High-strength concrete (HSC) will experience thermal microcracking, explosive spalling, and undesirable chemical changes when exposed to high temperatures, such as during fire, engulfment by lava flow, or nuclear meltdown. Knowledge of the resultant changes in mechanical, physical, and chemical properties is paramount for hazard mitigation. We present a multidisciplinary study on the influence of thermal-stressing on HSC. Our study shows that thermal microcracking in HSC initiates at 180 °C, is more prevalent during cooling, and exhibits the Kaiser 'temperature-memory' effect. We show that residual compressive strength, indirect tensile strength, ultrasonic wave velocities, and Youngs modulus and Poissons ratio decrease, whilst porosity and permeability increase with increasing temperature. We discuss these data in terms of the chemical changes during thermal-stressing, provided by thermo-gravimetric analysis, differential scanning calorimetry, and X-ray diffraction, and from optical microscopic analysis of thermally-stressed samples. We provide implications for thermally-damaged HSC structures and a new method for non-destructive monitoring.
This paper presents the results of an
experimental study on the transient strain of high
strength concrete (HSC) under heating up to 750 °C
and the impact of polypropylene (PP) fibers. Concerning
this topic only few results are available in the
literature and systematic investigations are missing.
However, basic knowledge is necessary for the
understanding of the internal damage processes in
the material as well as for heated structures. The
transient strain during heating can be separated in two
basic components: the free thermal strain and the
mechanical strain. They were experimentally determined
exemplarily for one HSC. For the determination
of the mechanisms of transient strain and particularly
the influence of PP fibers different techniques were
applied. In this context the monitoring of the microcracking
was done for the first time with acoustic
emission analysis in combination with ultrasonic
measurements. This new approach helps fundamentally
to explain the impact of PP fibers on free thermal
strain and mechanical strain during heating up.
Furthermore weight loss measurements were carried
out to characterize the moisture transport. It was
shown that the PP fibers cause an acceleration of the
moisture transport in the temperature range from 200
to 250 °C which leads to drying shrinkage in opposite
direction to the free thermal strain. Hence this paper is
a contribution to the general understanding of the
impact of PP fibers in HSC at high temperatures and
emphasizes the important influence of PP fibers on the
thermal and mechanical induced strain of HSC.
Einfluss einer druckschwellinduzierten Degradation von Fahrbahndeckenbeton auf die schädigende AKR
(2020)
In den letzten Jahren sind im deutschen Bundesautobahnnetz verstärkt Schäden an vor 2005 errichteten Betonfahrbahndecken aufgetreten, die mit einer Alkali-Kieselsäure-Reaktion (AKR) in Verbindung gebracht werden. Neben dem AKR-fördernden Einfluss von alkalihaltigen Taumitteln werden Fahrbahndecken zyklischen mechanischen Belastungen infolge des Verkehrs und Zwangsspannungen durch klimatische Einwirkungen ausgesetzt. Solche mechanischen Belastungen werden bisher in keinem AKR-Prüfverfahren berücksichtigt. Die zyklischen Belastungen können zu einer Degradation des Betongefüges führen, die ggf. einen AKR-fördernden Einfluss hat. Dieser Beitrag stellt Untersuchungen vor, die zur Beantwortung der Frage nach dem Einfluss einer zyklischen mechanischen Belastung auf den AKR-Schadensprozess beitragen. Dabei wird der Hypothese nachgegangen, dass die ermüdungsinduzierte Degradation zu einer Erhöhung des Stofftransports führt.
Dieser hat einen Einfluss auf die AKR-Schadensentwicklung, da die Reaktionspartner zunächst zum Reaktionsort transportiert werden müssen. Daher wird angenommen, dass sich mit dem Stofftransport auch die AKR-Schädigung verstärkt. Es werden Betonproben aus typischen Fahrbahndeckenbetonen einer vorgeschalteten zyklischen Druckschwellbelastung ausgesetzt.
Die Degradation infolge der Vorbelastung wird simultan mittels ZfP-Verfahren charakterisiert. Anschließend werden die Auswirkungen der zyklischen Vorschädigung auf den Stofftransport sowie auf die AKR vergleichend an Prüfkörpern ohne und mit Vorschädigung untersucht. Die Ergebnisse lassen den Schluss zu, dass die zyklische Vorschädigung sowohl den Stofftransport als auch die AKR fördert.
In this work, which is part of a larger research program, a framework called “virtual data fusion“ was developed to provide an automated and consistent crack detection method that allows for the cross-comparison of results from large quantities of X-ray Computed Tomography (CT) data. A partial implementation of this method in a custom program was developed for use in research focused on crack quantification in Alkali-Silica Reaction (ASR)-sensitive concrete aggregates. During the CT image processing, a series of image analyses tailored for detecting specific, individual crack-like characteristics were completed. The results of these analyses were then “fused” in order to identify crack-like objects within the images with much higher accuracy than that yielded by any individual image analysis procedure. The results of this strategy demonstrated the success of the program in effectively identifying crack-like structures and quantifying characteristics, such as surface area and volume. The results demonstrated that the source of aggregate has a very significant impact on the amount of internal cracking, even when the mineralogical characteristics remain very similar. River gravels, for instance, were found to contain significantly higher levels of internal cracking than quarried stone aggregates of the same mineralogical type.
This paper describes a novel methodology for quantitative in-situ moisture measurement without tracking agents using X-ray computed tomography (XCT). The high levels of grey-scale precision required for the measurement of moisture without tracking agents resulted in the need for an additional image calibration procedure to correct for water-related X-ray scattering and for equipment-variability related artefacts arising during in-situ testing. This calibration procedure was developed on the basis of existing principles of XCT image cor-rection. Resulting images of moisture distribution exhibit a high level of agreement with expected material behaviour. This research demonstrated that XCT can be successfully used to measure both moisture-front movement over time and changes in 3D moisture distribution within samples. This approach to moisture measurement lays the groundwork for the planned future investigation of the interaction between cracking induced by varying chemical and mechanical processes and water transport in concrete.
The recommendation is based on the co-authors’ work organized by the RILEM TC 256-SPF “Spalling of concrete due to fire: testing and modelling”. It aims to provide useful information, guidance and best practices in fire spalling assessment to laboratories that perform large-scale tests based on fire resistance test standards. It provides guidance on the spalling observation techniques during testing, as well as post-test spalling quantification/assessment methods. This document is intended to be used in conjunction with the fire resistance test standards, e.g. EN 1363-1 and ISO 834-1.
Bauteile bzw. Tragwerke aus Hochleistungsbetonen müssen in der Regel gegen brandinduzierte Abplatzungen mit geeigneten Maßnahmen geschützt werden, um einen ausreichenden Feuerwiderstand im Brandfall zu gewährleisten. Die bisher wirtschaftlich und technologisch sinnvollste Methode zur Verhinderung von explosionsartigen Betonabplatzungen im Brandfall ist die Zugabe von Polypropylen-Fasern. Die Wirksamkeit der Fasern konnte zwar empirisch gezeigt werden, es stellt sich allerdings die Frage, welche Mechanismen zur Verhinderung der Abplatzungen führen. Der vorliegende Beitrag fasst bisherige Theorien zur Wirkungsweise von Polypropylen-Fasern in brandbeanspruchten Hochleistungsbetonen zusammen und stellt eine innovative Methodologie zur Erforschung der mikrostrukturellen Prozesse vor. Die Ergebnisse zeigen, dass die nach dem Schmelzen und Zersetzen der Polypropylen-Fasern frei werdenden Mikrokanäle durch eine gleichzeitig einsetzende Mikrorissbildung netzartig verbunden werden. Die Mikrorissbildung ermöglicht somit den Abbau von Eigen- und Zwangsspannungen im Beton (mechanischer Effekt) und die Entstehung eines Transportwegesystems für den ausströmenden Wasserdampf (Permeationseffekt).--------------------------------------------------------------------------- Structural members and bearing structures of high performance concrete generally have to be protected against explosive spalling due to fire exposure to guarantee a sufficient fire resistance. Up to now, the economically and technologically most worthwhile method to prevent explosive spalling is the addition of polypropylene fibres. Though the effectiveness of the fibres could be shown empirically, the mechanisms preventing explosive spalling are still debatable. The present article summarizes the existing theories concerning the mode of action of polypropylene fibres in fire exposed high performance concretes and presents an innovative methodology for analysing the micro structural processes. The results show that due to the thermal decomposition of the polypropylene fibres micro channels are created and simultaneously connected due to a netlike micro crack formation. This enables the relief of internal stresses (mechanical effect) and the formation of a permeable transport system for the escaping water vapour (permeation effect).
Though, concrete in general is a non-combustible building material, modern High Performance Concrete (HPC) is very susceptible to violent explosive spalling during a fire attack. This requires protective measures for fire safety design of concrete structures. The current most worthwhile method to prevent explosive spalling is the addition of monofilament Polypropylene fibres (PP-fibres). However, since it has become common knowledge that PP-fibres are suitable for fire safety design, a variety of theories concerning the mode of action of PP-fibres have been suggested. The present article summarizes the most important hypothesis and presents an innovative method for the analysis of micro structural processes in heated specimens. The results show that due to the thermal decomposition of PP-fibres capillary channels are created. Simultaneously, a netlike micro crack formation occurs, which connects these capillary channels. This enables the relief of internal stresses (mechanical effect) and the formation of a permeable transport system for the escaping water vapour (permeation effect).
Water migration in one-side heated concrete: 4D in-situ CT monitoring of the moisture-clog-effect
(2019)
Explosive spalling due to fire exposure in concrete structures can lead severe damage and, in the worst case, to premature component failure. For this reason, an in situ investigation of water Migration in concrete due to surface heating was undertaken.
During these experiments, a miniaturized concrete specimen within a confining and insulating double-hull was subjected to surface heating during simultaneous X-ray computed tomography (CT) scanning. Through the use of subtraction-based Image analysis techniques, it was possible to observe and quantify not only drying within areas of the concrete matrix close to the heated surface, but also the migration of moisture to both pore and matrix regions deeper within the specimen. It was also discovered that the correction of CT images for specimen deformation using DVC and variable detector performance using calibrated image filters significantly improved the quality of the results. This clearly demonstrates the potential of X-ray CT for evaluation of other rapid-density-change phenomena in concrete and other building materials.