Organic/inorganic mixtures were prepared from ordinary Portland cement (OPC), water (w/c 0.22), a fluorescent dye in aqueous solution (stable at alkaline pH; BAM-I), and two different comb shape polycarboxylates (PCEs), i.e., high charge (PCE-HC) and low charge (PCE-LC), respectively. Rheological and calorimetric measurements were performed prior to optical studies in order to select PCE concentrations. Absorption and fluorescence spectroscopy of the system OPC + BAM-I (CBAM-I) revealed maxima of dye BAM-I located at 645 nm and 663 nm, respectively. In presence of PCE-HC and PCE-LC, these mixtures displayed a small red shift in reflectance and a faster decrease in intensity compared to studies with CBAM-I; however, only slight differences were observed between the different PCEs. With time, all systems exhibited a decrease in intensity of BAM-I in absorption/reflectance and emission. This could be caused by dye adsorption and possibly decomposition when in contact with cement particles or hydration products.
South Africa and recently Nigeria are the only net exporter of cement in Africa, yet cements are imported into the country mainly on the basis of price competitiveness. This poses potential for scatter in the properties of the cements in the South African market as pricing seems to be the only determining factor that affects Portland cements imported. A survey of cements of grade 42.5N in the South African cement market was carried out to identify major players in the industry. The identified cements, which included four locally produced and one imported cement were then analysed for both chemical composition and physical properties in line with the Eurocode EN 196. Tests carried out include loss on ignition, chloride content, sulphate content, specific surface (Blaine), standard consistence, initial setting time, final setting time, soundness and flexural and compressive strength at 2, 7 and 28 days. The testing program was initiated as part of on-going Africa-wide cement testing competency program in partnership with BAM and PTB in Germany. The performance of the identified cements from the different local manufacturers and the imported cement were analysed and are presented in this paper. These results reveal some similarities and differences in the properties. Particularly of interest is the marked difference in the 28 days compressive strength of the cements. This paper shows that there is need for further tests across the cement industry as some of the cements failed to meet certain requirement as set by EN 196. The paper also recommends the use of proficiency testing schemes in the cement industry of the country to ensure the cement laboratories are providing results of high quality and at the same time act as a check to make sure these laboratories are not failing to meet standard requirements.
In the last years flowable concrete has become increasingly important in applications such as, for systems with highly reinforced concrete with a complicated formwork, or sprayed concrete and 3D-printing of concrete. For all these applications it is necessary to have tailored rheological properties. Rheology can be described by values of yield stress and plastic viscosity, which can be determined for example by evaluation of rheometer measurements. But for different materials various rheometers with different geometries and stirrers are being used. To see the effects from paste in concrete, it is necessary to investigate mixes of paste, mortar and concrete, stepwise. But currently there exists no device, which is calibrated for these different systems at once. Due to this fact, conventional tests such as V-funnel efflux-time and flow diameter were determined, as well as rheometer data in different cell sizes and geometries.
In this study the assessment of rheological effects in the binder on the rheology of mortar and concrete was investigated by using combination of two rheometers.
Concrete technology was exposed to a rapid development during the last three decades. For the longest time in its history, concrete was considered as a three component System consisting of aggregates, which are bound by the hardened cement paste consisting of hydrated cement. Traditionally, the only way of adjusting the consistency of concrete was using well adjusted aggregates and grading curves and adding excess water to the concrete, accepting that the latter in return reduces strength and durability. During the last three decades, however, concrete has developed further from a three component System towards an (at least) five component system, since the use of mineral additions and Chemical admixtures has become state of the art. Both components are able to enhance the workability, the compactability, and the density of the microstructure with effects on strength, ductility and durability, while cement can be saved in parallel. Due to reasonable use of admixtures and additions, concrete can be designed to match mechanically high performance specifications. Traditionally, cement paste was considered the weakest component in concrete. Flowever, in modern concrete a good paste composition can yield highest performance, passing the role of the mechanical bottleneck towards the aggregates.
The African cement, concrete and construction business is growing at rapid pace. The cement sales are expected to grow rapidly until 2050. The number of newly built cement plants increases dramatically and in addition more cements are being imported from outside the continent, e.g. from Turkey, Pakistan, Indonesia, and China, driven by overcapacities in the countries of origin. This causes a high number of potentials and challenges at the same time. Newly built cement plants can operate directly at best technological state of the art and thus incorporate more sustainable technologies as well as produce new and more sustainable products such as cements blended with sustainable supplementary cementitious materials such as calcined clays, and industrial or agricultural by products. At the same time the new variety of binding agent as well as the international imports, which are driven by price considerations, make the cement market prone to quality scatter. This puts pressure on the quality control regulations and institutions to ensure safety of construction, healthy application, and environmental safety for the population. The paper presents possible solutions to build up the rapidly increasing African cement production more sustainably than in the rest of the world as well as the related challenges and obstacles that need to be overcome. Based on experiences with a series of pan-African cement testing laboratory proficiency schemes conclusions are made on technical, regulative and political level.
The use of starch and its derivatives in concrete as an admixture to modify relevant properties of concrete is on the increase in recent times. It is known to modify the rheology, to affect the hydration kinetics of cement, and influence on initial and final setting time of cement. This paper examines the effect of cassava starch on concrete. shrinkage properties of concrete, with and without starch addition, were studied. Various percentages (0, 0.5, 1.0, 1.5 and 2 %) of starches by weight of cement were added to concrete mixes prepared in the laboratory. Shrinkage tests were conducted for duration of up to one year. The result show that concretes with starch additions exhibit lower shrinkage, which is an indication the addition of starch as admixture in concrete improves the ability of the concrete reduce shrinkage problems.
Chemical admixtures allow to create a variety of fresh and hardened state properties in cementitious materials. In the case of self-compacting concrete, plasticizers or superplasticizers are introduced with the aim to decrease the yield stress and the viscosity of the materials.
However, in order to prevent segregation and bleeding, and to improve the water retention of cement-based system, stabilizing agents or viscosity agents are often introduced in addition.
Among these admixtures, polysaccharides are most commonly used. The aim of this study is to provide an understanding of competitive or synergetic effects induced by the combination of hydroxypropyl guar stabilizing agents (HPG) and superplasticizers on cement pastes. Two polycarboxylate superplasticizers (PCE) exhibiting different charge densities and one HPG were studied. It was found that the combination of HPG with PCE superplasticizer strongly affects the rheological behavior of cement pastes. Despite the presence of HPG, the viscosity of the pastes strongly decreased with increasing dosage of PCE until it became close to the viscosity of a cement paste with PCE only. However, the use of HPG in combination with PCE allows maintaining a significant yield stress in the cement paste compared to PCE alone. The increase in the charge density of the PCE seemed to amplify the drop of the viscosity and to reduce the gain on the yield stress induced by HPG. The results also highlight a delay in the setting-time of the cement paste by adding HPG and PCE. The delay induced by HPG is significantly lower than that generated by PCEs. However, the combination of the both kind of admixtures leads to a slightly shorter setting-time compared to the PCE alone.
Chemical admixtures allow to the create a variety of fresh and hardened state properties in cementitious materials. In the case of self-compacting concrete, plasticizers or superplasticizers are introduced with the aim to decrease the yield stress and the viscosity of the materials. However, in order to prevent segregation and bleeding, and to improve the water retention of cement-based system, stabilizing agents or viscosity agents are often introduced in addition. Among these admixtures, polysaccharides are most commonly used.
The aim of this study is to provide an understanding of competitive or synergetic effects induced by the combination of hydroxypropyl guar stabilizing agents (HPG) and superplasticizers on cement pastes. Two polycarboxylate superplasticizers (PCE) exhibiting different charge densities and one HPG were studied. It was found that the combination of HPG with PCE superplasticizer strongly affects the rheological behavior of cement pastes. Despite the presence of HPG, the viscosity of the pastes strongly decreased with increasing dosage of PCE until it became close to the viscosity of a cement paste with PCE only. However, the use of HPG in combination with PCE allows maintaining a significant yield stress in the cement paste compared to PCE alone. The increase in the charge density of the PCE seemed to amplify the drop of the viscosity and to reduce the gain on the yield stress induced by HPG.
The results also highlight a delay in the setting-time of the cement paste by adding HPG and PCE. The delay induced by HPG is significantly lower than that generated by PCEs. However, the combination of the both kind of admixtures leads to a slightly shorter setting-time compared to the PCE alone.
As soon as cement is mixed with water, the hydration reaction starts to set of. The progression of the hydration process is governed by the amount and the availability of water and its possibility to access the unhydrated cement grain surfaces. For a total hydration cement theoretically requires water amounting approximately 0.38 of its own mass. Nevertheless, due to the cement’s highly hygroscopic nature, already the moisture in the ambient air can cause first hydration reactions to set in upon the cement grain surfaces. Such pre-hydration processes have an effect on the cement's properties. Dpending on the specific conditions during the storage the significance of the impact on certain properties can vary.
If cement is consumed soon after production and is transported only short distances in a silo wagon to its final destination for immediate use without further stock transfer, the effects are rather negligible. However, if cement is delivered in bags, transported over long distances, shifted serval times and stored for longer time periods until it is finally consumend, these effects can be quite severe. Due to the actual logistical situation with comparably few cement plants, large delivery distances and partially less developed infrastructures, the latter scenario pictures the situation for the most cases in Africa quite well.
In order to verify the relevance of the pre-hydation for practical application, a series of tests was conducted at the German Federal Institute for Materials Research and Testing (BAM). The influence of the cement storage on gresh and hardened concrete properties was investigated for different concrete and mortar types. The investigations show that the impact of the storage conditions is more pronounced for specialized concretes with high sophisticated optimized mixture compositions containing admixtures. Nevertheless, the effects also occur for ordinary concrete and should not be ignored.