Filtern
Erscheinungsjahr
Dokumenttyp
- Vortrag (32)
- Zeitschriftenartikel (15)
- Beitrag zu einem Tagungsband (11)
- Posterpräsentation (4)
- Forschungsbericht (1)
Schlagworte
- MAG-Schweißen (23)
- Wasserstoff (20)
- Hochfester Feinkornbaustahl (16)
- Hydrogen (10)
- Wärmeführung (9)
- Implant-Test (8)
- High-strength steel (7)
- Hochfeste Feinkornbaustähle (7)
- Welding (7)
- High-strength steels (6)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (32)
Neutron cameras allow visualizing hydrogen distributions with radiographic or tomographic imaging methods in iron (and steel) and many other metals. The necessary contrast between hydrogen and these metals stems from the high difference in the total neutron cross section of both elements. This allows, e.g., the in situ measurement of hydrogen mass flow inside cm thick metal samples with a temporal resolution of at best 10 s using neutron radiography as well as the quantitative measurement of hydrogen accumulations, e.g., at the crack’s inner surfaces in hydrogen embrittled iron samples with neutron tomography. This new quality of the information on a micrometer scale allows new insights for the analysis of hydrogen-assisted damage mechanisms. Further, this method is non-destructive and provides local information in situ and in three dimensions with a spatial resolution of 20 μm - 30 μm. In this contribution, we give a short historical overview of neutron imaging and show examples that demonstrate the spatial and temporal resolution of the neutron radiography and tomography methods in order to visualize and quantify hydrogen accumulations, absorption processes, and diffusion. The examples are taken from the works of researchers dealing with titanium, palladium, zirconium, and iron or steel. More detailed descriptions of the experimental and analytic procedures are given for hydrogen detection using radiography and tomography on iron and steel samples.
Höherfeste Feinkornbaustähle mit Streckgrenzen ≥ 690 MPa neigen bei der schweißtechnischen Fertigung zur Bildung von wasserstoffunterstützten Kaltrissen. Diese Mikrorisse entstehen aus der kritischen Interaktion von lokalem risskritischem Gefüge, lokal erhöhter Wasserstoffkonzentration und lokal erhöhter Beanspruchung bzw. Dehnung. Aktuell gültigen Regelwerken zur schweißtechnischen Verarbeitung höherfester Feinkornbaustähle sind Anweisungen zu entnehmen, um das Risiko einer Kaltrissbildung zu minimieren. Die Weiterentwicklung der Werkstoffe (Legierungskonzepte)und neuer Lichtbogenprozesse zur Verringerung der Nahtöffnungswinkel bei gleichzeitiger Erhöhung der Abschmelzleistung (modifizierter Sprühlichtbogen) brachten jedoch auch neue Fragen hinsichtlich der Wasserstoffmenge in der Schweißverbindung nach dem Schweißen und der Kaltrissempfindlichkeit mit sich. Mikrolegierungselemente (V, Nb und Ti) bedingen bspw. eine verlangsamte Wasserstoffdiffusion. Schweißverbindungen unter reduziertem Nahtöffnungswinkel beinhalten höhere Wasserstoffkonzentrationen. Dieser Beitrag zeigt den Einfluss von Einbrandprofil (höhere Abschmelzleistung) auf die Kaltrissempfindlichkeit an einem höherfesten Feinkornbaustahl mit artähnlichem mikrolegierten Schweißzusatzwerkstoff anhand des fremdbeanspruchten Implant-Tests.
Höherfeste Feinkornbaustähle mit Streckgrenzen ≥ 690 MPa neigen bei der schweißtechnischen Fertigung zur Bildung von wasserstoffunterstützten Kaltrissen. Diese Mikrorisse entstehen aus der kritischen Interaktion von lokalem risskritischem Gefüge, lokal erhöhter Wasserstoffkonzentration und lokal erhöhter Beanspruchung bzw. Dehnung. Aktuell gültigen Regelwerken zur schweißtechnischen Verarbeitung höherfester Feinkornbaustähle sind Anweisungen zu entnehmen, um das Risiko einer Kaltrissbildung zu minimieren. Die Weiterentwicklung der Werkstoffe (Legierungskonzepte) und neuer Lichtbogenprozesse zur Verringerung der Nahtöffnungswinkel bei gleichzeitiger Erhöhung der Abschmelzleistung (modifizierter Sprühlichtbogen) brachten jedoch auch neue Fragen hinsichtlich der Wasserstoffmenge in der Schweißverbindung nach dem Schweißen und der Kaltrissempfindlichkeit mit sich. Mikrolegierungselemente (V, Nb und Ti) bedingen bspw. eine verlangsamte Wasserstoffdiffusion. Schweißverbindungen unter reduziertem Nahtöffnungswinkel beinhalten höhere Wasserstoffkonzentrationen. Dieser Beitrag zeigt den Einfluss von Einbrandprofil (höhere Abschmelzleistung) auf die Kaltrissempfindlichkeit an einem höherfesten Feinkornbaustahl mit artähnlichem mikrolegierten Schweißzusatzwerkstoff anhand des fremdbeanspruchten Implant-Tests.
Das Schweißen hochfester Feinkornbaustähle mit modifizierten Sprühlichtbögen bietet die Möglichkeit, kleinere Nahtöffnungswinkel zu schweißen.
Allerdings findet der modifizierte Sprühlichtbogen in den Regelwerken zur schweißtechnischen Verarbeitung hochfester Feinkornbaustähle unter Vermeidung von Kaltrissbildung bisher keine Berücksichtigung. Dieser Beitrag betrachtet die Wechselwirkungen der Haupteinflussgrößen auf die Kaltrissbildung beim Schweißen mit kleineren Nahtöffnungswinkeln am Beispiel des hochfesten Stahls S960QL.
Effect of weld penetration depth on hydrogen-assisted cracking of high-strength structural steels
(2019)
The need for steels with highest mechanical properties is a result of the increasing demands for energy and resource efficiency. In this context, high-strength structural (HSS) steels are used in machine, steel and crane construction with yield strength up to 960 MPa. However, welding of HSS steels requires profound knowledge of three factors in terms of avoidance of hydrogen-assisted cracking (HAC): the interaction of (1) microstructure, (2) local stress/strain and (3) local hydrogen concentration. In addition to the three main factors, the used weld-arc process is also important for the performance of the welded joint, especially when using modern arc variants. In the past, the conventional transitional arc process (Conv. A) was mainly used for welding of HSS grades. In the past decade, the so-called modified spray arc process (Mod. SA) has been used increasingly for welding production. This modified process enables reduced seam opening angles with increased deposition rates compared to the conventional process. Economic benefits of using this arc type are: a reduced number of necessary weld beads and a lower weld seam volume, which result in decreased total welding time and costs. Nonetheless, investigations on a high-strength S960QL showed significantly higher hydrogen concentrations in the weld metal at a reduced seam opening angle with Mod. SA. This indicates an increased susceptibility of the welded component to HAC. Hence, existing recommendations on HAC-avoidance cannot be transferred directly to the Mod. SA-process. In the present study, the susceptibility to HAC of the HSS steel S960QL with same type of filler material was investigated. For that purpose, both Conv. A and Mod. SA were used with same heat input at different deposition rates. For assessment of the HAC susceptibility, the externally loaded implant test was used. Both conducted test series with Conv. A and Mod. SA showed similar crack critical stress of about 280 MPa. Below this value, no delayed fracture appeared. The welds with Mod. SA showed higher hydrogen concentrations. The fracture occurred in the heat-affected zone (HAZ) or in the weld metal (WM). However, the test series with Mod. SA showed a significant extension of the time to failure of several hours compared to tests carried out with Conv. A.
High-strength structural steels are used in machine, steel, and crane construction with yield strength up to 960 MPa. However, welding of these steels requires profound knowledge of three factors in terms of avoidance of hydrogen-assisted cracking (HAC): the interaction of microstructure, local stress/strain, and local hydrogen concentration. In addition to the three main factors, the used arc process is also important for the performance of the welded joint. In the past, the conventional transitional arc process (Conv. A) was mainly used for welding of high-strength steel grades. In the past decade, the so-called modified spray arc process (Mod. SA) has been increasingly used for welding production. This modified process enables reduced seam opening angles with increased deposition rates compared with the Conv. A. Economic benefits of using this arc type are a reduction of necessary weld beads and required filler material. In the present study, the susceptibility to HAC in the heat-affected zone (HAZ) of the high-strength structural steel S960QL was investigated with the externally loaded implant test. For that purpose, both Conv. A and Mod. SA were used with same heat input at different deposition rates. Both conducted test series showed same embrittlement index “EI” of 0.21 at diffusible hydrogen concentrations of 1.3 to 1.6 ml/100 g of arc weld metal. The fracture occurred in the HAZ or in the weld metal (WM). However, the test series withMod. SA showed a significant extension of the time to failure of several hours compared with tests carried out with Conv. A.
Kaltrissprüfung hochfester Feinkornbaustähle beim Schweißen mit modifiziertem Sprühlichtbogen
(2019)
Der konstruktive Leichtbau erfordert den zunehmenden Einsatz hochfester Feinkornbaustähle mit Streckgrenzen bis zu 1300 MPa. Um darüber hinaus Schweißzeit, Schweißnahtvolumina und Schweißkosten zu minimieren, kam es zur Entwicklung moderner Lichtbogenprozesse mit erhöhter Abschmelzleistung, wie bspw. dem modifizierten Sprühlichtbogen (mod. SLB). Dieser Beitrag zeigt Kaltrissuntersuchungen beim Einsatz des mod. SLB unter reduziertem Nahtöffnungswinkel eines Hochfesten S960QL. Mit Hilfe des fremdbeanspruchten Implant-Tests konnte dargelegt werden, dass durch die erhöhte Abschmelzleistung ein tieferes Einbrandprofil entsteht und es dadurch zu einer zeitverzögerten Rissbildung kommt. Ergebnisse des selbstbeanspruchenden TEKKEN-Tests zeigen eine deutliche Rissbildung im Schweißgut unter reduziertem Nahtöffnungswinkel. Durch eine Nachwärmung unmittelbar nach dem Schweißen kann diese Rissbildung minimiert werden.
Kaltrissprüfung hochfester Feinkornbaustähle beim Schweißen mit modifiziertem Sprühlichtbogen
(2019)
Sind in Stahlkonstruktionen hohe Tragfähigkeiten bei geringem Eigengewicht gefordert, finden hochfeste Feinkornbaustähle mit Streckgrenzen ≥ 960 MPa Anwendung. In der Vergangenheit wurde der konventionelle Übergangslichtbogen (Konv. LB) zur schweißtechnischen Fertigung von hochfesten Stählen eingesetzt. In den letzten Jahren wurde der modifizierte Sprühlichtbogen (Mod. SLB) entwickelt, welcher reduzierte Nahtöffnungswinkel bei erhöhter Abschmelzleistung ermöglicht. Jedoch treten höhere Wasserstoffkonzentrationen verbunden mit Mikro-(Kalt-)rissen unter reduziertem Nahtöffnungswinkel mit Mod. SLB auf. In diesem Beitrag wird die Kaltrissempfindlichkeit des hochfesten Feinkornbaustahles S960QL mit artgleichem Schweißzusatzwerkstoff untersucht.
Der Implant-Test nach ISO 17642-3 gehört zur Gruppe der fremdbeanspruchten Kaltrisstests, bei dem eine äußere Beanspruchung auf einen zylindrischen Stab (Implant-Probe) definiert aufgebracht wird. Mit dieser Kaltrissprüfung wurde vergleichende Analysen zur Kaltrissempfindlichkeit der modernen hochfesten Feinkornbaustähle S960MC und S960QL durchgeführt.
Um den wachsenden Anforderungen an den stofflichen und konstruktiven Leichtbau sowie den Forderungen nach Ressourceneffizienz Rechnung zu tragen, werden in vielen Industriebranchen zunehmend höherfeste Feinkornbaustähle mit Streckgrenzen ≥ 690 MPa eingesetzt. Allerdings werden mit zunehmender Festigkeit deutlich höhere Anforderungen an deren schweißtechnische Verarbeitung gestellt, da gerade die Sensibilität gegenüber einer Degradation der mechanischen Eigenschaften, durch den beim Schweißen aufgenommenen Wasserstoff, mit steigender Festigkeit stark zunimmt. In der vorliegenden Arbeit erfolgten vergleichende Untersuchungen mit konventionellem Übergangslichtbogen und modifiziertem Sprühlichtbogen mit reduziertem Nahtöffnungswinkel hinsichtlich der Wasserstoffaufnahme beim Schweißen unter Variation von Streckenenergie, Arbeitstemperatur und Nachwärmprozedur. Grundsätzlich ist den erarbeiteten Ergebnissen zu entnehmen, dass im Schweißgut von Stumpfstoßverbindungen mit reduziertem Nahtöffnungswinkel erhöhte mittlere Wasserstoffkonzentrationen vorliegen. Geeignete Wärmeführungen führten zu einer signifikanten Reduzierung der Wasserstoffkonzentration beim Einsatz der Nahtkonfiguration mit abgesenktem Nahtöffnungswinkel. Dabei erwies sich eine Nachwärmprozedur aus der Schweißwärme heraus als zielführend.