Silver in LTCC - Interfacial reactions, transport processes and influence on properties of ceramics
(2009)
LTCC-Modules with integrated ferrite layers - Strategies for material development and co-sintering
(2009)
The integration of passive components (resistors, capacitors, inductors) into LTCC modules is a challenging task in multilayer ceramics technology. We report on multilayer assemblies consisting of combined layers of ferrite and dielectric LTCC tapes. Ni-Cu-Zn ferrites with maximum shrinkage at 900°C were processed to green tapes and laminated with dielectric LTCC tapes. Cosintering at 900°C led to multilayers with different defects such as incomplete densification of the ferrite layers, cracks, and warpage. Since ferrite tapes do not really allow compositional changes without deterioration of magnetic properties, the dielectric tape was modified with the following objectives: (i) matching of the shrinkage curves of dielectric and ferrite materials, (ii) adjusting the coefficients of thermal expansion to avoid cracking during cooling, and (iii) controlling of interface reactions. Using this concept we fabricated dense and defect-free multilayers consisting of dielectric and ferrite layers. However, compositional changes of the individual ferrite tapes require the development of a specific dielectric tape material with tailored properties.
LTCC-modules with integrated ferrite layers - Strategies for material development and co-sintering
(2008)
Integration of magnetic functional components in LTCC circuit boards calls for co-firing of dielectric and ferrite tapes. Ni-Cu-Zn ferrites with permeability of µ = 900 were fully densified at the standard LTCC sintering temperature of 900°C. Co-firing of this ferrite with dielectric tapes requires the adaptation of the shrinkage behavior of the materials as well as the thermal contraction during the cooling period – especially in the temperature range below the transformation point of the glass phase of the dielectric tape. To match these preconditions, a new dielectric LTCC material with steep sintering curve and high thermal expansion coefficient was designed. Sintered multilayer laminates composed of Ni-Cu-Zn ferrite and tailored dielectric tapes are free of cracks and possess no open porosity. No significant interdiffusion between the ferrite and dielectric tapes was found using microprobe analysis. Pure ferrite laminates show homogeneous microstructure with large grains up to 50 µm in diameter. However, growth of ferrite grains does not take place near the interface between ferrite and release or dielectric tapes. There is a strong correlation between permeability and volume fraction of large ferrite grains. Compared to pure ferrite laminates the permeability of co-sintered Ni-Cu-Zn ferrite layers is drastically reduced to 400, that is a decrease of more than 50%.