A guided drop test was performed to achieve a defined and reproducible impact orientation of jerrycans. The drop heights where 50% of the jerrycans experienced a failure from a crack where fluid can escape (50% failure drop height) were compared among jerrycans made of four different materials, in their original state and preconditioned with standard liquids. To analyse the impact of only elevated temperatures, the packages were preconditioned for 21?days at 40°C without the use of chemicals.
The 50% failure drop height was compared by using Young's modulus; the notched impact strength (NIS) of specimen cut from plates which were manufactured by compression moulding and the notched tensile impact strength of specimen cut-outs of the jerrycans' side walls. The NIS depends highly on the thermal preconditioning of the plates being manufactured by compression moulding. A trend can be seen that a higher Young's modulus, a higher NIS and a higher notched tensile impact strength result in a higher 50% failure drop height, but the values are spread. The influence of the wall thickness cannot be neglected.
The change of the 50% failure drop height in regard to the preconditioning at 40°C with and without nitric acid was compared in terms of their resistance to molecular degradation, density and degree of crystallinity. The conditioning at elevated temperature causes post-crystallization. It was shown that the resistance to molecular degradation determined on pressed plates correlates with the change of the 50% failure drop height after pre-storage with nitric acid.
The effect of the wall thickness variation of blow-moulded bodies made of high-density polyethylene on an internal pressure test after prestoring the packaging with standard liquids was evaluated in experiments and simulations. The objects of the investigation were jerrycans used for the transportation and storage of dangerous goods.
The wall thickness was determined using two alternative methods to the magnetostatic measurement. These alternative methods are used for research purpose to get a volumetric model of the jerrycan wall as a geometric model for the simulation. The comparison of the experiments and the simulations of the internal pressure test were performed using the digital image correlation method. The integral strain and deformation of the whole jerrycan was detected by measuring the total mass of the jerrycan being filled with water during the internal pressure test. This is a suitable alternative to the optical measurements of local deformation by the digital image correlation method. Prestorage at 40°C without the influence of chemicals strengthens the jerrycan, whereas the swelling effect of butyl acetate and hydrocarbon mixture softens the jerrycan. The comparison with the experiment is necessary to verify the accuracy of the simulation. It shows that the deformation can be simulated more precisely by using the actual measured geometry. The weakening of the high-density polyethylene caused by a hydrocarbon mixture can be simulated using the Arrhenius equation. The aim of the simulation was to discover whether it is possible to use specimens to predict the behaviour of a packaging both after the influence of standard liquids.
Verschiedene experimentelle Untersuchungen sind zur Erlangung einer Zulassung für Gefahrgutverpackungen notwendig, um die Eignung der Verpackung für den Transport gefährlicher Guter nachzuweisen. Ziel sind keine absoluten Werte für die Zeit bis zum Versagen bei der Innendruckprüfung oder die mittlere Versagensfallhöhe, sondern die Veränderung des Verpackungsverhaltens bei dem Einsatz eines anderen HDPEs. Alle Kanister aus den vier verschiedenen Werkstoffen wurden speziell hergestellt, um die Werkstoffeigenschaften differenziert beurteilen zu können. Das Granulat, aus dem die Platten gepresst und die Kanister hergestellt wurden, stammte aus derselben Charge, um Schwankungen zwischen den Chargen als Einflussquelle auszuschließen. Die Wanddicke ist entscheidend, daher wurden die Verpackungen mit dem Computertomographen und mittels Streifenprojektionsverfahren vermessen und die Ergebnisse mit dem magnetostatischen Messverfahren verglichen. Die Verformung bei der Innendruckprüfung wurde mittels Stereo-Bildkorrelationsverfahren vermessen. Die Verschiebung in radialer Richtung sowie die aquivalente Dehnung wurden ausgewertet und konnten in der numerischen Berechnung nachgebildet werden. Ebenso deren starke Beschleunigung aufgrund der Quellung, indem die Temperatur im Materialgesetz entsprechend der Quellung verwendet wurde. Der Widerstand gegen Innendruck und das Absorptionsverhalten hangen von der Dichte des Werkstoffs ab. Die Konditionierung bei erhöhter Temperatur führt zu Nachkristallisation und zum Abbau von Eigenspannungen. Die Veränderung der Dichte zwischen den Werkstoffen kann anhand gepresster Platten beurteilt werden. Eine höhere Dichte führt zu einem besseren Bauteilverhalten unter Innendruck. Der Zusammenhang von mittlerer Versagensfallhöhe und der Schlagzugzähigkeit gekerbter Proben aus den Seitenwanden der Kanister sowie der Kerbschlagzähigkeit von gepressten Platten konnte nachgewiesen werden. Eine höhere Kerbschlagzähigkeit führt zu einer höheren mittleren Versagensfallhöhe. Eine geringe Beständigkeit gegen oxidativen Abbau senkt die mittlere Versagensfallhöhe drastisch. Bei einer hohen Beständigkeit gegen oxidativen Abbau führt die Vorlagerung mit Salpetersaure jedoch nicht zu einer Verringerung der mittleren Versagensfallhöhe im Vergleich zum Zustand ohne Vorlagerung. Der oxidative Abbau kann an gepressten Platten ermittelt werden und erlaubt einen Ruckschluss auf die Veränderung der mittleren Versagensfallhöhe.