Sewage sludge ashes (SSA) contain up to 13% P and are thus promising raw materials for fertilizer production. However, SSAs also contain heavy metals and the main P-bearing mineral phases whitlockite and aluminium phosphate are poorly bioavailable. We developed and patented a process that produces fertilizers from SSA addressing the above mentioned challenges. SSA is thermo-chemically treated at ~950°C under reducing conditions (reductive: dry sewage sludge) in a rotary kiln together with an alkali compound such as sodium or potassium sulfate, hydroxide or carbonate. Some undesired trace elements such as As, Hg, Pb and Cd are evaporated and separated via off gas treatment system. The poorly soluble phosphates are transformed into calcium alkali phosphates (CaNaPO4 or CaKPO4) that are not water soluble but completely soluble in neutral ammonium citrate solution (NAC). Pot experiments showed that the fertilizer performance of the treated SSA containing calcium alkali phosphates as the single P-bearing mineral phase was comparable to the performance of triple superphosphate. The PNAC-solubility of fertilizer products correlated very well with the resulting contents of calcium alkali phosphates and the P-uptake of plants in pot experiments. The effect of the ratio alkali/P on the PNAC-solubility was investigated by crucible experiments and trial series with a medium scale rotary kiln using different SSAs and alkali phosphates. The effects of operational parameters such as the temperature and the retention time were investigated as well as concurring side reactions of the alkali compounds e.g. with SiO2 present in SSA. The alkali/P ratio must be roughly adjusted at 2 to achieve 100% PNAC-solubility for a common type of SSA. A demonstration trial with an output of 2 t recycling fertilizer was carried out in an industrial rotary kiln (product output 30 kg/h). The PNAC-solubility of the product varied between 60% and 80% during the 4 days campaign showing that the transformation of the mineral P-phases to calcium alkali phosphates was not complete. This was observed although the amount of Na2SO4 additive was dosed according to the results of the pre-investigations. Structure analysis by XRD showed that besides the target compound CaNaSO4 also some Ca3(PO4)2 remained in the SSA as well as some unreacted Na2SO4 additive. Obviously, the conditions in the industrial rotary kiln were not optimal for the process showing that some process aspects have to be reconsidered for the scale-up.
Sewage sludge has one of the highest phosphorus (P) recovery potentials of all waste materials.
Therefore, P-recycling from sewage sludge could contribute to closing the P-cycle. Recently, various thermal processes for P-recovery have been developed, but there is still a demand for information on the effect of different process parameters (e.g. additives and temperature) on P-speciation and especially on the fertilization performance. In the present study, two common methods (low-temperature conversion at 400–500° C and thermochemical treatment at 950° C) were investigated and combined to produce highly bioavailable P-fertilizers from two different types of sewage sludge based on chemical phosphorus precipitation (Chem-P) and enhanced biological phosphorus removal (Bio-P). The results of P-fractionation, X-ray diffraction analysis, and pot experiments with maize showed that Bio-P sludges attain high P-plant-availability after treatment at low temperatures (400° C). In contrast, Chem-P sludges can adequately be treated at higher temperatures under reductive conditions with sodium additives to form highly bioavailable calcium-sodium-phosphate. Additionally, also highly heavy-metal contaminated sludges can be thermochemically treated at high temperatures to achieve the legal requirements for fertilizers.
Sewage sludge has one of the highest phosphorus (P) recovery potentials of all waste materials.
Therefore, P-recycling from sewage sludge could contribute to closing the P-cycle. Recently, various thermal processes for P-recovery have been developed, but there is still a demand for information on the effect of different process parameters (e.g. additives and temperature) on P-speciation and especially on the fertilization performance. In the present study, two common methods (low-temperature conversion at 400–500 °C and thermochemical treatment at 950 °C) were investigated and combined to produce highly bioavailable P-fertilizers from two different types of sewage sludge based on chemical phosphorus precipitation (Chem-P) and enhanced biological phosphorus removal (Bio-P). The results of P-fractionation, X-ray diffraction analysis, and pot experiments with maize showed that Bio-P sludges attain high P-plant-availability after treatment at low temperatures (400 °C). In contrast, Chem-P sludges can adequately be treated at higher temperatures under reductive conditions with sodium additives to form highly bioavailable calcium-sodium-phosphate. Additionally, also highly heavy-metal contaminated sludges can be thermochemically treated at high temperatures to achieve the legal requirements for fertilizers.
Sewage sludge ashes (SSA) contain considerable mass fractions of phosphorus (5-10 w-% P) suitable for fertiliser production. Unfortunately, also most of the heavy metals remain in the ashes. A thermochemical process was developed for the treatment of SSA to i) remove heavy metals and ii) transform phosphates into bio-available mineral phases. The technology was already demonstrated in technical scale (capacity of 300 kg/h) and the company OUTOTEC is currently planning the first industrial plant. In order to manufacture a marketable multi-nutrient fertiliser from the thermochemically treated SSA further wastes and industrial by-products were taken into account. Ammonium sulphate occurs as a by-product of the caprolactam production and was chosen as N-carrier (21 w-% N). Straw ash was tested as potassium carrier (11-15 w-% K). Granulation campaigns were carried out with intensive mixers in lab-, medium-and technical scale. NPS-and NPKS-fertilisers were produced that were characterised by suitable particle size distributions and strength.
Slags from the production of high-alloyed steel contain both chemically bound chromium (mainly as Cr2O3) in the mineral fraction and elemental chromium in the metallic remainders. Thermochemical post treatment of the slag in an electric arc furnace under reducing conditions enables the nearly complete recovery of the total amount of chromium in form of a metallic alloy. The best results were achieved by resistance melting (submerged electrodes) with addition of a reducing agent into the melt. The efficiencies of the reducing agents carbon, aluminium, silicon (as ferrosilicon) and silicon carbide were investigated and compared. As aluminium is the strongest reducing agent, it is less selective and reduces much more SiO2 than Cr2O3. While SiC shows only low reactivity because of its high thermal resistance, carbon and silicon had the highest reducing potentials: More than 97% of the chemically bound chromium can be recovered by application of these reducing agents. Due to the high temperature required for the reduction of the chromium compounds, the reduction of SiO2 as an undesired side reaction cannot be avoided. However, compared with mechanical procedures that are limited to the recovery of the metallic remainders, the total chromium recovery can be significantly increased by the described reductive melting procedure.
Municipal sewage sludge is a carrier of nutrients most important phosphorus (P) but also contains organic pollutants and heavy metals. A two steps thermal treatment based on 1. mono-incineration of sewage sludge under destruction of organic pollutants and 2. thermochemical treatment of the resulting ashes to remove heavy metals and increase P-bioavailability is suggested by the authors. The process aims at P-fertilisers production from sewage sludge. Seven sewage sludge ashes of different origin and composition and one residue from gasification of sewage sludge were thermochemically treated. The raw ashes were mixed with a chlorine donor (e.g. MgCl2) and thermally treated in a gas tight lab-scale rotary furnace. The distributions of the heavy metals between solid and gas phase were determined. The heavy metals concentrations of the treated ashes matched the legislative limits in most cases. The products from thermochemical treatment are suited raw materials for P-fertiliser production. Relevant process parameters such as temperature, type and concentration of Cl-donor and retention time were optimised for the thermochemical treatment step.
Sewage sludge incineration is extensively practiced in some European countries such as the Netherlands, Switzerland, Austria and Germany. A survey of German sewage sludge ash showed that the recovery potential is high, approx. 19,000 t of phosphorus per year. However, the survey also discovered that the bioavailability of phosphorus in the sewage sludge ash is poor and that more than half of the ashes cannot be used as fertilizers due to high heavy metal content. A new thermochemical process for sewage sludge ash treatment was developed that transforms the ash into marketable fertilizer products. Sewage sludge ash was thermochemically treated with sodium and potassium additives under reducing conditions, whereby the phosphate-bearing mineral phases were transformed into plant available phosphates. High P-bioavailability was achieved with a molar Na/P ratio > 1.75 in the starting materials. Sodium sulfate, carbonate and hydroxide performed comparably as additives for this calcination process. Potassium carbonate and -hydroxide have to be added in a molar K/P ratio > 2.5 to achieve comparable P-solubility. The findings of the laboratory scale investigations were confirmed by an industrial demonstration trial for an ash treatment with sodium sulfate. Simultaneously, the volatile transition metal arsenic (61% removal) as well as volatile heavy metals such as cadmium (80%), mercury (68%), lead (39%) and zinc (9%) were removed via the off-gas treatment system. The product of the demonstration trial is characterized by high bioavailability and a toxic trace element mass fraction below the limit values of the German fertilizer ordinance, thus fulfilling the quality parameters for a P-fertilizer.
The Brazilian sugarcane industry produced around 173 million tons (Mt) of bagasse in 2018. Bagasse is a by-product of juice extraction for ethanol and sugar production and is combusted in order to generate power, producing up to 10 Mt of ash per year. This ash contains various concentrations of plant nutrients, which allow the ash to be used as a crop fertilizer. However, the concentration and extractability of phosphorus (P), an essential plant nutrient, are low in bagasse ash. To increase the P content, we co-gasified and co-combusted bagasse with P-rich chicken manure. The resulting ash was thermochemically post-treated with alkali additives (Na2SO4 and K2SO4) to increase the availability of P to plants. We aimed to: (i) investigate the effect of thermochemical post-treatment of co-gasification residue and co-combustion ash on P availability to soybeans, (ii) explore the potential of chemical extraction methods (citric acid, neutral ammonium citrate, formic acid, and Mehlich-I) and diffusive gradients in thin films (DGT) to predict the availability of P to soybeans, and (iii) identify the responsible P-phases using X-ray diffraction . We evaluated P availability to soybeans growing in Brazilian Oxisol soil in two independent greenhouse pot experiments. The positive effect of thermochemical treatment on P availability from gasification residue was confirmed through the observation of increased P uptake and biomass in soybean plants. These findings were confirmed by chemical extraction methods and DGT. The gasification residue contained whitlockite as its main P-bearing phase. Thermochemical post-treatment converted whitlockite into highly soluble CaNaPO4. In contrast, co-combustion ash already contained highly soluble Ca(Na,K)PO4 as its main P-bearing phase, making thermochemical post-treatment unnecessary for increasing P availability. In conclusion, increased extractability and availability of P for soybeans were closely connected to the formation of calcium alkali phosphate. Our findings indicate that this combined methodology allows for the prediction of P-fertilization effects of ash.