In contact with aqueous media glass tends to corrode leading to different surface properties. For the precision application this alteration might cause product failure. Hence precise knowledge of the surface interactions is essential. We performed an extensive investigation on the behavior of borosilicate glass under corrosive attack in order to identify critical processes. We identified appropriate investigation methods including sequential chemical analysis, ATR-IR, ellipsometry and SNMS. These techniques allow to identify the influence of specific production processes.
Industrial quality control (QC) nowadays requires the visualization of surface modifications from the macro-scopic to the microscopic or even nanoscopic scale. This is a prerequisite to the evaluation of functionality and reliability, the detection of defects and their separation of artefacts. The diversity of applications ranges from low-E glazings and solar panels, micro- and optoelectronics, micro- and smart devices to sensor-on-chip and lab-on-chip systems [1]. Optical microcopy (light, confocal laser scanning, white light interference) as established QC-tool is operated at normal incidence, i.e. p- and s-polarization are undistinguishable. Either light-intensity in terms of grey scale and colour or intensity-correlated effects of phase shifts are used. In case of ellipsometry, operated at oblique incidence, p- and s-polarization matter, and amplitude ratios and phase shifts upon reflection are measured. Hence, information content must be much higher.
The visualization of surface modifications may be very challenging for coating/substrate systems of either al-most identical optical constants, e.g. transparent films on substrates of the same material, or minor film thick-ness, substance quantity and affected area, e.g. ultra-thin or island films. Ellipsometry gives access to the con-trast of intensity (I), amplitude ratio (Ψ), and phase shift (Δ) with nanometer-scaled vertical and micrometer-scaled lateral sensitivity, one is able to identify tiny changes within an unmodified surface. As both mapping ellipsometry (ME) and imaging ellipsometry (IE) are operated in the optical far-field, surface inspection is also possible on the macroscopic scale. Near the Brewster-angle of the bare, undamaged, clean, and fresh substrate, the contrast to add-on and sub-off features is superior.
Fig. 1 shows three examples of ellipsometric imaging, i.e. a thin SnO:Ni film on SiO2/Si (Fig. 1a), a dried stain of an anti-body solution on cyclo-olefin-polymer (COP) shown in Fig. 1b, and a polyimide film residue on SiO2/Si (Fig. 1c). For all of these examples, ellipsometry provides much better contrast between substrate and surface modification than optical microscopy, sometimes primarily caused by the oblique incidence (Figs. 1a and 1c), in other cases related to the phase sensitivity of ellipsometry (Fig. 1b). Other examples are laser surface modifications and the corrosion of glass. In these cases, optical microscopy and IE yield to similar results, how-ever only ellipsometry gives access to modelling.
Further investigated coating/substrate systems are 100Cr6 steel, native oxide on silicon, borosilicate glass, and the polymer polycarbonate with deposited films of graphene and ta-C:H, printed and dried pattern of liquids such as water, cleaning agents, and dissolved silicone. Besides imaging ellipsometry, referenced spectral ellipsometry (RSE) has been applied, combining the advantages of both optical microscopy (fast measurement) and ellipsometry (high sensitivity to tiny modifications).