Filtern
Dokumenttyp
Schlagworte
- UHPC (6)
- Durability (4)
- Microstructure (4)
- Thermal treatment (4)
- Zonation (4)
- Hydrothermal treatment (3)
- Architectural Concrete (2)
- Concrete (2)
- Desiccation (2)
- Einzelfaserdurchzugsversuch (2)
- Facade Elements (2)
- Fasermodifikation (2)
- Fibres (2)
- Grenzflächenaktive Verbindung (2)
- Hydroxylellestadite (2)
- Lichtmikroskopie (2)
- Oberflächenfunktionalisierung (2)
- Röntgen-3D-Computertomographie (2)
- Self-Cleaning Properties (2)
- Shrinkage (2)
- Tobermorite (2)
- Windkanal (2)
- Zementgebundene Baustoffe (2)
- Accelerated testing (1)
- Adhesive Pull-Strength (1)
- Alite (1)
- Alkali silica reaction (1)
- BOFS (1)
- Biofilm (1)
- Bioreceptivity (1)
- Brown coal fly ash (1)
- Building and Construction (1)
- Cementitious materials (1)
- Compressive strength (1)
- Computed tomography (1)
- Damage analysis (1)
- Developing building materials (1)
- Ettringit (1)
- Ettringite (1)
- Functionalization (1)
- General Materials Science (1)
- Green facades (1)
- Heat treatment (1)
- Hydration products (1)
- Hydrogarnet (1)
- Hydrogranat (1)
- Hydrothermale Behandlung (1)
- Hydroxyellestadit (1)
- In-situ XRD (1)
- Internal sulfate resistance (1)
- Kristalline CSH-Phase (1)
- LD-Schlacke (1)
- Mechanical strength (1)
- Mitigation strategies (1)
- Mortar (1)
- Non-destructive testing (1)
- Phase composition (1)
- Phase development (1)
- Portland Cement (1)
- Road pavement (1)
- Steelmaking slag (1)
- Strain hardening (1)
- Surface interactions (1)
- Test methods (1)
- Thermal analysis (1)
- Tobermorit (1)
- Transport mechanism (1)
- Tricalcium-silicate (1)
- Tricalciumsilikat (1)
- Ultra-High Performance Concrete (1)
- Ultra-High-Performance Concrete (1)
- Ultra-high performance concrete (1)
- Wärmebehandlung (1)
- X-ray diffraction (1)
- XRD (1)
- Zement (1)
Organisationseinheit der BAM
Paper des Monats
- ja (1)
Im Gegensatz zur Druckfestigkeit weisen zementgebundene Werkstoffe i. a. nur geringe Zugfestigkeiten auf. Ein Weg, Zugfestigkeiten zementgebundener Werkstoffe zu erhöhen und Rissbildung aufgrund von Zugspannungen zu verringern, besteht in der Einarbeitung von Fasern, die diese Spannungen aufnehmen. Häufig eingesetzt werden Stahlfasern, obwohl synthetische Polymerfasern leichter und meist beständiger gegenüber chemischen Angriffen und Korrosion sind. Die Polymerfasern zeigen allerdings meist einen deutlich schwächeren Haftverbund, was an der hydrophoben Faseroberfläche liegt. Um nun eine Anbindung der Fasern an die mineralische Matrix zu erreichen, müssen die Faseroberflächen modifiziert werden, ohne dass die mechanischen Eigenschaften negativ beeinflusst werden. Eine Herausforderung besteht somit in einer Oberflächenmodifikation durch eine schonende Behandlung der Fasern zur Erzeugung von anbindungsfähigen Gruppen.
Durch eine Behandlung von modifizierten Fasern mit geeigneten Polymerlösungen werden die Oberflächeneigenschaften verändert und erlauben eine Anbindung an die Zementsteinmatrix. Der Einsatz von Tensiden als grenzflächenaktive Verbindungen ermöglicht in diesem Zusammenhang eine Vermittlung zwischen Polymeroberflächen und mineralischen Werkstoffen.
Im Gegensatz zur Druckfestigkeit weisen zementgebundene Werkstoffe i. a. nur geringe Zugfestigkeiten auf. Ein Weg, Zugfestigkeiten zementgebundener Werkstoffe zu erhöhen und Rissbildung aufgrund von Zugspannungen zu verringern, besteht in der Einarbeitung von Fasern, die diese Spannungen aufnehmen. Häufig eingesetzt werden Stahlfasern, obwohl synthetische Polymerfasern leichter und meist beständiger gegenüber chemischen Angriffen und Korrosion sind. Die Polymerfasern zeigen allerdings meist einen deutlich schwächeren Haftverbund, was an der hydrophoben Faseroberfläche liegt. Um nun eine Anbindung der Fasern an die mineralische Matrix zu erreichen, müssen die Faseroberflächen modifiziert werden, ohne dass die mechanischen Eigenschaften negativ beeinflusst werden. Eine Herausforderung besteht somit in einer Oberflächenmodifikation durch eine schonende Behandlung der Fasern zur Erzeugung von anbindungsfähigen Gruppen. Durch eine Behandlung von modifizierten Fasern mit geeigneten Polymerlösungen werden die Oberflächeneigenschaften verändert und erlauben eine Anbindung an die Zementsteinmatrix. Der Einsatz von Tensiden als grenzflächenaktive Verbindungen ermöglicht in diesem Zusammenhang eine Vermittlung zwischen Polymeroberflächen und mineralischen Werkstoffen.
Basic oxygen furnace slags (BOFS) are by-products of the steelmaking process. Several researchers have studied the production of Portland cement clinker and metallic iron from BOFS via a reductive treatment.
In this study, we applied a carbothermal reduction of BOFS in a technical-scale electric arc furnace and characterised the clinker-like products. Those clinker-like non-metallic products (NMPs) had a chemical and mineralogical composition comparable to clinker for ordinary Portland cement (OPC) and contained large elongated alite crystals as major component. The pure NMPs reacted more slowly and achieved a lower degree of hydration compared with commercial OPC.
If the reactivity of the products can be further increased by employing specific adaptations, it can be used as a full clinker substitute for OPC. Nevertheless, it is also an option to use the material without further modifications as a cement component or concrete addition, which contributes to the strength development in both cases.
Fused cement clinker can be produced from molten basic oxygen furnace slag (BOFS) by way of a reductive thermochemical treatment. During the thermochemical treatment, oxidic iron is reduced to metallic iron and separated. The resulting low-iron slag has a chemical and mineralogical composition similar to ordinary Portland cement (OPC) clinker. In this study, the hydraulic reactivity of the fused clinker from BOFS with and without gypsum was investigated using isothermal calorimetry, differential scanning calorimetry, in situ X-ray diffraction and powder X-ray diffraction. Furthermore, a synthetic fused clinker without foreign ions and fused clinker produced by a mixture of both materials was studied. The hydraulic reaction of the fused clinker from BOFS was considerably slower than that of OPC. However, the reaction can be accelerated by adding gypsum as a sulfate carrier. Furthermore, the results showed an increased reaction rate with decreasing content of foreign ions such as Fe, P or Mn.
Die Klinkerphasenbildung durch Sinterung in Drehrohröfen bei der Herstellung von Portlandzementklinker (PZK) ist gründlich erforscht und optimiert. Im Hinblick auf mögliche ökonomische und ökologische Vorteile befassen sich aktuelle Forschungsvorhaben darüber hinaus mit der Herstellung von Klinkermineralen aus Stahlwerksschlacken, die eine vergleichbare chemische Zusammensetzung aufweisen.
Neuste Untersuchungen zeigen, dass nach der reduzierenden Behandlung schmelzflüssiger Linz-Donawitz-(LD)-Schlacken und Abscheidung des gebildeten metallischen Eisens eine mineralische Schlacke entsteht, die unabhängig von ihren Abkühlbedingungen ca. 50–60 Gew.% des wichtigsten Klinkerminerals Alit (C3S) enthält und eine hohe hydraulische Reaktivität aufweist.
Die Stabilität des Alits auch nach langsamer Abkühlung deutet auf eine Stabilisierung des Minerals durch Nebenelemente aus den LD-Schlacken hin. Ein sinkender Anteil an LD-Schlacke durch Zusatz synthetischer Schlackemischung, die sich hinsichtlich ihrer Hauptkomponenten wie eine ausreduzierte LD-Schlacke zusammensetzt, führt zu einem Rückgang des Alitgehaltes und dem Zerfall der Schlacke beim Erstarren.
Tricalcium-silicate (C3S) or Alite is the most important mineral in Portland cement. Since pure tricalcium-silicate is only stable above temperatures of 1250 °C, its decomposition has to be prevented technically by fast cooling after the sintering process. At room temperature, the decomposition velocity is very slow so that metastable tricalcium-silicate is obtained.
Although the mechanisms of clinker phase formation during burning process of Portland cement in a rotary kiln were solved and improved over the years, in view of possible economic and ecological benefits current projects aim to produce clinker phases from metallurgical slags. Recent studies discovered that the mineral phase which remained after a reducing treatment and separation of formed metallic iron from molten Linz-Donawitz (LD-) slags contained about 60 wt.% Alite despite it was cooled slowly. Because the results could be verified using slags from different origins and varying cooling velocities a chemical stabilisation of the Alite can be assumed. First tests in mortars indicate that workability, hardening and solid state properties are comparable with an ordinary Portland cement. An application of the observed phenomenon in cement production requires enhanced knowledge about formation and stabilisation conditions of Alite during crystallisation from melts in contrast to the sintering reactions in conventional Portland cement production. Therefore, this study focuses on the stabilisation mechanisms of Alite in consolidating melts. Samples from different melting experiments are analysed to determine stabilising factors.
UHPC (engl. ultra-high-performance concrete) bietet außergewöhnliche Eigenschaften, die sich durch eine optimierte Wärmebehandlung weiter verbessern lassen. Wie bei normalen Beton beschleunigt eine Wärmebehandlung den Aushärteprozess und reduziert das Schrumpfen. Durch Ausbildung eines dichteren Gefüges wird weiterhin die Druckfestigkeit und die Resistenz gegenüber Umwelteinflüssen erhöht.
Die Art der Wärmebehandlung wird durch die Parameter: Temperatur, Druck, Wasserdampfsättigung und Dauer definiert und hat einen entscheiden Einfluss auf die Phasenentwicklung und damit auf die makro- und mikroskopischen Eigenschaften des UHPCs. Auch die Dauer und Art der Vorlagerung des UHPCs vor der thermischen Behandlung sind von Bedeutung.
Ziel der vorgestellten Untersuchung war der Vergleich und die Optimierung verschiedener Wärmebehandlungsarten mit Blick auf die Druckfestigkeits- und Phasenentwicklung. Dafür wurden UHPC-Zylinder und Prismen hergestellt und ungeschützt bzw. in Folie eingeschweißt bei 90 °C im Ofen, im Heißwasserbad, sowie alternativ bei 185 °C und 1.1 MPa im Autoklaven wärmebehandelt. Zusätzlich wurde die Vorlagerungs- und die Behandlungszeit systematisch variiert.
Die Ergebnisse zeigen, dass eine praxisnahe Wärmebehandlung im Ofen (kurze Vorlagerungs- und Behandlungszeit, Verdunstungsschutz durch Einschweißen in Folie) zwar zu einer stark erhöhten Frühfestigkeit führt, aber die Langzeitfestigkeit wird nicht signifikant erhöht. Erst längere Behandlungszeiten verbunden mit intensiviertem Schutz gegen das Austrocknen führen darüber hinaus zu deutlich erhöhten Langzeitfestigkeiten. Nach der Autoklavierung dagegen wurden Festigkeitszuwächse von bis zu 30 % gemessen.
Die röntgenographisch nachgewiesene Phasenentwicklung wird in beiden Behandlungsarten durch die Limitierung des zur Verfügung stehenden Wassers bestimmt. Bei der Wärmebehandlung im Ofen wird das durch den Ettringitzerfall freigesetzte Wasser für die puzzolanische Reaktion der Mikrosilika verbraucht, reicht aber für eine weitere Reaktion der Klinkerphasen nicht aus. Bei der hydrothermalen Behandlung dagegen zeigen die Veränderungen im Phasenbestand sowohl eine Intensivierung der puzzolanischen als auch der hydraulischen Reaktion. Der für autoklavierte Baustoffe charakteristische Tobermorit konnte jedoch nicht im Probeninneren, sondern nur als Belag auf der Probenoberfläche nachgewiesen werden. Ursächlich hierfür ist vermutlich wiederum das zu geringe Wasserangebot im Gefüge des UHPC.
Materials that support natural biodiversity on their surfaces can compensate for human activities that have a negative impact on nature and thus contribute to a carbon-neutral and nature-positive world. Specifically designing bioreceptive materials which favor the growth of biofilms on their surface is an approach complementing conventional, macroscopic green façades. But what exactly characterizes a bioreceptive substrate and how do biofilm and substrate interact? How and why does a spontaneous colonization and the formation of biofilms take place? What are biofilms and how can they be established in a laboratory setting? How can this existing knowledge be transferred to the artificial stone concrete so that this material can be tuned to increase (or decrease) its bioreceptivity?
This review paper aims at summarizing the existing state of knowledge on bioreceptive concrete and pointing out inconsistencies and contradictions which can only be removed by more interdisciplinary research in the field.
Ultra high performance concrete (UHPC) is characterised by its high compressive strength of more than 120 MPa and its high durability. With thermal treatment at 90°C, hydration is accelerated and a strength comparable to the 28-day strength can be achieved immediately after the treatment. In applying Optimum process conditions, the strength can be even further increased by up to 30%. Previous Research showed that thermal treatment can lead to inhomogeneities in form of a visible zonation within the cross-section, if the UHPC is not protected sufficiently from desiccation. This led to the question, to what extent the related changes in mechanical properties, microstructure and phase composition are of relevance for the performance of the UHPC. First investigations of small specimens thermally treated without protection exhibited a decrease of compressive strength, indicating that the zonation aspect requires further research.
In this study the zonation of UHPC treated thermally at 90°C is investigated after applying four different procedures of treatment and curing in comparison. The samples are characterized with respect to their chemistry, mineral composition and microstructure to allow an assessment on durability and strength development, with focus on potential depth dependent changes associated with the zonation.
The measurements reveal the formation of a visible zonation in case of unprotected treatment, if followed by immersion in water. The compressive strength is not significantly impaired, but a decrease in bending strength gives reason for concern. Further results allow clear correlation with changes in pore structure, whereas the interpretation of relationships with phase distribution, degree of hydration, microchemistry is more complex and therefore, provides only partial clarification.
Ultra high performance concrete (UHPC) is characterised by its high compressive strength of more than 150 MPa and its high durability. Due to thermal treatment at 90°C a strength comparable to the 28-days-strength can be achieved immediately after the treatment and in some cases can be even further increased up to 30 %. The explanations for the increase in strength are the accelerated hydration of the clinker minerals and the intensified pozzolanic reaction contributing to a denser microstructure and hence, a high performance in compressive strength.
Former research shows that thermal treatment can lead to inhomogeneities in form of a visible zonation within the cross-section. The width of the margin increases with shorter pre-storage time before the thermal treatment and with omitting protective measures against desiccation during the treatment. Specimens exhibiting a zonation typically show a lower compressive strength compared to the undisturbed reference whereas changes in chemistry, mineral content and microstructure were not reported in detail.
In this study the zonation of thermally treated UHPC is investigated with respect to its chemistry, mineral composition and microstructure to allow predictions on durability and strength development. Measurements show a change in pore sizes, minerals phase composition and element distribution leading to the visible zonation and weaker bending tensile strength compared to the reference.