Polymers of intrinsic microporosity (PIMs) are promising candidates for the active layer in gas separation membranes due to their high permeability and reasonable permselectivity. These appealing properties originate from a microporous structure as a result of inefficient segment packing in the condensed state due to a combination of a ladder-like rigid backbone and sites of contortion. However, this class of polymers suffers from a significant decrease in the permeability with time due to physical aging, whereby typically, the permselectivity increases. The initial microporous structures approach a denser state via local rearrangements, leading to the reduction of the permeability. Hence, a detailed characterization of the molecular mobility in such materials can provide valuable information on physical aging. In this work, the dielectric behavior of PIM-1 films and their behavior upon heating (aging) were revisited by isothermal frequency scans during different heating/cooling cycles over a broad temperature range between 133 and 523 K (−140 to 250 °C). In addition, the obtained results were compared with data of samples that were annealed at ambient temperatures over different time scales. Multiple dielectric processes were observed: several relaxation processes due to local fluctuations and a Maxwell−Wagner−Sillars polarization effect related to the microporosity. The temperature dependence of the rates of all processes follows the Arrhenius law where the estimated activation energy depends on the nature of the process. The influence of the thermal history (aging) on the processes is discussed in detail.
Polymers with intrinsic microporosity (PIMs) are of great interest in the field of gas separation membranes. Already the first synthesized PIM-1 shows extraordinary permeability and selectivity. Unfortunately, PIM-1 is susceptible to physical aging and thus gradually loses its outstanding properties. In this study a polyhedral oligomeric silsesquioxane with phenethyl substituents (PhenethylPOSS) was used as a nanofiller (0–40 wt%) in the PIM-1 matrix to potentially improve the gas transport properties and prevent physical aging. The molecular mobility of the solution-cast nanocomposite films was analyzed by Broadband Dielectric Spectroscopy (BDS). Furthermore, gas permeability was determined with the time lag method (0–20 bar upstream pressure) at 35 °C for N2, O2, CH4 and CO2.
The increasing demand for energy efficient separation processes fosters the development of new high performance polymers as selective separation layers for membranes. PIM-1 is the archetypal representative of the class of polymers of intrinsic microporosity (PIM) which are considered most promising in this sector, especially for gas separations. Since their introduction, PIMs stimulated a vast amount of research in this field and meanwhile evolved to the state of the art in membrane technology for gas separation. The major obstacle for extending the practical membrane application is their strong tendency to physical aging. For the first time, investigations by broadband dielectric spectroscopy (BDS) addressing molecular dynamics and conductivity in PIM 1 are presented. As chain packing during film formation from the casting solution and physical aging are key factors determining the separation performance of PIMs as membrane materials, characterization of the molecular mobility in such materials as revealed by BDS will provide valuable information for further development and optimization.