Schlagworte
- Adsorption (1)
- Alkali-silica reaction (1)
- Cement hydration (1)
- Concrete (1)
- Concrete rehabilitation (1)
- Damage analysis (1)
- Environmental conditions (1)
- Materials characterisation (1)
- Mixture composition (1)
- Polycarboxylate (1)
- Polymer cement concrete (PCC) (1)
- Preparation of thin sections (1)
- Repair mortar (1)
- Repair systems (1)
- Sprayed polymer cement concrete (SPCC) (1)
Since its invention in the early 1990’s, self-consolidating concrete has never become well established in the ready-mix sectors worldwide. The reason for this can be mainly found in the fact that the sophisticated compositions are sensitive against changing environments. This lack of robustness can be attributed to the interaction between cement hydration reaction and high range water reducing agent (HRWRA). Understanding the relevant mechanisms that control the initial flow performance as well as the flow retention helps optimizing SCC mixtures that perform either steadily in one specific environment or that perform largely similarly at steadily changing environments.
This paper depicts how HRWRAs interact with clinker and hydration phases and discusses the important role of the charge density of a polycarboxylic HRWRA in the way the rheology is affected. Based on rheometric results and observations of the Vicat setting times, it is shown that increasing charge densities of the HRWRA and decreasing water to powder ratios (w/p) reduce the flow retention and have lesser retarding effect on the setting. Based on the discussion, optimization procedures for the mixture composition and the HRWRA modification are suggested to achieve optimized performance for varying environmental situations or highest robustness for specific conditions.
Influence of selected aspects of the mixture proportioning on the performance of repair mortars
(2012)
Concrete is the most applied building material in modern times. It is present in all kinds of structures and no other material secms to rcplace concrete as the most selected building material in the near future. The prime advantages are the high performance, the easy production and a facile processability. The sustainability and durability are important requirements to concrete. Even if concrete is significantly less susceptible against factors promoting a damage, compared to other materials, there are still mechanisms affecting it. In particular, high-ways and hydraulic structures made of concrete worldwide show cases of alkali-silica reaction (ASR) damages. This article refers to experience at BAM Federal InstituteforMaterials Research and Testing for several decades to ASR research and darnage assessment. ASR is a severe darnage mechanism that can occur in concrete, when certain conditions related to composition and cxposition arise in a critical combination. The chemical reaction is based on the alkalis and the silica in the concrete and was first identified by Stanton in highway structures in California (Stanton, 1940). Actually three components are needed to initiate ASR: alkali-sensitive siliceous aggregates, alkalis coming from internal (cement or other components) or external sources (de-icing salt or sea water) and water. If all of these components are sufficiently present an alkali-silica gel could be formed (Hobbs, 1988). This gel itself needs additional space when it is formed. Furthermore it is able to swell in the presence of humidity, both processes generating an expansion pressure inside the concrete. As a consequence of intensive expansion, cracks can occur, which significantly lowers thc strength of the material. Parameters like amount and chemical composition of the gel as weil as the pattern and width of cracks can help to classify the ASR darnage (Swamy, 1992). The objective of this article is to demoostrate the microscopic work on ASR affected concrete samples, carried out to assess the damaging process or to evaluate various alkali-sensitive aggregates. It will explain the approach of ASR investigation from the macroscale to microscale, starting briefly with the condition assessment, over treatment and investigations of samples in the laboratory, to the use of different microscopical and analytical techniques. In the main part the characteristic features for identifying ASR in concrete are presented by using microscopic images. Especially the emphasis lies on the role of the aggregate.