A new setup is presented which enables simultaneous wide- and small-angle X-ray scattering (WAXS/SAXS) and Raman spectroscopic experiments during the synthesis of Mo-based mixed oxide catalyst precursors at the µ-spot beamline at the Berliner Elektronenspeicherring-Gesellschaft für Synchrotronstrahlung (BESSY). Furthermore, we report about the separate monitoring of the same reactions under comparable conditions by simultaneous combined ATR/UVvis/Raman spectroscopic measurements. For testing the performance of both experimental setups two syntheses were described comprising the precipitation of metal molybdates by mixing solutions of metal nitrates and ammonium heptamolybdate. Additionally, the effect of H3PO4 admixture on precipitation was investigated. The combined evaluation of spectroscopic and WAXS/SAXS data allows the discrimination between different molybdate species appearing in solution and precipitate. Furthermore, these molybdate species could be assigned to separate phases of different crystallinity.
Methane dry reforming (DRM) was investigated over highly active Ni catalysts with low metal content (2.5wt%) supported on Mg-Al mixed oxide. The aim was to minimize carbon Deposition and metal sites agglomeration on the working catalyst which are known to cause catalyst deactivation.
The solids were characterized using N2 adsorption, X-ray diffraction, temperature-programmed reduction, X-ray photoelectron spectroscopy, and UV-Vis diffuse reflectance spectroscopy. The results showed that MgO-Al2O3 solid solution phases are obtained when calcining Mg-Al hydrotalcite precursor in the temperature range of 550–800 °C. Such phases contribute to the high activity of catalysts with low Ni content even at low temperature (500 °C). Modifying the catalyst preparation with citric acid significantly slows the coking rate and reduces the size of large octahedrally coordinated NiO-like domains, which may easily agglomerate on the surface during DRM. The most effective Ni catalyst shows a stable DRM course over 60 h at high weight hourly space velocity with very low coke deposition. This is a promising result for considering such catalyst systems for further development of an industrial DRM technology.