The need of clean water and the water-poor are increasing daily in the world. In addition, we are facing a dramatic increase in the industrial pollutions of rivers and groundwater, which led us to find a new way to treat industrial pollutants. The plasma discharge technique is one of the important, safe, and applicable for industrial wastewater decontamination. Decolorization of Brilliant Blue R (BBR) dye as a hazard material was noticed when the contaminated solution was exposed to the plasma discharge technique. The combination between the nonthermal plasma and catalysts was evaluated in this work to optimize the degradation efficiency. The PVDF/(MWCNTs/TiO2) as three system composites was employed to enhance the nonthermal plasma performance. The surface area, phase purity, shape, and photonic efficiency were characterized employing XRD, FTIR, SEM, DSC, and UV–Vis. techniques. The obtained results of degradation using NTP technique in presence of the PVDF/MWCNTs catalyst have been enhanced the BBR dye degradation by 19% than only plasma treatment for 20 min.
The durability processes of prepared PVDF/(MWCNTs/TiO2) was investigated and evaluated until 8 solar photocatalytic process repeating times.
For the first time, structure−electrochemical relationships of thin films of a plasma-polymerized acrylic acid/carbon dioxide AA/CO2 (75/25%) copolymer modified by implanted silver nanoparticles are discussed. The pulsed plasma polymerization of AA/CO2 was utilized and adjusted to obtain a maximal amount of COOH Groups forming an almost uncross-linked polymer structure. The prepared polymer layer is rinsed by a silver nitrate solution to impregnate Ag+ ions. This step is followed by its reduction of Ag+ with NaBH4 as a chemical route in comparison to the reduction by sunlight as an ecofriendly photoreduction method. The chemical composition and morphology of the topmost surface layer of the AA/CO2 polymer thin film were investigated by X-ray photoelectron spectroscopy and atomic force microscopy. Moreover, the molecular mobility, conductivity, and thermal stability of the polymer layer were analyzed using broadband dielectric spectroscopy. The dielectric properties of the AA/
CO2 polymer thin film were studied in the presence of Ag+ ions or Ag0. It was found that a cross-linked polymer layer with a smooth surface and high conductivity was obtained in the presence of Ag+/ Ag0.