Filtern
Erscheinungsjahr
Dokumenttyp
- Beitrag zu einem Tagungsband (83) (entfernen)
Referierte Publikation
- nein (83) (entfernen)
Schlagworte
- Rheology (23)
- Cement (21)
- Concrete (14)
- Superplasticizer (7)
- Admixtures (6)
- Africa (6)
- Polycarboxylate ether (6)
- Rheologie (6)
- Self-compacting concrete (6)
- Sustainability (6)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (20)
- 7.4 Baustofftechnologie (17)
- 6 Materialchemie (5)
- 6.6 Physik und chemische Analytik der Polymere (5)
- 7.0 Abteilungsleitung und andere (3)
- 1 Analytische Chemie; Referenzmaterialien (2)
- 1.2 Biophotonik (2)
- 8 Zerstörungsfreie Prüfung (2)
- 8.0 Abteilungsleitung und andere (2)
- 7.2 Ingenieurbau (1)
Organic/inorganic mixtures were prepared from ordinary Portland cement (OPC), water (w/c 0.22), a fluorescent dye in aqueous solution (stable at alkaline pH; BAM-I), and two different comb shape polycarboxylates (PCEs), i.e., high charge (PCE-HC) and low charge (PCE-LC), respectively. Rheological and calorimetric measurements were performed prior to optical studies in order to select PCE concentrations. Absorption and fluorescence spectroscopy of the system OPC + BAM-I (CBAM-I) revealed maxima of dye BAM-I located at 645 nm and 663 nm, respectively. In presence of PCE-HC and PCE-LC, these mixtures displayed a small red shift in reflectance and a faster decrease in intensity compared to studies with CBAM-I; however, only slight differences were observed between the different PCEs. With time, all systems exhibited a decrease in intensity of BAM-I in absorption/reflectance and emission. This could be caused by dye adsorption and possibly decomposition when in contact with cement particles or hydration products.
Organic/inorganic mixtures were prepared from ordinary Portland cement (OPC), water (w/c 0.22), a fluorescent dye in aqueous solution (stable at alkaline pH; BAM-I), and two different comb shape polycarboxylates (PCEs), i.e., high charge (PCE-HC) and low charge (PCE-LC), respectively. Rheological and calorimetric measurements were performed prior to optical studies in order to select PCE concentrations. Absorption and fluorescence spectroscopy of the system OPC + BAM-I (CBAM-I) revealed maxima of dye BAM-I located at 645 nm and 663 nm, respectively. In presence of PCE-HC and PCE-LC, these mixtures displayed a small red shift in reflectance and a faster decrease in intensity compared to studies with CBAM-I; however, only slight differences were observed between the different PCEs. With time, all systems exhibited a decrease in intensity of BAM-I in absorption/reflectance and emission. This could be caused by dye adsorption and possibly decomposition when in contact with cement particles or hydration products.
Todays superplasticizers for self-compacting concrete and high Performance cementitious materials are very versatile. Typically superplasticizers are composed of a polycarboxylic backbone equipped with polyethylene oxide graft chains of variable length and grafting degree. The mode of operation of these admixtures is based on the steric repulsion of the particles upon adsorption. The adsorption is strongly depending upon the charge density of a superplasticizer and the time dependent Adsorption processes control the retention of the flow performance – an important issue particularly for ready-mix and construction site concrete. However, the properties of polycarboxylic superplasticizers typically remain a black box for users. The paper suggests a simple and rapid test method, which can be conducted without sophisticated equipment, to qualitatively distinguish between two types of superplasticizers based on the adsorption mechanism. Interpreting the results in the right way provides a powerful tool to choose the right admixture for individual time dependent flow specifications.