Filtern
Dokumenttyp
- Zeitschriftenartikel (9)
- Beitrag zu einem Tagungsband (3)
- Vortrag (1)
Schlagworte
- Neutron diffraction (3)
- Residual stress (3)
- Computed tomography (2)
- Eigenspannungen (2)
- IN718 (2)
- Additive Fertigung (1)
- Additive Manufacturing (1)
- Additive manufacturing (1)
- Aluminium matrix (1)
- Bitter technique (1)
Organisationseinheit der BAM
- 8 Zerstörungsfreie Prüfung (6)
- 8.5 Röntgenbildgebung (6)
- 5 Werkstofftechnik (3)
- 5.0 Abteilungsleitung und andere (2)
- 9 Komponentensicherheit (2)
- 9.4 Integrität von Schweißverbindungen (2)
- 5.2 Metallische Hochtemperaturwerkstoffe (1)
- 8.4 Akustische und elektromagnetische Verfahren (1)
- 9.2 Versuchsanlagen und Prüftechnik (1)
Eingeladener Vortrag
- nein (1)
Background Due to physical coupling between mechanical stress and magnetization in ferromagnetic materials, it is assumed in the literature that the distribution of the magnetic stray field corresponds to the internal (residual) stress of the specimen.
The correlation is, however, not trivial, since the magnetic stray field is also influenced by the microstructure and the geometry of component. The understanding of the correlation between residual stress and magnetic stray field could help to evaluate the integrity of welded components.
Objective This study aims at understanding the possible correlation of subsurface and bulk residual stress with magnetic stray field in a low carbon steel weld. Methods The residual stress was determined by synchrotron X-ray diffraction (SXRD, subsurface region) and by neutron diffraction (ND, bulk region). SXRD possesses a higher spatial resolution than ND. Magnetic stray fields were mapped by utilizing high-spatial-resolution giant magneto resistance (GMR) sensors.
Results The subsurface residual stress overall correlates better with the magnetic stray field distribution than the bulk stress.
This correlation is especially visible in the regions outside the heat affected zone, where the influence of the microstructural features is less pronounced but steep residual stress gradients are present.
Conclusions It was demonstrated that the localized stray field sources without any obvious microstructural variations are associated with steep stress gradients. The good correlation between subsurface residual stress and magnetic signal indicates that the source of the magnetic stray fields is to be found in the range of the penetration depth of the SXRD measurements.
Room temperature mechanical behavior of extruded Mg–Y–Zn alloys with varying fractions of LPSO phase was studied in tension and compression along the extrusion direction. The microstructure is characterized by elongated LPSO fibers along the extrusion direction within the magnesium matrix. Moreover, the magnesium matrix presents a bimodal grain structure with dynamically-recrystallized grains and deformed, elongated grains with the basal plane parallel to the extrusion direction. The beginning of plasticity depends on the volume fraction of deformed and DRX grains. Alloys with low volume fraction of LPSO phase(o10vol%),with a high volume fraction of deformed grains, show the typical behavior of extruded magnesium alloys where yield stress in tension is higher than in compression. This effect is, however, reversed as the volume fraction of the LPSO phase increases since DRX grains are majority.
Room temperature mechanical behavior of extruded Mg–Y–Zn alloys with varying fractions of LPSO phase was studied in tension and compression along the extrusion direction. The microstructure is characterised by elongated LPSO fibers along the extrusion direction within the magnesium matrix. Moreover, the magnesium matrix presents a bimodal grain structure with dynamically-recrystallized grains and deformed, elongated grains with the basal plane parallel to the extrusion direction. The beginning of plasticity depends on the volume fraction of deformed and DRX grains. Alloys with low volume fraction of LPSO phase (<10 vol%), with a high volume fraction of deformed grains, show the typical behavior of extruded magnesium alloys where yield stress in tension is higher than in compression. This effect is, however, reversed as the volume fraction of the LPSO phase increases since DRX grains are majority.
While there is a large body of literature on the micro-mechanical behavior of metal matrix composites (MMCs) under uniaxial applied stress, very little is available on multi-phase MMCs. In order to cast light on the reinforcement mechanisms and damage processes in such multi-phase composites, materials made by an Al-based piston alloy and containing one and two ceramic reinforcements (planar-random oriented alumina fibers and SiC particles) were studied. In-situ compression tests during neutron diffraction experiments were used to track the load transfer among phases, while X-ray computed tomography on pre-strained samples was used to monitor and quantify damage. We found that damage progresses differently in composites with different orientations of the fiber mat. Because of the presence of intermetallic network, it was observed that the second ceramic reinforcement changed the load transfer scenario only at very high applied load, when also intermetallic particles break. We rationalized the present results combining them with previous investigations and using a micromechanical model.
X-Ray computed tomography and traditional analysis of a capillary absorption test in cement pastes
(2020)
Water absorption testing has the attraction of being simple, relatively quick and use water as a fluid which is the key substance in the possible concrete deterioration. However, in spite of the advantages its application has remained empirical, except for the testing of resistance to frost, through the identification of the critical degree of saturation. Rilem TC-116 studied this test, among others, for the characterization of concrete resistance against transport through the concrete pore network. Results indicated a low discriminating ability of the absorbency for qualifying concrete resistance and then, it seemed necessary to try to move forward by making the link between the absorption testing and the concrete pore microstructure. In the present work, thanks to the X-Ray computed tomography, it is described the evolution of the water front in three paste-specimen with different w/c ratios (different pore radius distributions). The observations allowed us to deduce that all the pores start to fill simultaneously, but the bigger ones fill quicker and rise less. The saturation degree is measured along the height of the sample, showing that each pore size has a different rate which becomes constant after the first hour. Washburn’s equation was applied to the progressive advance of the water front, resulting in a pore radius much smaller than the one expected.
Abstract While classically used to visualise the magnetic microstructure of functional materials (e.g., for magnetic applications), in this study, the Bitter technique was applied for the first time to visualise macroscopic deformation gradients in a polycrystalline low-carbon steel. Spherical indentation was chosen to produce a multiaxial elastic–plastic deformation state. After removing the residual imprint, the Bitter technique was applied, and macroscopic contrast differences were captured in optical microscopy. To verify this novel characterisation technique, characteristic “hemispherical” deformation zones evolving during indentation were identified using an analytical model from the field of contact mechanics. In addition, near-surface residual stresses were determined experimentally using synchrotron radiation diffraction. It is established that the magnetic domain distribution contrast provides deformation-related information: regions of different domain wall densities correspond to different “hemispherical” deformation zones (i.e., to hydrostatic core, plastic zone and elastic zone, respectively). Moreover, the transitions between these three zones correlate with characteristic features of the residual stress profiles (sign changes in the radial and local extrema in the hoop stress). These results indicate the potential of magnetic domain distribution imaging: visualising macroscopic deformation gradients in fine-grained ferromagnetic material with a significantly improved spatial resolution as compared to integral, mean value-based measurement methods.
The evolution of the internal strains during in situ tension and compression tests has been
measured in an MgY2Zn1 alloy containing long-period stacking ordered (LPSO) phase using
neutron diffraction. The alloy was extruded at two different temperatures to study the influence
of the microstructure and texture of the magnesium and the LPSO phases on the deformation
mechanisms. The alloy extruded at 623 K (350 °C) exhibits a strong fiber texture with the basal
plane parallel to the extrusion direction due to the presence of areas of coarse non-recrystallised
grains. However, at 723 K (450 °C), the magnesium phase is fully recrystallised with grains
randomly oriented. On the other hand, at the two extrusion temperatures, the LPSO phase
orients their basal plane parallel to the extrusion direction. Yield stress is always slightly higher
in compression than in tension. Independently on the stress sign and the extrusion temperature,
the beginning of plasticity is controlled by the activation of the basal slip system in the dynamic
recrystallized grains. Therefore, the elongated fiber-shaped LPSO phase which behaves as the
reinforcement in a metal matrix composite is responsible for this tension–compression asymmetry.
The magneto-mechanical memory (MMM) method, that is often referred to as the metal magnetic memory method, has been reported to be a non-destructive testing technique capable of quantifying stress concentrations and detecting defects in ferromagnetic materials. The underlying mechanism behind MMM has been explained in the literature, but the sensitivity to stress concentration has not been satisfactorily investigated. In this paper, both the normal and tangential components of the stress-induced MMM signal were measured by permanently installed magnetic sensor arrays on specimens made from three grades of L80 alloy steel and 20 other structural steels; tests were also carried out on a pipe made from the 4140-L80 steel. As expected, the stress history affects the MMM signal, but the experimental results show that significant irreversible change of magnetization always occurs only in the first cycle of loading regardless whether the deformation is purely elastic or partially plastic. If the peak stress level is increased at a given point during cycling, the immediately following next cycle acts as a new “first” cycle at that peak stress level and causes additional significant irreversible change of magnetization, but there is no evidence that plastic deformation might build up a cumulative magnetization. The MMM effect is very small in the steel samples tested, indicating that it will not be useful in field applications. In un-notched specimens the irreversible change in magnetization caused a proportional change in the measured external magnetic field on the order of only 5–10 A/m, while in the case of notched specimens the leakage field was on the order of 30–60 A/m.
Bei der additiven Fertigung können sich während des Prozesses aufgrund von hohen Aufheiz- und Abkühlraten Eigenspannungen ausbilden, die potentiell zu einem Verzug von Bauteilen führen und sich negativ auf das mechanische Verhalten auswirken. In dieser Studie wurden Ti-6Al-4V Proben durch Selektives Laserschmelzen mit verschiedenen Lasergeschwindigkeiten additiv gefertigt, um die Auswirkung der Laserenergiedichte auf den Eigenspannungszustand zu untersuchen. Die oberflächennahe Eigenspannungsanalysen wurden mittels energiedispersiver Synchrotronbeugung durchgeführt. Insgesamt wurden hohe Zugspannungen an den Seitenflächen der Proben gefunden. Es wurde festgestellt, dass je höher die Laserenergiedichte während der Fertigung ist, desto geringer fallen die Eigenspannungen aus. Eine nachträglich durchgeführte Wärmebehandlung führt zu einem vollständigen Abbau von Eigenspannungen.
Die Schicht-für-Schicht additive Fertigung (AM) in Form des selektiven Laserschmelzens (SLM) bietet einerseits Vorteile bezüglich des Probendesigns, andererseits sind thermische Eigenspannungen (ES) aufgrund des hohen Temperaturgradienten unvermeidbar. Diese Eigenspannungen wurden in zwei SLM-gefertigten Proben aus IN718 zerstörungsfrei mit Neutronenstreuung hinsichtlich der folgenden zwei Einflüsse analysiert: der Einfluss der Hatch-Länge und das Abtrennen des Werkstücks von der Bauplatte. Begleitet wurden die Messungen der Eigenspannungen durch optische Mikroskopie und die taktile Vermessung der Oberfläche. Eine Korrelation zwischen den Eigenspannungen und der Hatch-Länge konnte beobachtet und erklärt werden.