In this work, four triazole-based poly(ether-pyridine)s polymers were synthesized and used as an adsorbent for the removal of phenolic compounds from aqueous solutions. For this purpose, new fluoromonomers containing 1,2,3-triazole units were prepared by the Cu(I)-catalyzed 1,3-dipolar cycloaddition reaction and then used for the elaboration of novel poly(ether-pyridine-triazole)s (PEPTs) by direct polyconden-sation with isosorbide and bisphenol A. Chemical structure of fluorinated pyridinicmonomers as well as resulting polymers was confirmed by 1H and 19F NMR spectroscopic methods. The thermal behavior of the obtained PEPTs was characterized using differential scanning calorimetry and thermogravimetric analysis. Results of sorption showed that polymers can be effectively used as a sorbent for the removal of polarorganic pollutants. The isosorbide-based poly(ether-pyridine-triazole) which contains hydrophilic hydroxyl groups as pendants chains (P4) exhibited the highest sorption efficiencies (78%–100% after 1 h). In order to explain the results an adsorption mech-anism mainly based on π–π interactions and hydrogen bonding with the pendent groups is proposed.
Cyclic and linear poly(L-lactide)s by ring-expansion polymerization with Bu2SnO, Oct2SnO, and Bu2SnS
(2023)
To elucidate the usefulness of commercial Bu2SnO as catalyst for syntheses of linear and/or cyclic polylactides L-Lactide was polymerized in bulk with variation of the LA/Cat ratio, temperature and time. Based on a ring-expansion polymerization (REP) mechanism cyclic polylactides (PLAs) with weight average molecular weights in the range of 200,000–300,000 are obtained at the highest temperature (180 °C). Polymerizations at 150 °C yielded crystalline, mainly cyclic polylactides which, after annealing, showed high melting temperatures (up to 197.5 °C) and high crystallinities (>80%). Polymerization at 120 °C confirmed the trend towards more linear chains with lower temperatures but yielded extended-ring crystals showing a “saw-tooth pattern” in the mass spectra. Oct2SnO gave similar results as Bu2SnO. Bu2SnS proved a sluggish polymerization catalyst, but a good transesterification catalyst in solid PLA.