Ceramic particulate composites in the system SiC-TiC-TiB2 sliding against SiC and Al2O3 under water
(1999)
The tribological behaviour of SiC, SiC-TiC and SiC-TiC-TiB2 was determined in oscillating sliding against SiC and -Al2O3 in water at room temperature. The tribo-systems with the composite materials containing TiC and TiB2 differ significantly from the systems with the single phase SiC: The wear is reduced and the friction is increased. The wear reduction up to a factor of 10 is mainly due to the formation of an oxide film containing titanium oxides which is soft, stable in water and well adhering to the bulk material. This oxide film is transferred to the alumina ball but not to the silicon carbide ball.
The friction and wear behaviour of a new developed, pressureless sintered TiB2 ceramic was studied in comparison to SiC against SiC and Al2O3 balls under unlubricated conditions at room temperature. Special attention was paid to the influence of relative humidity on friction and wear results. For both ceramics the coefficient of friction against both ball materials decreases with increasing humidity and is higher in tests against alumina than against SiC. The wear rate is affected significantly by humidity and decreases by one order of magnitude for Al2O3/SiC system and by 2 orders of magnitude for SiC/SiC system. For TiB2 wear rates are nearly not affected by humidity against both ball materials and are much smaller than for SiC.
Tribological characterisation of siliconcarbonitride ceramics derived from preceramic polymers
(2006)
Amorphous SiCN ceramics were prepared in a laboratory scale as disk shaped specimens with 10 mm diameter and 0.3 mm thickness. The friction and wear behaviour was characterised in gross slip fretting tests under unlubricated conditions at room temperature against steel (100Cr6) and ceramic (Al2O3). Tests with a ball-on-disk contact were performed in laboratory air with different content of water vapour. The results show clearly that the relative humidity has a significant effect on friction and wear behaviour. All tests in dry air lead to higher friction and higher wear rate than in normal air. Improved friction and wear behaviour was observed with increasing pyrolysis temperature up to 1100 °C of the SiCN specimens. This is attributed to increasingly better mechanical properties and higher stiffness of the amorphous network due to the evaporation of gaseous organic species and the formation of free graphite like carbon.
Different fretting tests of thin steel wires under different conditions (loads, strokes, number of cycles and mean pressures) were performed. The wires used had 0.45 mm in diameter and the material was a cold-drawn eutectoid carbon steel (0.8% C) with a tensile strength over 2800 MPa. The tests were carried out with 90° "crossed cylinders" configuration varying the stroke, normal load and testing time (number of cycles). Afterwards the volumetric wear was obtained using surface profilometry with diamond stylus.
With a classical study of the coefficient of wear with respect to the sliding distance, the results show that the wear coefficient increases with normal load and stroke, consequently, for the same sliding distance, the wear produced was higher when the load and/or stroke is increased. In this work, the coefficient of wear is decreasing continuously as the test is running. In order to analyze better the wear behaviour, another method, in which the volumetric wear is compared with respect to the Archard's loading factor, is proposed. As result of this method, two distinctive behaviours were detected; one corresponds to the running-in period with a more aggressive wear behaviour and the second one to the stable steady state period. In all the tests the running-in period was similar with regard to the wear rates but in the stable period the wear rates were increasing with higher loads or strokes.
The influence of temperature and counterbody material on the tribological properties of a-C:H
coatings deposited on Cronidur 30 steel has been investigated in a lubricated ball on disk
contact situation with alpha-alumina and silicon nitride as counterbodies. The results show, that the wear volumes of the systems increase exponentially with increasing temperature, for alpha-alumina more than for silicon nitride. Two different wear mechanisms seem to have a
major influence: First, the abrasive action due to materials hardness and second, the tribo-oxidation when silicon nitride is counter material.
Three different contact geometries, ball on disk and two different settings with crossed cylinders have been investigated with regard to the agreement of the results of the tribological quantities determined by each method. The material combination was α-alumina as upper specimen and steel 100Cr6 as lower specimen. For each of the contact geometries 5 independent measurements were carried out and evaluated independently. The agreement between the single results of coefficient of friction and the coefficient of system wear as well as between the different groups and conditions are good. Largest scatter of the results were found in the dry air regime where both friction and wear depend strongly on the relative humidity. However, comparison of the absolute values of the coefficient of wear between the ball on disk contact geometry on one side and the 2 crossed cylinder contact geometries on the other side reveals a significant difference in that the ball on disk results are lower by about a factor of two. The results document also a high degree of repeatability of single wear tests.
Wear mechanisms, as adhesion, abrasion, fatigue and tribochemical wear, are complex in their physical and chemical nature. A theoretical description and prediction of wear are in most cases still far from reality. It is, therefore, important to use test rigs before a practical application of a given material combination under tribological loading.
On the other hand, model equations can be helpful for wear description, if a single wear mechanism is dominant.
Under oscillating and continuous sliding contact conditions, equations for wear calculation are presented to describe running-in and stationary wear behaviour of metals and ceramics. By using shear energy density, real area of contact, flash temperature, activation energy and numerical simulations with the method of movable cellular automata (MCA), wear data were calculated and compared to experimental laboratory results.
An extended study on tribological properties of carbon nitride coatings under oscillating sliding conditions has been carried out. The coatings were prepared by reactive magnetron sputtering with graphite target using nitrogen as reactive gas in an argon/nitrogen atmosphere during the deposition process to deposit carbon nitride, CNx. Coating thickness was about 2 µm. A 200300 nm thick Ti interlayer was used to enhance adhesion. The nitrogen flow during the deposition was varied to control the amount of nitrogen in the coating. Maximum amount of N-content was about 28 at%, achieved at a maximum N2 flow rate. Other deposition parameters were target to substrate distance, substrate temperature during deposition and bias voltage. The results show a large variation of hardness depending mainly on the nitrogen content and bias voltage. Higher bias voltage produced harder coatings as did lower nitrogen content. The tribological properties were tested unlubricated and lubricated by paraffin oil under gross slip fretting conditions at room temperature against alumina as counter material. Most coatings, but not all, showed a more or less pronounced dependence of wear on relative humidity with wear rates from 10-5 to 10-6 mm3/Nm. The best coatings with regard to a low wear rate and the least dependence upon relative humidity were carbon nitride coatings deposited at elevated substrate temperatures up to 350 °C. The wear resistance of these coatings was increased under the most severe conditions by about one order of magnitude. The results are discussed on the basis of a transfer layer formation. The results show clearly that wear is not significantly correlated to the coating hardness which itself is strongly dependant on the nitrogen content. However, under lubricated conditions with paraffin oil, wear rates were generally very low with wear coefficients at about 10-8 mm3/Nm.
The friction and wear properties of polyetherimide composites under dry oscillating sliding condition at room temperature (RT) as well as at elevated temperature (120 °C) was investigated. The polymer specimens were made to oscillate against steel cylinder as a counterpart. The friction and wear properties of PEI and composites were strongly influenced by the temperature. In case of carbon fiber composite abrasive action of carbon fibers has severely damaged the counterpart and resulted in accelerated wear of the composite at RT. Solid lubricants filled (PTFE, MoS2, graphite) along with glass fiber is beneficial in improving the friction and wear performance of the PEI composite at RT, whereas at elevated temperature wear performance was deteriorated.
The influence of temperature and counterbody material on the tribological properties of a-C:H coatings deposited on Cronidur 30 steel has been investigated in a lubricated ball on disk contact situation. The results show, that the wear volumes of the system increase exponentially with increasing temperature. Two different wear mechanisms seem to have a major influence: First, the abrasive action due to materials hardness and second, the tribooxidation when silicon nitride is counter material.
Pristine, reduced, and alkylated graphene oxides are applied as lubricating additives in paraffin grease. It has revealed that their crystalline structure governs the tribological properties of grease for steel tribo-pair. The microstructural analyses of grease samples showed that a loose fiber network of soap in the presence of graphene-based additive allows their facile release for efficient lubrication. The surface analyses based on the microscopic and elemental mapping show the development of a graphene-derived protective film on the worn scars, which protected the tribo-surfaces and subsided the wear. The reduced graphene oxide (rGO) with the interlamellar distance of 0.35 nm in the (002) plane provided minimum resistance to shear and exhibited maximum reduction in coefficient of friction (COF) for the paraffin grease. The presence of oxygen functionalities in the basal of pristine and alkylated graphene oxide (GO) compromised the interlamellar shearing under tribo-stress; consequently, higher COF than that of rGO.