Filtern
Erscheinungsjahr
Dokumenttyp
- Beitrag zu einem Tagungsband (90)
- Zeitschriftenartikel (73)
- Vortrag (60)
- Buchkapitel (5)
- Beitrag zu einem Sammelband (4)
- Posterpräsentation (4)
- Dissertation (1)
- Sonstiges (1)
- Forschungsbericht (1)
Sprache
- Englisch (151)
- Deutsch (78)
- Mehrsprachig (10)
Schlagworte
- Rheology (55)
- Cement (49)
- Concrete (30)
- Africa (16)
- Rheologie (14)
- Superplasticizer (14)
- Polysaccharides (13)
- Self-compacting concrete (13)
- Admixtures (12)
- Polycarboxylate ether (11)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (55)
- 7.4 Baustofftechnologie (52)
- 6 Materialchemie (6)
- 6.6 Physik und chemische Analytik der Polymere (6)
- 1 Analytische Chemie; Referenzmaterialien (4)
- 1.2 Biophotonik (4)
- 7.2 Ingenieurbau (4)
- 7.0 Abteilungsleitung und andere (3)
- 8 Zerstörungsfreie Prüfung (3)
- 8.0 Abteilungsleitung und andere (3)
- 5 Werkstofftechnik (1)
- 5.6 Glas (1)
- 7.1 Baustoffe (1)
- 7.3 Brandingenieurwesen (1)
- 7.7 Modellierung und Simulation (1)
- KM Kommunikation, Marketing (1)
- MP Mitglied des Präsidiums (1)
Eingeladener Vortrag
- nein (60)
Design : and use of engineered recycled mineral admixtures obtained from industrial and mineral waste are promising strategies to increase the range of materials suitable for use in cement-based composites. In this work, Portland cement-blended pastes containing mineral admixtures designed for improving particle packing were evaluated in the presence of low- and high-charge polycarboxylate-based superplasticizers. The powders were obtained from basic oxygen furnace slag, iron ore tailings, quartz mining tailings, and quartzite mining tailings. The zeta-potentials of the particles were obtained via electrophoretic mobility. The flow properties were evaluated by rheological tests performed in a Couette type rheometer. The hydration kinetics was evaluated by isothermal calorimetry and an adapted method based on the Vicat needle test. The high-charge PCE and the finer mineral admixtures produced more stable blends. Coarser mineral admixtures led to increased flowability and delayed hydration compared to finer ones. Steel slag powders presented the most significant plasticizer effects, but also the largest setting delays and segregation tendency. Quartz-rich superfines reduced the setting delays caused by the superplasticizers. In summary, both superplasticizers were effective in improving flow properties, but the high-charge PCE was effective in preventing segregation in pastes containing mineral admixtures coarser and heavier than cement.
Viscosity modifying agents: Key components of advanced cement-based materials with adapted rheology
(2022)
Viscosity modifying agents (VMAs) are essential ingredients for the production of flowable cement-based materials. This paper presents an overview of commonly used VMAs and attempts to shed some light on the underlying physics at the origin of their mechanisms of action. The main molecular parameters of VMA controlling the rheological properties of the cement pore solution are highlighted. As the mechanisms of action of VMAs in cement-based materials are closely related to their affinity with the surface of cement particles, the adsorption of the main VMA types is discussed. The effect of VMAs on flow properties and stability of cement-based materials is presented for VMAs added without any superplasticizer, and then in systems incorporating both VMAs and superplasticizers. Finally, the effect of VMAs in enhancing concrete properties to secure adequate performance of different construction applications, and perspectives for future developments of novel cement-based materials made with VMAs are showcased.
NMR is becoming increasingly popular for the investigation of building materials as it is a non-invasive technology that does not require any sample preparation nor causes damage to the material. Depending on the specific application it can offer insights into properties like porosity and spatial saturation degree as well as pore structure. Moreover it enables the determination of moisture transport properties and the (re-)distribution of internal moisture into different reservoirs or chemical phases upon damage and curing. However, as yet most investigations were carried out using devices originally either designed for geophysical applications or the analysis of rather homogeneous small scale (< 10 mL) samples. This paper describes the capabilities of an NMR tomograph, which has been specifically optimized for the investigation of larger, heterogeneous building material samples (diameters of up to 72 mm, length of up to 700 mm) with a high flexibility due to interchangeable coils allowing for a high SNR and short echo times (50 - 80 m s).
In this paper, we demonstrate the value of 1H NMR relaxometry for studying the hydration of clinker-reduced, more climate-friendly cementitious binders. The results were obtained on typical CEM I cements and sister samples containing two different reactive agricultural ashes as well as non-reactive biochars as supplementary cementitious materials. The findings prove that time-resolved NMR measurements provide valuable additional information when combined with classical heat flow calorimetry.
In this work, engineered recycled mineral admixtures were obtained from four different industrial residues: basic oxygen furnace slag, iron ore tailings, quartz mining tailings and quartzite mining tailings.
The grinding performance was evaluated in two different programs and the characterization included chemical and mineralogical composition, particle morphology, and physical properties. Performance evaluations were carried out in blended pastes and mortars, including flow properties, hydration kinetics, soundness, pozzolanic activity, and compressive strength. Coarser-than-cement admixtures allowed better flow performance, greater dimensional stability and more economical production, while finer-thancementn admixtures improved mechanical performance by both filler effect and cementing activity.
The existing cement and concrete standards are not capable of making full use of the current technology capacity due to strong focus on conventional concrete and thus they are not fit for the current and future challenges of construction industry. The paper highlights shortcomings with regard to the implementation of the existing standards. It can be seen that future-oriented standards are generally required to contribute to a lower-carbon footprint of the industry. These changes are significantly more relevant in sub-Saharan Africa, due to the rapidly increasing urbanisation challenge and the enormous potentials to develop lower-carbon technologies than elsewhere in the world.
Effect of Polycarboxylate Superplasticizer in Ordinary Portland Cement and Sulfate Resistant Cement
(2023)
Polycarboxylate superplasticizers (PCE) are the most widely used admixtures in today’s cementitious construction materials. The molecular structure has a decisive influence on the effectiveness of PCE, which also can be tailored to serve in a different cementitious system.
The current study investigates the influence of the backbone charge density of PCE on the rheology, hydration kinetics, and adsorption behavior of ordinary Portland cement (OPC) and sulfate-resistant cement (SRC). The results indicate that regardless of the PCE type, OPC requires a higher amount of PCE to be adsorbed to induce changing of rheological parameters and hydration kinetics. Regardless of the cement type, the PCE with a higher charge density exhibits higher adsorption behavior, corresponding to lower viscosity measurement.
Compared to OPC, SRC is more sensitive to the introduction of both PCEs and has a lower saturation dosage, indicating that SRC generally provides better workability properties regardless of the PCE.
The structural build-up of fresh cement paste is often considered as a purely thixotropic phenomenon in literature even though cementitious materials undergo a non-reversible hydration process that can have an influence on the structuration process. In the current paper a method is proposed to validate the impact of the non-reversible structural build-up. It is shown that fresh cement paste samples lose their structural gain almost completely due to thixotropy while the structural build-up due to hydration can be observed but occurs in a significantly lower order of magnitude over the course of the first hours of hydration. In addition, it is shown, that the chemical component of the structural build-up accelerates with the onset of the acceleration period of hydration, while its contribution in the entire structural build-up remains constant.
Structural build-up describes the stability and early-age strength development of fresh mortar used in 3D printing. lt is influenced by several factors, i.e. the composition of the print able material, the printing regime, and the ambient conditions. The existing modelling approaches for structural build-up usually define the model parameters for a specific material composition with out considering the influence of the ambient conditions. The goal of this contribution is to explicitly include the temperature dependency in the modelling approach. Temperature changes have signifi cant impact on the structural build-up process: an increase of the temperature leads to a faster dissol ution of cement phases and accelerates hydration. The proposed extended model includes temperature dependency using the Arrhenius theory. The new model parameters are successfully calibrated based on Viskomat measurement data using Bayesian inference. Furthermore, a higher impact of the temperature in the re-flocculation as in the structuration stage is observed.