Filtern
Dokumenttyp
- Forschungsdatensatz (11)
- Zeitschriftenartikel (9)
- Sonstiges (1)
- Forschungsbericht (1)
Sprache
- Englisch (22)
Schlagworte
- SAXS (22) (entfernen)
Organisationseinheit der BAM
- 6 Materialchemie (22)
- 6.5 Synthese und Streuverfahren nanostrukturierter Materialien (22)
- 6.6 Physik und chemische Analytik der Polymere (4)
- 6.0 Abteilungsleitung und andere (2)
- 6.3 Strukturanalytik (2)
- VP Vizepräsident (2)
- VP.1 eScience (2)
- 5 Werkstofftechnik (1)
- 5.1 Mikrostruktur Design und Degradation (1)
- 6.1 Oberflächen- und Dünnschichtanalyse (1)
he main objective of the nPSize project is to improve the measurement capabilities for nanoparticle size based on both measurement methods traceable to SI units and new reference materials. Two basic approaches have been used in order to develop measurement procedures resulting in traceable results of the nanoparticle size distribution: physical modelling for the methods used in the project (TSEM, SEM, AFM and SAXS) and machine learning.
Physical modelling: In this part, the physical models associated with different shape measurements for the techniques TSEM, SEM, AFM and SAXS have been collected and further developed with the aim to simulate the resulting signal as measured by the individual methods. Uncertainties and traceability associated with each model were investigated and evaluated. In the following, the progress on these physical models is reported for each individual method.
Machine Learning modelling: The aim of this part is to use machine learning to enable automatic measurement of nanoparticle shape from expert a-priori information only. No physical model will be used as a-priori information in this task.
The accuracy and traceability of the size results obtained by each technique will be analyzed and compared with the physical modelling. A machine learning database will then be used to create automatic detection algorithms.
Assembly of permanently porous metal–organic polyhedra/cages (MOPs) with bifunctional linkers leads to soft supramolecular networks featuring both porosity and processability. However, the amorphous nature of such soft materials complicates their characterization and thus limits rational structural control. Here we demonstrate that aging is an effective strategy to control the hierarchical network of supramolecular gels, which are assembled from organic ligands as linkers and MOPs as junctions. Normally, the initial gel formation by rapid gelation leads to a kinetically trapped structure with low controllability. Through a controlled post-synthetic aging process, we show that it is possible to tune the network of the linked MOP gel over multiple length scales. This process allows control on the molecular-scale rearrangement of interlinking MOPs, mesoscale fusion of colloidal particles and macroscale densification of the whole colloidal network. In this work we elucidate the relationships between the gel properties, such as porosity and rheology, and their hierarchical structures, which suggest that porosity measurement of the dried gels can be used as a powerful tool to characterize the microscale structural transition of their corresponding gels. This aging strategy can be applied in other supramolecular polymer systems particularly containing kinetically controlled structures and shows an opportunity to engineer the structure and the permanent porosity of amorphous materials for further applications.
Herein, we provide a "systems architecture"-like overview and detailed discussions of the methodological and instrumental components that, together, comprise the "MOUSE" project (Methodology Optimization for UltrafineStructure Exploration). The MOUSE project provides scattering information on a wide variety of samples, with traceable dimensions for both the scattering vector (q) and the absolute scattering cross-section (I). The measurable scattering vector-range of 0.012≤ q (nm-1) ≤ 92, allows information across a hierarchy of structures with dimensions ranging from ca. 0.1 to 400 nm. In addition to details that comprise the MOUSE project, such as the organisation and traceable aspects, several representative examples are provided to demonstrate its flexibility. These include measurements on alumina membranes, the tobacco mosaic virus, and dual-source information that overcomes fluorescence limitations on ZIF-8 and iron-oxide-containing carbon catalyst materials.
Mechanically stable structures with interconnected hierarchical porosity combine the benefits of both small
and large pores, such as high surface area, pore volume, and good mass transport capabilities. Hence, lightweight micro-/meso-/macroporous monoliths are prepared from ordered mesoporous silica COK-12 by means of spark plasma sintering (SPS, S-sintering) and compared to conventionally (C-) sintered monoliths. A multi-scale model is developed to fit the small angle X-ray scattering data and obtain information on the hexagonal lattice parameters, pore sizes from the macro to the micro range, as well as the dimensions of the silica population. For both sintering techniques, the overall mesoporosity, hexagonal pore ordering, and amorphous character are preserved. The monoliths' porosity (77–49%), mesopore size (6.2–5.2 nm), pore volume (0.50–0.22 g cm-3
), and specific surface area (451–180 m2 g-1) decrease with increasing processing temperature and pressure. While the difference in porosity is enhanced, the
structural parameters between the C-and S-sintered monoliths are largely converging at 900 C, except for the mesopore size and lattice parameter, whose dimensions are more extensively preserved in the
S-sintered monoliths, however, coming along with larger deviations from the theoretical lattice. Their higher mechanical properties (biaxial strength up to 49 MPa, 724 MPa HV 9.807 N) at comparable porosities and ability to withstand ultrasonic treatment and dead-end filtration up to 7 bar allow S-sintered monoliths to reach a high permeance (2634 L m-2 h-1 bar-1), permeability (1.25 x 10^-14 m2), and ability to reduce the chemical oxygen demand by 90% during filtration of a surfactant-stabilized oil in water emulsion, while indicating reasonable resistance towards fouling.
OpenSCAD, STL and technical drawings for the capillary flow-through cell designed primarily for use with The MOUSE instruments.
This flow-through cell can be used in conjunction with:
- Modular sample holder (10.5281/zenodo.7499416)
- Solid sample rack/plate (10.5281/zenodo.7499424)
- Laser-cut sample holder (10.5281/zenodo.7499437)
Technical drawings and documents for building a compact, heated, vacuum compatible flow-through sample holder. This holder is in use at the BAM MOUSE instrument as well as at the I22 beamline at the Diamond Light Source (see references for instrument details).
This holder has several features:
- The holder can be used in vacuum environments as well as in atmosphere
- It has two G 1/4" UNF fittings to attach HPLC tubing for (optionally) flowing a medium through the sample cell
- There are two additional (unflowed) sample positions for backgrounds and calibrants, held at the same temperature
- The low-mass design coupled with a 250W heating element can achieve heating rates of 1 degree C per second, when coupled (for example) with an Omron E5CC PID controller.
- The sample holder insert can be made from various materials depending on the application. Sealing the sample from the vacuum can be achieved using kapton, teflon or Magic tape, depending on the temperature requirements. The inlet and outlet holes will need to be punctured with a needle to enable flow.
- Large exit cones ensure a clear exit angle of at least 45 degrees two theta.
- It has been tested with temperatures up to 400 degrees C.
- Compression area has been raised and polished to ensure a good vacuum seal.
OpenSCAD, STL and technical drawings for the solid sample rack designed primarily for use with The MOUSE instruments.
This solid sample rack can be used in conjunction with:
- Laser-cut sample holder (10.5281/zenodo.7499437)
- Modular sample holder (10.5281/zenodo.7499416)
- Capillary flow-cell for liquid samples (10.5281/zenodo.7499421)
PDF file for the laser-cut sample holder designed primarily for use with The MOUSE instruments.
This sample holder can be used in conjunction with:
- Solid sample rack/plate (10.5281/zenodo.7499424)
- Modular sample holder (10.5281/zenodo.7499416)
- Capillary flow-cell for liquid samples (10.5281/zenodo.7499421)
The Lycurgus cup is an ancient glass artefact that shows dichroism as it looks green when a white light is reflected on it and a red colouring appears when a white light is transmitted through it. This peculiar dichroic effect is due to silver and gold nanoparticles present in the glass. In this research we show the synthesis of dichroic silver nanoparticles and their embedding in a 3D printable nanocomposite. The addition of gold nanoparticles to the silver nanoparticle composite, gave a 3D printable nanocomposite with the same dichroism effect of the Lycurgus cup.
Metal carbides have shown great promise in a wide range of applications due to their unique catalytic, electrocatalytic and magnetic properties. However, the scalable production of dispersible metal carbide nanoparticles remains a challenge. Here, we report a simple and scalable route to dispersible iron carbide (Fe3C) nanoparticles. This uses MgO nanoparticles as a removable ‘cast’ to synthesize Fe3C nanoparticles from Prussian blue (KFeIII[FeII(CN)6]). Electron tomography demonstrates how nanoparticles of the MgO cast encase the Fe3C nanoparticles to prevent sintering and agglomeration during the high-temperature synthesis. The MgO cast is readily removed with ethylenediaminetetraacetic acid (EDTA) to generate Fe3C nanoparticles that can be used to produce a colloidal ferrofluid or dispersed on a support material.