The non-destructive assessment of cracks in concrete is a common task for which non-destructive evaluation solutions have been published. Primarily, these tests have been carried out on artificial cracks that have been created by using notches instead of natural cracks. This study evaluates a procedure designed to create reproducible and controlled cracks in concrete. The procedure is based on using expanding mortar in a series of blind holes. This is done in combination with carefully aligned reinforcement to guide the direction of the crack development. The depth of the crack is also controlled by reinforcement. Crack depth varies statistically in the range of the Maximum aggregate size (16 mm) used for concrete.
Locating and sizing delaminations is a common inspection task in the maintenance and quality control of construction and rehabilitation. Their detection is an important area of application of nondestructive testing in civil engineering (NDT-CE). To improve this application, NDT test systems and test solutions must be compared, for which specimens containing well-defined delaminations are needed to serve as a reference. Currently, there are no widely accepted procedures available for creating such flaws locally and reproducibly. This study presents procedures for creating artificial delaminations repeatably and as close as possible to natural delaminations. To produce the discontinuities only substances were used which can occur in concrete components and do not affect the application of NDT-CE methods. Ultrasonic pulse-echo (UPE) was used to test the flaws in the specimens. The delaminations were created by applying expansive mortar in prepared through holes. Three specimens with two delaminations each were built and tested using UPE.
Decades of non-destructive evaluation (NDE) for the quality assurance of concrete bridges revealed the necessity of developing procedures for building reference specimens for different defects. External objects have been widely used in specimen construction to represent defects. However, embedded materials can alter the actual defect characteristics, interrupting the NDE responses. This study proposes new approaches to fabricating reference specimens for reinforced concrete that feature substantial defects, including cracks, delamination, honeycombing and rebar corrosion, without external objects. As a result, realistic responses can be acquired to identify promising NDE methods for characterising actual deteriorations. The procedures were produced with the intent of being reproducible in any laboratory. Destructive and non-destructive testing methods were performed to verify the effectiveness of the processes in creating defects. This study provides research laboratories with techniques for
fabricating reference specimens for characterising defects and assessing the performance of NDE technologies.