Compared to its intrinsic strength, the practical strength of glasses is substantially
lowered by microscopic flaws. Their sub critical growth from the surface is strongly
affected by ambient humidity.
A new device was designed to enable the observation of sub critical crack growth
(SCCG) in vacuum and controlled atmosphere. It allows measurements in transparent and
semi-transparent materials in double cantilever beam (DCB) geometry. The aim of the
present work is to study the effect of crystals on crack growth.
Premature failure of glass under load is caused by sub-critical crack growth (SCCG) originate from microscopic flaws at the surface. While SCCG is related to the humidity of the ambient atmosphere, leading to stress corrosion phenomena at the crack tip, the detailed mechanism and the effect of different network formers are still not fully understood. For more clarity, various soda silicate glasses with a second network former were investigated by double cantilever beam technique: Na2O*Al2O3*SiO2 (NAS), Na2O*B2O3*SiO2 (NBS), Na2O*PbO*SiO2 (NPbS).
Three effects on the crack growth velocity, v, versus stress intensity, KI, curves were found out. The slope in region I, which is limited by corrosion, increases in the order NAS < NBS ≲ NPbS. The velocity range of region II reflecting the transition between corrosion effected and inert crack growth (region III), varies within one order of magnitude between the glasses. The KI region of inert crack growth strongly scatters between 0.4 and 0.9 MPam1/2. For comparison, crack growth at different humidity in commercial soda lime silicate glass (NCS) was measured.
The practical strength of glasses under ambient conditions is substantially lower compared to its intrinsic strength because of sub-critical crack growth (SCCG) from microscopic flaws. While SCCG is related to the humidity of the ambient atmosphere, leading to stress corrosion phenomena, the detailed kinetics are still not fully understood. To get better insight to the contribution of water on the crack-tip, highly water bearing glasses will be investigated by a new device for inert SCCG-measurements using double cantilever beam (DCB) geometry specimens. This device was designed to investigate the stress intensity factor in modus I and crack velocity in vacuum, but different atmospheres can also be introduced.
For validation of the new device, first experiments were performed on microscope slides as well as on a soda-lime silicate and a borosilicate crown glass. The results achieved will be presented in comparison to the published results of Wiederhorn.
Glass strength and fatigue is limited by surface cracks. As subcritical crack growth (SCCG) is governed by ambient humidity, stress corrosion at the crack tip is widely accepted to be the underlying mechanism. However, as water is known to have decisive effect on glass properties and can rapidly enter the crack tip near glass region, SCCG could be affected by such water related phenomena. We tried to mimic these effects studying water dissolution and speciation, mechanical properties, and SCCG in water-bearing glasses. For this purpose, glasses up to 8 wt% water have been prepared by means of high-pressure melting of glass powder - water mixtures.
As part of this effort, SCCG in dry and hydrous commercial micros¬cope slide glass (CW = 6 wt%) was studied in double cantilever beam (DCB) geometry and sub-Tg relaxation was measured by Dynamic Mechanical Analysis (DMA).
For SCCG in ambient air (24% r.h.), SCCG was promoted by the presence of 6wt% bulk water with respect to the dry glass. On the other hand, stress intensity values, KI, required to cause slow crack growth (v < 10-6 ms-1) resemble literature findings for float glass of similar composition in liquid water, which might represent the maximum possible promoting effect of ambient water on SCCG.
For SCCG in vacuum (10-3 mbar), dissolved bulk water causes even more pronounced effects. Most strikingly, it strongly decreases the slope of the log v(KI)-curve, which is a measure of dissipated energy during fracture. A strong increase of sub-Tg relaxation with increasing water content was confirmed by DMA. As a consequence, slow crack growth occurs at KI values as measured in the dry glass whereas fast crack growth occurs at much larger KI than that of the dry glass. Kinks and shoulders shown by the inert log v(KI)-curve indicate that bulk water does not simply affect bulk mechanical properties.
As part of a joint project involving the Fraunhofer Institute for Silicate Research (ISC), the Friedrich Schiller University of Jena, the Clausthal University of Technology and the Federal Institute for Materials Research and Testing (BAM), digital tools are to be created for the development of new types of glass materials. Current processes for the production of glasses with improved properties are usually very cost- and energy-intensive due to the low degree of automation and are subject to long development cycles. The use of robotic synthesis processes in combination with self-learning machines is intended to overcome these problems in the long term. The development of new types of glass can then not only be accelerated considerably, but also be achieved with much less effort.
In this talk, data generation via a robotic high-throughput glass melting system is presented, which should be the experimental basis for the ontology developed within the project GlasDigital.
GlasDigital
(2023)
Der aktuelle Stand des MateriaDigital Projektes GlasDigital wird vorgestellt. Hierbei wird allgemein die Problem- und Zielstellung präsentiert, als auch auf 2 separaten Postern die Ergebnisse. Diese beinhalten zum Einen die smarte Gestaltung der robotergestützten Glasschmelzanlage der BAM inkl. Analytik und zum Anderen die Digitalisierungsbestrebungen im Bereich Glas, d.h. ML-gestützte C-S-P-Simulation, Ontologie für den Werkstoff Glas, Digitaler Zwilling des Gießprozesses.