A thorough characterization of base materials is the prereq- uisite for further research. In this paper, the characterization data of the reference materials (CEM I 42.5 R, limestone pow- der, calcined clay and a mixture of these three components) used in the second funding phase of the priority program 2005 of the German Research Foundation (DFG SPP 2005) are presented under the aspects of chemical and min- eralogical composition as well as physical and chemical properties. The data were collected based on tests performed by up to eleven research groups involved in this cooperative program.
α(1 0 0) Dislocations are observed in nickel-base superalloys after creep deformation at high temperatures and low stresses. They are formed in the γ/γ´ interfaces by a three step mechanism. First, primary dislocations with Burgers vector α/2(1 0 1) and 60° character are left behind in the interfaces when dislocation loops glide through the γ channels. The 60° dislocations move into edge orientation and react forming secondary dislocations α/2(1 1 0). In the third step, new primary dislocations are knit into the already existing meshes of primary and secondary dislocations, which results in hexagonal misfit dislocation networks consisting of secondary dislocations α/2(1 1 0) and tertiary dislocations α(1 0 0), both of edge type. This self-organisation process is explained by dislocation theory and crystallography.
Creep deformation accelerates when the α(1 0 0) interfacial dislocations enter the γ´ phase. During their climb towards the opposite interface, they attain a characteristic rectangular shape. This shape and the importance of the α(1 0 0) super dislocations for creep deformation are discussed.
A new technique for investigation of interfacial dislocations in nickel-base superalloys by scanning electron microscopy is presented. At high temperatures the pressure of interfacial dislocations against the γ/γ'-interface causes grooves. This 'fingerprint of the dislocation network' is visualized by deep selective etching, which removes the γ'-phase down to the γ/γ'-interface. Compared with transmission electron microscopy, the proposed method has important advantages: observation of large sample areas, no superposition of dislocations lying in different specimen depths, possibility of three-dimensional view of dislocation configurations, information about the dislocation mobility, reduced time for preparation and visualization. The method can be applied for multiphase materials where the interface is grooved by interfacial dislocations.
Pore annihilation during hot isostatic pressing (HIP) was investigated in the single-crystal nickel-base superalloy CMSX-4 experimentally by interrupted HIP tests at 1288 °C/103 MPa. The kinetics of pore annihilation was determined by density measurement and quantitative metallography. Transmission electron microscopy of a HIPed specimen showed that the pores shrink via dislocation movement on octahedral glide planes. Theoretically pore closure under HIP condition was modelled by the finite element method using crystal plasticity and large strain theories. The modelling gives a similar kinetics of pore annihilation as observed experimentally, however somewhat higher annihilation rate.
The shape of X-ray reflections from the cuboidal γ/γ'-microstructure was investigated. The measurements were performed on the 4th generation single-crystal nickel-base superalloy TMS138. It is shown that reflections from non-cubic crystallographic planes split not only in d-scale due to the different spacing of the γ- and γ'-lattices but also in the pole figure due to the tilting of γ-lattice planes. This tilting results from the elastic distortion of the γ-lattice caused by the γ/γ'-misfit. The results obtained are discussed under the methodical aspect of misfit measurement.