The flame retardancy of poly(butylene terephthalate) (PBT) containing aluminium diethlyphosphinate (AlPi) and/or nanometric metal oxides such as TiO2 or Al2O3 was investigated. In particular the different active flame retardancy mechanisms were discovered. Thermal analysis, evolved gas analysis (TG-FTIR), flammability tests (LOI, UL 94), cone calorimeter measurements and chemical analyses of residues (ATR-FTIR) were used. AlPi acts mainly in the gas phase through the release of diethylphosphic acid, which provides flame inhibition. Part of AlPi remains in the solid phase reacting with the PBT to phosphinate-terephthalate salts that decompose to aluminium phosphate at higher temperatures. The metal oxides interact with the PBT decomposition and promote the formation of additional stable carbonaceous char in the condensed phase. A combination of metal oxides and AlPi gains the better classification in the UL 94 test thanks to the combination of the different mechanisms.
Basic paths towards fully green flame retarded kenaf fiber reinforced polylactic acid (K-PLA) biocomposites are compared. Multicomponent flame retardant Systems are investigated using an amount of 20 wt% such as Mg(OH)2 (MH), ammonium polyphosphate (APP) and expandable graphite (EG), and combinations with Silicon dioxide or layered silicate (LS) nanofillers. Adding Kenaf fibers and flame retardants increases the E modulus up to a factor 2, although no compatibilizer was used at all. Thus, in particular adding EG and MH decreases the strength at maximum elongation, and kenaf fibers, MH, and EG are crucial for reducing the elongation to break. The Oxygen index is improved by up to 33 vol% compared to 17 vol% for K-PLA. The HB classification of K-PLA in the UL 94 test is outperformed. All flame retarded biocomposites show somewhat lower thermal stability and increased amounts of residue. MH decreases the fire load significantly, and the greatest reduction in peak heat release rate is obtained for K-PLA/15MH/5LS. Synergistic effects are observed between EG and APP (ratio 2:1) in flammability and fire properties. Synergistic multicomponent systems containing EG and APP, or MH with adjuvants offer a promising route to green flame retarded natural fiber reinforced PLA biocomposites.
The recently approved EU Construction Products Regulation (CPR) applies to cables as construction products.
The difficulty of predicting the fire performance of cables with respect to propagation of flame and contribution to fire hazards is well known. The new standard EN 50399 describes a full-scale test method for the classification of vertically mounted bunched cables according to CPR. Consideration of the material, time, and thus cost requires an alternative bench-scale fire test, which finds strong demand for Screening and development purposes. The development of such a bench-scale fire test to assess the fire Performance of multiple vertically mounted cables is described. A practical module for the cone calorimeter is proposed, simulating the fire scenario of the EN 50399 on the bench scale. The efficacy of this module in predicting full-scale CPR test results is shown for a set of 20 different optical cables. Key properties such as peak heat release rate (PHRR), fire growth rate (FIGRA), and flame spread are linked to each other by factors of around 5. In a case study, the bench-scale test designed was used to investigate the influence of the main components on the fire behaviour of a complex optical cable.