Tungsten-tungsten carbide (W/W2C) composites are considered as possible structural materials for future nuclear fusion reactors. Here, we report on the effect of helium (He) implantation on microstructure evolution of polycrystalline W/W2C composite consolidated by field-assisted sintering technique (FAST), homogenously implanted at room temperature with 1 MeV 4He+ ions at the fluence of 8 × 1016 ions cm−2 and annealed at 1873 K for 20 minutes. Samples were analysed by scanning and transmission electron microscopy to study the presence and size of He bubbles. Monomodal He bubbles in W (30-80 nm) are limited to point defects and grain boundaries, with a considerable void denuded zone (150 nm). Bubbles do not form in W2C, but at the W|W2C interface and are considerably larger (200-400 nm). The experimental observations on He behaviour and migration in W and W2C were assessed by density functional theory (DFT) calculations, suggesting He migration and accumulation in the composite are determined by the effective He-He binding in clusters, which will give rise to decohesion. In the presence of He clusters, the decohesion of bulk W into free surfaces is energetically highly favourable but not sufficient in the W2C; hence bubbles are only observed in W grains and interfaces and not within bulk W2C.
The embrittlement of metallic alloys by liquid metals leads to catastrophic material failure and severely impacts their structural integrity. The weakening of grain boundaries by the ingress of liquid metal and preceding segregation in the solid are thought to promote early fracture. However, the potential of balancing between the segregation of cohesion-enhancing interstitial solutes and embrittling elements inducing grain boundary decohesion is not understood. Here, we unveil the mechanisms of how boron segregation mitigates the detrimental effects of the prime embrittler, zinc, in a Σ5 [0 0 1] tilt grain boundary in α −Fe (4 at.% Al). Zinc forms nanoscale segregation patterns inducing structurally and compositionally complex grain boundary states. Ab-initio simulations reveal that boron hinders zinc segregation and compensates for the zinc induced loss in grain boundary cohesion. Our work sheds new light on how interstitial solutes intimately modify grain boundaries, thereby opening pathways to use them as dopants for preventing disastrous material failure.