A new application of neutron transmutation doping is described. The method is useful to prepare graded zinc contents in highly pure copper materials. The research reactor BER II at the Hahn-Meitner-Institute, Berlin served as a neutron source. The zinc content produced in the samples was analyzed by determining the 65Zn-activity via gamma-spectrometry. Simultaneously irradiated flux monitors were used to determine the neutron flux density. Since cylindrical sample geometries are favorable for a reference material application in optical emission (OE) spectroscopy, the spatial distribution of the induced activity in a cylinder with a diameter of 8 mm and a length of 35 mm was investigated.
The ?- branching ratio of 64Cu was determined by investigating the resulting decay products in copper doped by neutron transmutation. The numbers of 64Zn and 64Ni atoms were analyzed using isotope dilution analysis combined with thermal ionization mass spectrometry. A ?- branching ratio of (38.06±0.30)% was obtained, which agrees with the study of Kawada (Appl. Radiat. Isot. 37 (1) (1986) 7) to a higher accuracy. However, our result differs from the value cited in the NUDAT database of (39.0±0.3)%.
A set of ten calibration materials based on acrylonitrile-butadiene-styrene terpolymer (ABS) containing the elements Br, Pb, Cd, Cr, and Hg was produced in order to control polymer samples in regard to the restriction on the use of certain hazardous substances (RoHS) directive. The materials were produced with respect to the special demands of X-ray fluorescence analysis (XRF) and inductively coupled plasma mass spectrometry in combination with laser ablation (LA-ICP-MS).
The mass fractions of all elements were 0-1500 mg/kg and the materials were produced as granulates and solid discs with a diameter of 40 mm and thicknesses of 1, 2, and 6 mm. It could be shown that the signals measured by XRF strongly depend on the thickness of polymeric samples.
Macroscopic homogeneity was assessed with XRF measuring a total of 180 samples. The microscopic homogeneities were determined for a material with average elemental mass fractions with the aid of synchrotron radiation (SR) µ-XRF and LA-ICP-MS. Sufficient macroscopic and microscopic homogeneities for all elements could be achieved. It was observed that organic additives show a better homogeneity than oxides.
XRF and LA-ICP-MS were successfully calibrated with the new materials. Limits of detection were in the range of 0.4-22 mg/kg for XRF and 2.3-26.8 mg/kg for LA-ICP-MS. The materials are considered as candidate reference materials (RM) by the Federal Institute of Materials Research and Testing (BAM, Germany).
In this study the microscopic homogeneity of the newly developed plastic reference materials BAM H001-BAM H010 was investigated. The materials consist of an acrylonitryle-butadien-styrene terpolymer, doped with different amounts of the elements Br, Cd, Cr, Hg and Pb. For the quantitative determination of the degree of homogeneity, a procedure proposed by Kempenaers et al. (Fresenius J. Anal. Chem., 2001, 369, 733-737) was used. On every sample an extensive number of different points were analyzed and standard deviation for every element mentioned above was used to calculate a minimal sampling mass that is necessary to reach a certain level of uncertainty caused by inhomogeneity (mmin,5%). The experiments were taken out with synchrotron µ-XRF (SR µ-XRF) at BESSYII in Berlin and by laser ablation inductively coupled plasma mass spectroscopy (LA-ICP-MS). The calculated values for mmin,5% of both techniques showed comparable results for all elements. It could be shown that the materials are suitable for calibration of micro analytic techniques if at least 64 µg are used.
In activation analysis of traces in small samples, the non-equivalence of the activating radiation doses of sample and calibration material gives rise to sometimes tolerable systematic errors. Conversely, analysis of major components usually demands high trueness and precision. To meet this, beam geometry activation analysis (BEAMGAA) procedures have been developed for instrumental photon (IPAA) and neutron activation analysis (INAA) in which the activating neutron/photon beam exhibits broad, flat-topped characteristics. This results in a very low lateral activating flux gradient compared to known radiation facilities, however, at significantly lower flux density. The axial flux gradient can be accounted for by a monitor-sample-monitor assembly. As a first approach, major components were determined in high purity substances as well as selenium in a cattle fodder additive.
The neutron transmutation doping (NTD) of highly pure copper with zinc was investigated as a promising means of achieving controlled gradation of the zinc content in the range 1-20 wg g-1. The doping process leads to the enrichment of two stable isotopes 64Zn and 66Zn in a ratio which differs from that of natural isotopic distribution. Mass spectrometric investigations by thermal ionization mass spectrometry (TIMS) were performed to validate the results obtained by gamma spectrometry. The investigations included both determination of the isotopic ratios of the doped zinc isotopes and the analysis of the accumulated zinc contents by isotope dilution (ID) analysis. Thereby a sample-specific correction of the blank could be performed because the isotope 68Zn was not influenced, because of the transmutation process. The results obtained by TIMS prove the strict proportionality of the doped zinc content, in the range 5 to 20 wg g-1, to the neutron fluence. Comparison with gamma spectrometric results showed a very good agreement within the uncertainties.