diy cycles. Pure Portland blends and slag blends witli high level of slag replacement (70 wt.-%) were investigated.
The exposure regime has been found to play a major role in the damage process. In ponding conditions, the damage process takes place in three stages characterised by a first period of induction, followed by surface damage thatfinally extends to the bulle of the material. Paradoxically, the w/c-ratio does not seem to have much impact on the ionic transport phenomena but might be more decisive in the microstructure mechanical strength against local stresses. The slag blends, considered as sulfate resistant in ponding exposure, revealed badperformances under wet/diy cycles. This beliaviour was attributed to poor proper physical resistance of the slag hydrates against diying.
The fieid concretes selected for the comparison with the laboratoiy cases were partially buried in a sulfate-enriched soil in Argentina. A pure Portland blend and a slag blends with high level of slag replacement (80 wt.-%) were investigated. The submerged part of the samples could be compared to the laboratoiy ponding exposure, wliile the upper layer of the samples subjected to weathering could be compared to the laboratoiy wet/diy cycles exposure. The fieid obsen’ations tend to confirm the laboratoiy results and validate the fest settings.
It has been underlined that a direct relationship between damage (e.g.; cracking/expansion) andphase assemblage was not evident. However, the study highlights that sulfate combination with the hydrates of the cement (e.g.; C-S-H) and with those of the slag would play a rote in the initiation of the expansion, which would be attributed to a swelling of the hydrates or to the precipitation offine ettringite after the Saturation level in sulfate of the hydrates has been reached.
Deterioration of cementitious materials by sulfate ions is a concern for concrete in contact with ground water (and in a lesser extent sea water) in many parts of Europe, and is an important issue for underground construction identified as a major area for progress in the construction industry. Sulfate resistance relates closely to testing and standardization and therefore to prescriptive approaches. The lack of feed back on the durability of structures made of blended cements makes it difficult to fit these new concretes with existing test methods and performance criteria. This paper concerns the microstructural study of field samples and structures made of blended concretes available across Europe. This concerns several materials exposed to various climate regimes, ranging from Southern to Northern Europe (Spain, Germany, United Kingdom, Denmark and Norway). Complementary techniques such as SEM, micro-XRF, XRD and PIXE are used to evaluate the microstructural performance and stability of the phase assemblage of those blended concretes in the case of sulfate (and chloride in some instances) ingress, compare to pure Portland concrete.