Effect of Polycarboxylate Superplasticizer in Ordinary Portland Cement and Sulfate Resistant Cement
(2023)
Polycarboxylate superplasticizers (PCE) are the most widely used admixtures in today’s cementitious construction materials. The molecular structure has a decisive influence on the effectiveness of PCE, which also can be tailored to serve in a different cementitious system.
The current study investigates the influence of the backbone charge density of PCE on the rheology, hydration kinetics, and adsorption behavior of ordinary Portland cement (OPC) and sulfate-resistant cement (SRC). The results indicate that regardless of the PCE type, OPC requires a higher amount of PCE to be adsorbed to induce changing of rheological parameters and hydration kinetics. Regardless of the cement type, the PCE with a higher charge density exhibits higher adsorption behavior, corresponding to lower viscosity measurement.
Compared to OPC, SRC is more sensitive to the introduction of both PCEs and has a lower saturation dosage, indicating that SRC generally provides better workability properties regardless of the PCE.
NMR is becoming increasingly popular for the investigation of building materials as it is a non-invasive technology that does not require any sample preparation nor causes damage to the material. Depending on the specific application it can offer insights into properties like porosity and spatial saturation degree as well as pore structure. Moreover it enables the determination of moisture transport properties and the (re-)distribution of internal moisture into different reservoirs or chemical phases upon damage and curing. However, as yet most investigations were carried out using devices originally either designed for geophysical applications or the analysis of rather homogeneous small scale (< 10 mL) samples. This paper describes the capabilities of an NMR tomograph, which has been specifically optimized for the investigation of larger, heterogeneous building material samples (diameters of up to 72 mm, length of up to 700 mm) with a high flexibility due to interchangeable coils allowing for a high SNR and short echo times (50 - 80 m s).
Influence of the hydroxypropylation of starch on its performance as viscosity modifying agent
(2022)
Synopsis: Starch is a commonly used viscosity modifying agent (VMA). The performance of starch as VMA depends on its origin (e.g. potato, corn, cassava, etc.) and corresponding molecular properties, such as molecular weight, ratio between amylose and amylopectin etc. Depending upon the application, the efficiency of starch can be enhanced by hydroxypropylation. The maximum degree of substitution (DoS) cannot be greater than 3.0, which is the number of hydroxy groups per glucose monomer in the polymer. In the current research three potato starches exhibiting the DoS of 0.4, 0.6 and 0.8 were utilised. The influence of the modified starch on the rheological properties and hydration of cement paste, as well as the viscosity of the pore solution were investigated. Our findings show that the starch with the highest DoS increases the dynamic yield stress the most, while the plastic viscosity is less dependent on the DoS. Additionally, starch with the highest DoS retards hydration to lower degree than other starches.
The presence of polycarboxylate ether (PCE) based superplasticizers (SPs) has an enormous influence on the early hydration of cement. The hydration is retarded and the timing of formation and the morphology of hydrates is affected. This short paper presents experimental results about the influence of delayed Addition time of PCE SPs on hydration of cement and tricalcium aluminate (C3A) pastes, investigated by isothermal heat flow calorimetry. For cement pastes the hydration is retarded with SP, whereby the high charge PCE has a stronger retarding effect than the low charge PCE. With delayed PCE addition the cement shows a less retarded setting than with simultaneous addition. The alteration caused by PCE is much more pronounced for C3A and gypsum mixes than for cement. If the SP is added simultaneous, the exothermic peak of C3A is retarded. However, with delayed addition of SP the hydration is shortened, the gypsum depletion is fastened and the exothermic peak occurs less retarded or even accelerated compared to simultaneous addition. It is obvious that for C3A pastes there is less retardation the later the Addition of SP. Furthermore, the PCE alter the hydration of C3A when added delayed and exhibit changes in kinetics and hydration rates. The rate of reaction in the second stage is lower, discernible in decreased slopes and broader peaks. Besides this, a distinct ramp in the C3A heat flow curves within the first stage of C3A hydration occurs for all pastes with delayed addition of SP, which suggests an accelerated ettringite formation.
Organic/inorganic mixtures were prepared from ordinary Portland cement (OPC), water (w/c 0.22), a fluorescent dye in aqueous solution (stable at alkaline pH; BAM-I), and two different comb shape polycarboxylates (PCEs), i.e., high charge (PCE-HC) and low charge (PCE-LC), respectively. Rheological and calorimetric measurements were performed prior to optical studies in order to select PCE concentrations. Absorption and fluorescence spectroscopy of the system OPC + BAM-I (CBAM-I) revealed maxima of dye BAM-I located at 645 nm and 663 nm, respectively. In presence of PCE-HC and PCE-LC, these mixtures displayed a small red shift in reflectance and a faster decrease in intensity compared to studies with CBAM-I; however, only slight differences were observed between the different PCEs. With time, all systems exhibited a decrease in intensity of BAM-I in absorption/reflectance and emission. This could be caused by dye adsorption and possibly decomposition when in contact with cement particles or hydration products.