The aluminium alloy 2618A is an Al-Cu-Mg alloy which is part of the 2xxx series of age-hardenable alloys. These materials are designed for long-term Operation in transportation and aerospace industries. The desired properties, e.g. creep behavior, hardness, and damage tolerance, are controlled by the distribution of fine precipitates formed within the matrix. However, the strength of the material declines du ring exposition to elevated temperatures due to the overageing of the S-phase precipitates (AI2CuMg) and the conversion of the S-phase into the stable equilibrium S-phase. A quantitative model of the overageing process at application relevant temperatures would be desirable for accurate predictions of component lifetime made from the 2618A alloy.
The aluminum alloy 2618A is an Al-Cu-Mg alloy with additions of Fe and Ni, which was designed for long-term operation at elevated temperature in transportation and aerospace industries. Typical applications include aircraft parts and structures (sheet material) or engine components such as turbo charger centrifugal compressor wheels (forged material). Such components are subjected to prolonged aging during service, (e.g. 50 000 h) at temperatures which are close to their age hardening temperature (ca. 190 °C).
The microstructural evolution during creep exposure is studied.
The aluminum alloy 2618A is an Al-Cu-Mg alloy with additions of Fe and Ni, which was designed for long-term operation at elevated temperature in transportation and aerospace industries. Typical applications include aircraft parts and structures (sheet material) or engine components such as turbo charger centrifugal compressor wheels (forged material). Such components are subjected to prolonged aging during service, (e.g. 50 000 h) at temperatures which are close to their age hardening temperature (ca. 190 °C). The microstructural evolution was investigated.
In the present work, the titanium alloy Ti-6.8Mo-4.5Fe-1.5Al (Timetal LCB) was investigated with respect to the microstructural evolution during strain controlled fatigue loading. The alloy was developed to reduce the generally high material costs of β-alloys by substituting expensive beta stabilizers by using a standard Fe-Mo master alloy. One possible application seen in the automotive industry is the substitution os suspension structural parts currently made of steel, suc as suspension springs. These components require a high strength and fatigue resistance.
Materials subjected to high-temperature service conditions will change their microstructure with time. Associated with this aging process is a change of mechanical properties as well as a change of damage mechanisms. Within the scope of the FVV project Aging and Lifetime, Fraunhofer IWM in Freiburg and BAM in Berlin (both Germany) experimentally characterized the widespread high-temperature aluminum alloy EN AW-2618A in different overaging states. Based on the experimental findings, models for numerical lifetime assessment with the finite-element method were implemented.
Aluminiumlegierungen mit besonders hoher Festigkeit werden vor allem in der Luft- und Raumfahrt sowie der Automobilindustrie eingesetzt. Ein Anwendungsbeispiel im Fahrzeugbereich sind Radialverdichterräder von Abgasturboladern. Der hierfür untersuchte Werkstoff ist die Legierung 2618A. Die hohe Festigkeit wird durch Ausscheidungshärtung erreicht. Es scheiden sich hierbei durch eine entsprechende Wärmebehandlung Al-Cu-Mg-Teilchen in die Aluminium-Matrix aus. Diese Teilchen stellen Hindernisse für die Bewegung von Versetzungen dar und haben im Fall der Legierung 2618A stabförmige Geometrie. Durch Einsatz bei Betriebstemperatur von etwa 160 °C bis 190 °C vergröbern die Teilchen im Verlauf der Einsatzzeit (Ostwaldreifung) und die Festigkeit nimmt ab.
Der Zwischenbericht soll einen Überblick über die bisherigen experimentellen und theoretischen Ergebnisse geben. Es konnten Brinell-Härteverläufe nach Auslagerung bei 160 °C, 180 °C und 190 °C bis 8.760 h Auslagerungszeit gemessen werden. Erste TEM (Transmissionselektronenmikroskopie )-Untersuchungen der Mikrostruktur liegen vor. Anhand dieser Untersuchungen wurden erste Simulationen und Berechnungen der AI-Cu-Mg-Teilchengrößenentwicklung (Vergröberung) durchgeführt. Auswirkungen dieser Vergröberung der AlCu-Mg-Teilchen auf die Fließgrenze bei Raumtemperatur wurden berechnet. Weitere Ergebnisse sind Kriechversuche an Proben im Ausgangszustand T61 der Legierung 2618A bei den Temperaturen 160 °C, 180 °C und 190 °C. Um das zyklische visko-plastische Verhalten des Werkstoffes und den Einfluss der Alterung zu untersuchen, wurden LCF-Ermüdungsversuche an verschiedenen Auslagerungszuständen durchgeführt.