Filtern
Dokumenttyp
- Beitrag zu einem Tagungsband (15) (entfernen)
Referierte Publikation
- nein (15) (entfernen)
Schlagworte
- Schallemissionsanalyse (4)
- Alkali-Kieselsäure-Reaktion (3)
- Polypropylene fibres (2)
- Spalling (2)
- alkali-silica-reaction (2)
- 60° C-Betonversuch (1)
- ASR (1)
- Accelerated concrete prism test (1)
- Acoustic emission (1)
- Alkali-Silica Reaction (1)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (3)
- 7.1 Baustoffe (3)
Untersuchung des Einflusses der Gefügedichte von Betonen auf die AKR mit neuartiger Prüftechnik
(2011)
It has been shown in fire tests that polypropylene fibres reduce or avoid explosive spalling of high performance concrete. In the critical temperature ränge up to 300 °C the permeability of HPC increases by using polypropylene fibre. Due to this the water vapour, which is the main reason for explosive spalling, can escape. There exist different theories in the literature conceming the micro structural mechanisms, which cause an increase in the permeability. Within the framework of an internal research project at BAM an innovative methodology was developed for experimental verifying of existing theories and to get new insights into this problem The methodology used is unique and has been undertaken here for the first time. This consists of the combination of acoustic emission and ultrasonic measurement during temperature loading and the non-destructive micro structural analysis of cooled down samples with the aid of micro X-ray computed tomography. For the validation of the nondestructive test methods scanning electron microscopic images of prepared samples were undertaken. The results show that due to the thermal decomposition of the polypropylene fibres micro canals emerge. These are connected due to a simultaneous micro cack formation.
Although concrete in general is a non-combustible material, the fire resistance of concrete structures depends, to a large extent, on the mechanical material behaviour. Fire tests have shown that SCC is often susceptible to explosive spalling due to fire exposure, in a similar manner to HPC. But there are hardly any studies available that report properties of specimens at high temperatures.
Vom Baustoff zum sicheren Bauwerk: Einsatz der Schallemissionsanalyse in der Bauabteilung der BAM
(2013)
Seit 2006 wird die Schallemissionsanalyse (SEA) in der Abteilung 7 Bauwerkssicherheit der BAM genutzt, um Gefügeveränderungen in Betonen zu untersuchen. Dabei haben sich bis heute im Wesentlichen folgende vier Forschungsbereiche herauskristallisiert:
Hydratation
Während der Hydratation von Beton ist eine ausgeprägte Schallemissionsaktivität zu beobachten, anhand derer der Hydratationsverlauf nachvollzogen werden kann. Zur Aufklärung der Quellmechanismen der Schallemissionen besteht noch weiterer Forschungsbedarf. Des Weiteren kann mit Hilfe der SEA die frühe Rissbildung in Betonen, hervorgerufen durch autogenes oder plastisches Schwinden, analysiert werden.
Alkali-Kieselsäure-Reaktion (AKR)
Bei der AKR handelt es sich um eine Reaktion alkaliempfindlicher Gesteinskörnungen mit den Alkalien des Betons bzw. mit extern, z.B. durch Tausalze, zugeführten Alkalien. Dabei werden um die oder in der Gesteinskörnung quellfähige Gele gebildet, die zu einer völligen Zerstörung des Gefüges führen können. Mit der SEA können die Rissbildung detektiert und somit die Schädigungsphasen im Verlauf der AKR identifiziert werden.
Brandverhalten
Unter Brandeinwirkung platzt die Oberfläche gefügedichter Hochleistungsbetone explosionsartig ab. Um dies zu verhindern und somit den Feuerwiderstand von Bau-teilen aus Hochleistungsbeton zu erhöhen, werden dem Beton Polypropylenfasern beigemischt. Das Schmelzen der Fasern bei einer Temperaturerhöhung trägt zu einer erhöhten Mikrorissbildung bei, die einen Spannungsabbau ermöglicht. Die SEA konnte erfolgreich eingesetzt werden, um diesen Wirkmechanismus der Fasern nachzuweisen und weiter aufzuklären.
Ermüdungsverhalten
Durch die hohen zyklischen Lasten, für die Türme und Fundamente von Windkraft-anlagen ausgelegt werden müssen, gewinnen gesicherte Kenntnisse über das Ermüdungsverhalten von Betonen an Bedeutung. Mit der SEA ist es bei hochzyklischen Belastungsversuchen an Betonen möglich, den Schädigungsgrad im Verlauf der Beanspruchung zu bestimmen. Die Schallemissionsaktivität eignet sich als Kriterium, um die Versuche bei vorab definierten Schädigungsgraden zu unterbrechen und so Proben für weitergehende Untersuchungen zu gewinnen. Diese Ergebnisse sollen perspektivisch für Überwachungssysteme für Betonbauwerke unter zyklischer Beanspruchung genutzt werden.
In recent years the German motorway network has seen an increase in the occurrence of damage to concrete road surfaces which can be attributed to the alkali-silica reaction (ASR). In view of the often drastically reduced life expectancy of road surfaces due to ASR, research activity in this field has notably increased. Alongside preventative measures in concrete technology, the main research focus up to now has been the development of performance-oriented testing procedures for ASR prevention. This included more specifically the accelerated simulation of climatic effects and external alkali penetration on road surfaces. The effects of mechanical pre-damage resulting from cyclic traffic loading and climatic impact had previously not been taken into consideration. Since 2011, the five-partner research group 1498 sponsored by the German Research Foundation (DFG) has been pursuing research on how simultaneous cyclic loading and external alkali penetration impacts destructive ASR in road surface concretes. The depiction of the myriad degradation and transport processes necessary for an understanding of these effects requires close interaction between experiments and their multi-scale modelling. This paper aims to focus on the aforementioned experiments by means of innovative testing techniques. The research is founded on a series of cyclic fatigue tests performed on large-format beams, both with and without previous application of a sodium chloride (NaCl) solution, with simultaneous tracking of crack development. Subsequently, smaller test specimens were extracted from the pre-damaged beams for further experiments. These included the spatial visualization and quantification of fatigue-induced cracks using micro X-ray 3D-computed tomography (3D-CT). Additionally, the effects of fatigue-induced cracks on alkali transport were investigated using Laser-Induced Breakdown Spectroscopy (LIBS). Subsequent storage of the small-format test specimens, with and without cyclic pre-damage, in an ASR-conducive environment then provided initial findings on the influence of fatigue-induced predamage on the ASR.
The susceptibility of different aggregate types used in concrete to ASR is strongly associated with their petrography. The aim of this study is to assess the influence of the aggregate size on the ASR potential, in particular applied to the sand fractions in the size range of 0.125-4 mm. The investigation concept is based on the hypothesis that at a specific particle size reactive aggregates could change their characteristic influence in mitigating ASR instead of promoting it. For the study of the size dependent behaviour mortars are prepared, considering aggregates of different reactivity, including very reactive, slow-late and quasi non-reactive types. The analysis is based on a stepwise substitution concept, in which mortars with a constant overall grain size distribution are compared, while only one size fraction of the non-reactive base aggregate is substituted by a reactive aggregate type of this specific size fraction. For the expansion experiments an accelerated mortar bar test (80°C, immersed in NaOH solution) was applied. The results show that the slow-late reactive greywacke yielded a strong reduction of the expansion below an aggregate size in the range of 0.5-1 mm. On the other side with the very reactive borosilicate glass, the expansions increased steadily with decreasing size. To validate if the acquired expansions were caused by ASR, thin sections were analysed. Mainly, higher expansion values were consistent with extensively more amounts of ASR indicators.
ln den letzten Jahren sind im deutschen Bundesautobahnnetz verstärkt Schäden an Betonfahrbahndecken aufgetreten, die mit einer Alkali-Kieselsäure-Reaktion (AKR) in Verbindung gebracht werden. Die damit einhergehende oft drastische Reduzierung der Nutzungsdauer der Betonfahrbahndecke führte zu einer starken Intensivierung der Forschung auf diesem Gebiet. Zentraler Forschungsgegenstand war bisher neben der Suche nach geeigneten präventiven betontechnologischen Maßnahmen vor allem die Entwicklung performanceorientierter Prüfverfahren zur AKR-Prävention. Dabei wurden insbesondere die klimatischen Einwirkungen auf die Betonfahrbahndecke und der externe Alkalieintrag zeitraffend simuliert. Die zusätzlich interagierenden mechanischen Einwirkungen aus dem Verkehr fanden bisher keine Berücksichtigung. Vor diesem Hintergrund verfolgt die 2011 eingerichtete und 2015 um weitere drei Jahre verlängerte DFG-Forschergruppe 1498 u. a. das Ziel, den Einfluss einer mechanisch induzierten Vorschädigung (Ermüdungsbeanspruchung) auf den AKR-Schädigungsprozess zu klären. Die hierfür erforderliche Beschreibung der vielfältigen interagierenden Schädigungs- und Transportprozesse erfordert eine enge Verknüpfung von Experimenten mit einer mehrskaligen Modellierung. Die experimentelle Basis bildet die mechanische Vorschädigung (Ermüdung) großformatiger Balken aus einem Fahrbahndeckenbeton mit einem erhöhten AKR-Schädigungspotenzial. Aus diesen Balken werden nach der Ermüdungsbeanspruchung kleinformatige Probekörper gewonnen, an denen die Auswirkungen der mechanischen Vorschädigung auf das Betongefüge und die interagierenden Transport- und Schädigungsprozesse analysiert werden. Das Teilprojekt der SAM hat in diesem Kontext die Aufgabe, ganzheitlich die Rissbildungsprozesse und den interagierenden Eintrag bzw. Auslaugung der Alkalien von der mechanisch induzierten Vorschädigung bis zum AKR-Schädigungsprozess in enger Abstimmung mit den Forschungspartnern zu untersuchen. Den Schwerpunkt dieses Beitrags bildet die Charakterisierung der Rissbildungsprozesse durch die mechanische Vorschädigung und ihrer Auswirkungen auf die interagierenden Transportprozesse. Das schließt die Vorstellung der hierfür angewandten innovative Prüftechniken und Prüfmethodologien ein.