Poly(allyl alcohol) films with a thickness of about 150 nm were deposited by pulse plasma polymerization onto different substrates (inorganic and organic). The structure/property relationships of these samples were studied in dependence on the duty cycle (DC) of the plasma by a broad combination of different techniques and probes. For the first time volume sensitive methods (FTIR and dielectric spectroscopy) are combined with surface analytics by employing XPS for that system. FTIR spectroscopy gives qualitatively the same dependence of the concentration of the OH groups on DC like XPS.
The observed differences are discussed considering the different analytical depths of both the methods. The dielectric measurements show that the plasma deposited films are not thermally stable but undergo a post plasma chemical reaction during heating. The results obtained by dielectric spectroscopy are discussed in detail with the data from FTIR and XPS measurements.
Thin poly(acrylic acid) PAA films were deposited by pulsed plasma polymerization on different organic and inorganic substrates. The structureproperty relationships of the deposited acrylic acid polymers were studied in dependence on the monomer pressure by various techniques and probes. The surface and bulk properties of the plasma deposited films were investigated by X-ray photoelectron spectroscopy, attenuated total reflection infrared, and broad band dielectric spectroscopy. The experimental infrared frequencies of PAA films are compared with those predicted from quantum mechanical calculation. The concentration of the COOH groups in the film (stored in ambient air) decreased by about 15 % compared to the as-prepared sample. The plasma deposited PAA probably form a highly branched product. However, the dielectric measurements show that in addition to the hydrogen bonds, self condensation process was able to hinder the localized fluctuation as well. These processes lead to form a cross-linked network polymer film. Nevertheless, a low energy is sufficient to break these processes during heating at atmospheric pressure. Therefore, homogenized samples with free branches (functional group) were obtained after a first heating with structures close to conventional polymerized acrylic acid. Thus, a thermally stable product was obtained.
Polystyrene (PS) spin coated thin films were modified by O2 and Ar plasma as
well as by UV irradiation treatments. The modified PS samples were compared with
plasma polymerized and commercial polystyrene. The effects of plasma (O2 and Ar) and
UV irradiation treatments on the surface and the bulk properties of the polymer layers were
discussed. The surface properties were evaluated by X-ray Photoelectron Spectroscopy and
Contact angle measurements and the bulk properties were investigated by FTIR and
dielectric relaxation spectroscopy. As a result only one second treatment time was sufficient
to modify the surface. However, this study was also dedicated to understand the effect
of plasma and plasma irradiation on the deposited layers of plasma polymers. The
dielectric measurements showed that the plasma deposited films were not thermally stable
and underwent an undesired post-plasma chemical oxidation.
In contrast to most of the existing literature on plasma polymerization of acrylic acid (AA), not only the chemical structure and film thickness of the deposits were studied, but also a new way to obtain COOH-rich surfaces. This is an important aspect when applying the obtained coatings for biomedical and electronics applications. Therefore, acrylic acid/CO2 polymer films with a thickness of ca. 150 nm were deposited in the pulsed plasma regime onto polyethylene and aluminium as organic and inorganic substrates. Their structure–property relationships were studied in dependence on the mixture ratio of acrylic acid monomer and CO2 gas. The influence of the CO2 gas on the regularity and functionality of plasma deposited poly(acrylic acid) (PAA) was studied in detail using bulk-sensitive (dielectric spectroscopy and Fourier transforms infrared spectroscopy) as well as surface-sensitive methods such as X-ray photoelectron spectroscopy. For a clear identification of the functionality of the deposited films, the COOH groups were estimated after derivatization with trifluoroethanol by XPS measurement as well as by the quantitative analysis of the FTIR data. Results show, in presence of a small amount of CO2 gas within the acrylic acid plasma, a structure of poly(acrylic acid) with high concentration of COOH groups was obtained. However, the excess of CO2 gas in the plasma chamber leads to fragmentation of the monomer or/and degradation of the layer which is already deposited. A polymer network is obtained with an increasing abundance of branched groups for AA/CO2 with increasing CO2 gas in the mixture.
Copolymers of acrylic acid and styrene (AA/S) were prepared by pulsed plasma deposition technique. Their structure–property relationships were studied in dependence on the comonomer ratio. Both, the regularity of the structure and the composition of the thin copolymer films were investigated by bulk-sensitive (dielectric spectroscopy, FTIR, and differential scanning calorimetry) as well as surface-sensitive methods such as X-ray photoelectron spectroscopy (XPS). For an unambiguous identification of the functionality of the deposited films the COOH groups were estimated by derivatization with trifluoroethanol and subsequent XPS measurement as well as by the quantitative analysis of the FTIR data. As a result, the concentration of COOH groups on the surface and in the bulk is increasing with the fraction of AA in precursor mixture in a non-monotonous way but similar to the dependence obtained by conventional free radical polymerization.