Underground sealing structures are necessary to seal radioactive or toxic waste in underground repositories. A special version of MgO concrete is used in the mine in Teutschenthal and applied at a large-scale test with the aim to provide a low permeability barrier. The test structures (up to 10 m long) were created by shotcreting. Besides destructive tests, non-destructive ultrasonic measurements have been evaluated for quality assurance to monitor potential anomalies such as cracks, concrete inhomogeneities, and delamination. We show results of ultrasonic measurements with a multi-transducer system used at the front and from the side of the concrete structure. Images are obtained by synthetic aperture focusing techniques. The boundaries between concreting sections are not visible in the ultrasonic images systematically so that a successful concreting is assumed, which is confirmed by the low permeabilities observed. Several reflectors up to a depth of 1.2 m are identified and interpreted as potential damages in the concrete. Phase analysis of prominent reflectors reveal a negative impedance contrast thus indicating air filled voids, cracks or delamination. Boreholes through some of the identified reflectors are used to verify the results from ultrasonic measurements. Additionally, an experiment with incorporated artificial defects was undertaken to analyse the reliability of the applied methods. Overall, the conducted tests show the potential of ultrasonic measurements to detect critical anomalies. Despite challenges at small-scale structures (cm-order), large-scale anomalies can be identified. Consequently, implementing ultrasonic monitoring during and after the construction of concrete sealing structures has shown its potential as a tool for quality assurance, but needs further development and validation.
Ultrasonic transmission measurements are used to monitor concrete elements mostly on a laboratory scale since decades. Recently, coda wave interferometry, a technique adapted from seismology, has been introduced to civil engineering experiments. It can be used to reveal subtle changes in concrete samples and even large construction elements without having a transducer directly at the location where the change is taking place. The methodology works best with embedded transducers to avoid coupling issues or excessive environmental influence. These transducers can be used for newly built and existing structures. Recently, large concrete beams have been equipped with a network of transducers and loaded until failure. Using code wave interferometry, it was possible to visualize stress fields and damaged areas. This paper gives an overview of the state of the art, recent results achieved at BAM and a task list for further results and development.
Ultrasonic transmission measurements are used to monitor concrete elements mostly on a laboratory scale since decades. Recently, coda wave interferometry, a technique adapted from seismology, has been introduced to civil engineering experiments. It can be used to reveal subtle changes in concrete samples and even large construction elements without having a transducer directly at the location where the change is taking place. The methodology works best with embedded transducers to avoid coupling issues or excessive environmental influence. These transducers can be used for newly built and existing structures. Recently, large concrete beams have been equipped with a network of transducers and loaded until failure. Using code wave interferometry, it was possible to visualize stress fields and damaged areas. This paper gives an overview of the state of the art, recent results achieved at BAM and a task list for further results and development.
Previous work has shown that ultrasonic monitoring using externally applied or embedded transducers and imaging methods based on coda wave interferometry are able to detect subtle changes in concrete elements. In this study, a limited number of embedded transducers has been used to monitor changes in several 12 m long two-span concrete beams subjected to point or linear loads until failure.
The ultrasonic results showed the high sensitivity to stress changes and the nonlinear character of the associated effects. However, the ultrasonic features showed a very good correlation to several conventional monitoring parameters. For higher loads (significant amount of cracking), the technique had to be modified to cope with large wave velocity variations and high decorrelation compared to the reference signal.
Using a very simple imaging procedure, the 2D stress field inside the beam has been visualized including inhomogeneities and artifact at places where cracking occurred at higher loads. The technique has the potential to be included in real time monitoring systems.
Ultrasonic transmission measurements are used to monitor concrete elements mostly on a laboratory scale since decades.
Recently, coda wave interferometry, a technique adapted from seismology, has been introduced to civil Engineering experiments. It can be used to reveal subtle changes in concrete samples and even large construction elements without having a transducer directly at the location where the change is taking place. The methodology works best with embedded transducers to avoid coupling issues or excessive environmental influence. These transducers can be used for newly built and existing structures. Recently, large concrete beams have been equipped with a network of transducers and loaded until failure. Using code wave interferometry, it was possible to visualize stress fields and damaged areas.
Ultrasonic non-destructive testing methods have found various applications in quality assurance and condition assessment of nuclear concrete structures. This includes but is not limited to the localization of construction features (thickness measurements, reinforcement, tendon ducts, and others) and damage detection (e. g. corrosion or cracks). However, there are still limitations, e. g. limited penetration depth and resolution, issues when testing hybrid steel/concrete structures as well as absence of standards and regulations.
This presentation will show progress in some of these issues and will focus on advanced instrumentation and validation of ultrasonic NDT for concrete structures.
Ultrasonic echo testing has been limited to a penetration depth of less than one meter in reinforced concrete. The development of the LAUS (Large Aperture Ultrasonic System), using a large array of ultrasonic transducers and wider offsets between transmitter and receiver, allows to reach up to 5 m in reinforced concrete and 9 m in unreinforced concrete. This capability has been demonstrated by collecting data from an engineered salt concrete barrier in an underground nuclear waste storage facility. Due to an increasingly competitive environment, commercial manufacturers will continue to develop equipment with enhanced penetration and/or increased resolution.
To quantify the capabilities and reliability of ultrasonic tests, validation mockups with engineered flaws are required. EPRI and BAM have built a large-scale mockup at a test site close to Berlin (BAM-TTS, Horstwalde) using a design which is repeated at other places. This presentation will also cover the methods deployed on engineered flaws and the repeatability of the test results.
Ultrasonic monitoring, making use of the sensitivity of the coda of repeated transmission meas-urements to changes in stress, temperature, moisture, as well as localized or distributed damage, has gotten at-tention in structural health monitoring (SHM) research recently. Analysis methods such as coda wave inter-ferometry (CWI), including its nonlinear extension, have been shown to be able to measure ultrasonic wave velocity changes with a 1∙10-5 resolution, while indicators such as cross-correlation or cross-coherence have been used to distinguish between reversible and irreversible changes. Several small- and large-scale laboratory experiments have demonstrated that stress changes in structures can be captured or damage detected in a very early stage. The use of this technique for pre-warning before failure are currently under investigation, as well as detailed research on the physical causes and the connection between ultrasonic wave properties and materi-al/structural behavior. Recently, several of large-scale laboratory and real structures have been instrumented with embedded ultrasonic transducers to gather experience and evidence on how to use this technology in re-al-world applications. Preliminary results from installations on a new bridge, an existing bridge, a tunnel, a la-boratory earthquake test as well as a historic stadium in Germany, Poland, and the United States, respectively, are presented. Environmental influences (mainly temperature) and validation by load tests are discussed.
Due to the importance of reinforced concrete structures for modern society, damage assessment during the entire life-cycle of such structures has become a special interest in non-destructive testing. Using embedded ultrasound sensors in combination with other measurement methods, numerical modeling and self-made data collectors, tailored specifically for monitoring tasks, the German research group DFG FOR CoDA aims to investigate and develop novel methods for damage detection and rapid model updating in reinforced concrete structures. In the first stage of the project, besides the development of custom-built, low-cost data collectors, ultrasonic transducers are embedded in a large, reinforced concrete specimen on a BAM test site near Berlin. In this experiment, the influence of changing environmental conditions (mainly temperature) on the ultrasound signal is investigated using coda-wave interferometry. The results show a correlation between changes in temperature and ultrasonic velocity. Such changes must be taken into consideration in a long-term monitoring setup to distinguish between reversible and permanent changes. By correcting the data using a linear relation between concrete temperature and velocity change to remove the seasonal trends and by low-pass filtering the data to remove daily variations can remove most of the temperature influence on the ultrasound measurements.