Slags from the production of high-alloyed steel contain both chemically bound chromium (mainly as Cr2O3) in the mineral fraction and elemental chromium in the metallic remainders. Thermochemical post treatment of the slag in an electric arc furnace under reducing conditions enables the nearly complete recovery of the total amount of chromium in form of a metallic alloy. The best results were achieved by resistance melting (submerged electrodes) with addition of a reducing agent into the melt. The efficiencies of the reducing agents carbon, aluminium, silicon (as ferrosilicon) and silicon carbide were investigated and compared. As aluminium is the strongest reducing agent, it is less selective and reduces much more SiO2 than Cr2O3. While SiC shows only low reactivity because of its high thermal resistance, carbon and silicon had the highest reducing potentials: More than 97% of the chemically bound chromium can be recovered by application of these reducing agents. Due to the high temperature required for the reduction of the chromium compounds, the reduction of SiO2 as an undesired side reaction cannot be avoided. However, compared with mechanical procedures that are limited to the recovery of the metallic remainders, the total chromium recovery can be significantly increased by the described reductive melting procedure.
Sewage sludge and sewage sludge ashes (SSA) are produced in huge amounts at municipal waste water treatment plants (WWTP) all around the world and have become an issue for many urbanized areas. To deal with this unceasing mass flow in an ecologically and economically responsible way a comprehensive chemical and structural characterization of all types of SSA is needed. X-ray powder diffraction (XRD) is one of the most promising analytical methods for this task. Although, there has been ample chemical evidence showing that many SSA contain aluminium phosphate as a major component up to now no aluminium phosphate or aluminium-rich mixed phosphate phase has been reported to be identified by XRD in a SSA produced at a mono-incineration facility. The outcome of the present com-bined XRD and Mossbauer spectroscopy investigation provides comprehensive evidence closing this gap for the first time.
Evidence is provided that the tridymite component observed in the X-ray diffraction patterns of some sewage sludge ashes (SSAs) should not be interpreted as the tridymite modification of SiO2 but as the tridymite form of AlPO4. This proof is based on a combined X-ray Powder Diffraction (XRD), X-ray fluorescence (XRF) and Mossbauer spectroscopy investigation of two SSAs produced at two fluidized bed incineration facilities, located in different municipalities and operated differently. The structural and chemical characterization was carried out on the 'as received' SSA samples as well as on the residues of these two SSAs pretreated by leaching in citric acid. In addition, direct proof is presented that the tridymite form of AlPO4 does crystallize from X-ray amorphous precursors under conditions that mimic the huge heating rate and short retention time (just seconds at T ≈ 850 °C) typical for fluidized bed incinerators.
For the first time evidence is provided that a nanocrystalline and stacking-disordered, chemically stabilized β-cristobalite form of AlPO4 occurs in a sewage sludge ash (SSA). This proof is based on a combined X-ray powder diffraction and X-ray fluorescence investigation of an SSA produced at a large-scale fluidized bed incineration facility serving a catching area with a population of 2 million. The structural and chemical characterization was carried out on 'as received' SSA samples as well as on solid residues remaining after leaching this SSA in sodium hydroxide solution. Thus, it was ascertained that the observed nanocrystalline and stacking-disordered cristobalite-like component belongs to the aluminum phosphate component of this SSA, rather than to its silicon dioxide component. In addition, a direct proof is presented that the chemically stabilized β-cristobalite form of AlPO4 does crystallize from X-ray amorphous precursors under conditions that mimic the huge heating rate and short retention time (just seconds at T ≈ 850°C), typical for fluidized bed incinerators.
This paper reports the first successful synthesis and the structural characterization of nanocrystalline and stacking-disordered β-cristobalite AlPO4 that is chemically stabilized down to room temperature and free of crystalline impurity phases. Several batches of the title compound were synthesized and thoroughly characterized by X-ray powder diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy, selected area electron diffraction, energy dispersive X-ray spectroscopy mapping in SEM, solid-state 31P nuclear magnetic resonance (31P-NMR) spectroscopy including the TRAPDOR method, differential thermal analysis (DTA), gas-sorption methods, optical Emission spectroscopy, X-ray fluorescence spectroscopy, and ion chromatography. Parameters that are critical for the synthesis were identified and optimized. The synthesis procedure yields reproducible results and is well documented. A high-quality XRD pattern of the title compound is presented, which was collected with monochromatic copper radiation at room temperature in a wide 2θ range of 5°–100°.
The present study shows the potential of high-resolution imaging and nano-Fourier-transform infrared (nano-FTIR) spectroscopy for corrosion science. The protective oxidation layers of different chlorine-gas treated silicon
carbides (SiCs) were characterized with these techniques. A nitrified SiC showed the highest resistant strength against chlorine corrosion at 1000 °C compared to the other SiCs. Nano-FTIR spectroscopy with a lateral resolution below 40 nm detected differences in the crystallinity of the bulk-SiC and in the transitional region to the protective layer. Furthermore, high-resolution imaging provides deep insight in the interfacial layer between bulk-SiC and the protective oxidation layer on sub-micrometer scale.
Gegenstand dieser Arbeit ist die Untersuchung eines bestehenden pyrometallurgischen Prozesses zur Rückgewinnung von Tantal und Niob aus metallurgischen Reststoffen mit vorwiegend niedriger Wertstoffkonzentration.
Zur näheren Erforschung der im vorliegenden Stoffsystem ablaufenden Reduktionsprozesse wurden in einem Elektrolichtbogenofen Schmelzversuche im Pilotmaßstab durchgeführt. Als Reduktionsmittel diente Koks, welcher mithilfe einer Argon-gespülten Eisenlanze in die flüssige mineralische Schmelze eingebracht wurde. Während der Reduktionsbehandlung werden Refraktärmetalle wie Tantal und Niob in ihre Carbide überführt und anschließend in der erschmolzenen eisenbasierten Metallphase am Boden des Reaktors angereichert. Neben Tantal und Niob gelangt auch ein Teil des im Einsatzmaterial enthaltenen Titans als unerwünschtes Begleitelement in die Metallphase.
Sein Großteil verbleibt jedoch als Oxid in der Schlacke und wird dort hauptsächlich im Mineral Perowskit (CaTiO3) gebunden. Die erstarrten Schlackeproben wurden mit verschiedenen Methoden wie Röntgenfluoreszensanalyse, Röntgenbeugung und Rasterelektronenmikroskopie mit gekoppelter energiedispersiver Röntgenanalyse untersucht, um die Bildung tantalhaltiger Mineralphasen zu verschiedenen Stadien des Reduktionsprozesses zu verfolgen.
Die hier gewonnenen Erkenntnisse zeigen, dass weniger die durch das Einblasen von Koks verursachte Reduktionsreaktion, sondern das Absinken der tantalreichen Eisentröpfchen in der flüssigen mineralischen Schmelze, gefolgt von ihrer Anreicherung in die Metallphase, für die Kinetik ausschlaggebend ist.
Da das Recycling von tantalhaltigen Post-Consumer-Abfällen praktisch nicht existiert, stellen metallurgische Reststoffe eine äußerst wichtige Rohstoffquelle für das Tantalrecycling dar. Die meisten Zinnerze enthalten von Natur aus erhebliche Mengen an Refraktärmetallen. Diese Elemente werden in den Schlacken der pyrometallurgischen Primärzinngewinnung angereichert. Aufgrund ihrer vergleichsweise hohen Wertstoffkonzentration und ihrer Funktion als zusätzlicher Schlackenbildner stellen diese Schlacken einen wertvollen Rohstoff für die Verhüttung tantalhaltiger Reststoffe dar. In der vorliegenden Arbeit wird ein existierendes Verfahren zur Tantalrückgewinnung diskutiert, dem hauptsächlich pyrometallurgische Rückstände geringer Wertstoffkonzentration als Einsatzstoff dienen. Mit Hilfe des Verfahrens sollte dasoxidisch vorliegende Tantal vollständig reduziert und in der Metallphase angereichert werden. Weiterhin sollte vermieden werden, dass unerwünschte Elemente wie Titan in die Metallphase überführt werden. Ziel der Untersuchung war es, die ablaufenden Reduktionsprozesse besser zu verstehen, um so Ansätze für die Prozessoptimierung identifizieren zu können.
Basic oxygen furnace slags (BOFS) are by-products of the steelmaking process. Several researchers have studied the production of Portland cement clinker and metallic iron from BOFS via a reductive treatment.
In this study, we applied a carbothermal reduction of BOFS in a technical-scale electric arc furnace and characterised the clinker-like products. Those clinker-like non-metallic products (NMPs) had a chemical and mineralogical composition comparable to clinker for ordinary Portland cement (OPC) and contained large elongated alite crystals as major component. The pure NMPs reacted more slowly and achieved a lower degree of hydration compared with commercial OPC.
If the reactivity of the products can be further increased by employing specific adaptations, it can be used as a full clinker substitute for OPC. Nevertheless, it is also an option to use the material without further modifications as a cement component or concrete addition, which contributes to the strength development in both cases.