Self-compacting concrete typically contains a higher content of powder materials than normal concrete. Furthermore it is assumed that the use of superplasticizers yields a more homogenous microstructure in the hardened paste. Both aspects generate a very dense microstructure, which can be assumed to cause material behaviour that differs from than normal concrete when it is exposed to elevated temperatures. However, the paste volumes in SCC can vary significantly based on the mixture composition. At a low paste volumes SCC can be very similar to normal concrete at hardened state while it can vary greatly at higher paste volumes. Since the high temperature behaviour of concrete is strongly affected by the different physical behaviour of the paste and the aggregates, it is likely that the high temperature behaviour is consequently strongly affected by the ratio of these mixture components. In the present study different SCC mixtures were observed with similar mechanical properties, but with significantly differing paste to aggregate ratios. Based on observations of the heat evolution at the fire exposed surface and at different depths inside the specimens as well as based on photogrammetric observations of the spalled dimensions, the results indicate that with increasing paste volumes the heat conductivity is reduced and as a result concrete with higher paste to aggregate ratios shows less spalling.
Polysaccharides are important rheology modifying admixtures in the building material sector.
The use of starch is becoming increasingly important, due to many ecological and economic advantages. In the construction sector, starch ethers are being used as thickeners and as means to increase the yield stress. The starch ethers that are available on the market differ in
their behaviour, which can vary greatly depending upon the binder system and mortar composition, e.g. solid volume content, binder type, additional admixtures. In view of the limited knowledge about the influence of molecular modifications associated with cement based systems, some fundamental rheological functional mechanisms were analysed in this study. The differently modified starch ethers used were derived from potatoes. They varied in their charges and degrees of hydroxypropylation. The setting and the flow behaviour of all examined variations
of starch ethers were analysed in cement pastes. In order to illustrate the effects of the starch ethers that were used, the water-cement ratio (w/c) was held constant in all the mixtures [Schmidt 2012]. The results indicated significant differences in setting and flow behaviour.
In der aktuellen Projektphase liegt der Fokus auf der Datenaufnahme, -bearbeitung und -speiche-rung mit dem Ziel, automatisierte Auswerteverfahren einsetzen zu können. Aktuell wurden primär punktuelle Messungen an ausgewählten Messtagen aufgenommen. Die Systeme sollen so weiter-entwickelt werden, dass sie sich auch für kontinuierliche Messungen im Rahmen von Monitoring-aufgaben eignen.
Ein wichtiger Fokus bei der Auswertung ist die Kombination mit numerischen Modellen, die mithilfe von Bayesian Update Verfahren und den aufgenommenen Messdaten kalibriert und im Verlauf der Monitoringaufgabe angepasst werden sollen. Insbesondere sollen auch zeitabhängige Modelle, die eine zeitliche Entwicklung von Struktureigenschaften beinhalten (Kriechen, Schwinden, Ermüdung, Korrosion) dazu verwendet werden, die zukünftige Performance der Struktur bewerten zu können. Basierend darauf werden dann Konzepte zur Planung von Inspektion und Wartung erstellt.
Unter zyklischen Belastungen findet im Beton, wie bei anderen Materialien auch, ein Ermüdungsprozess statt, der letztlich im Versagen des Materials enden kann. Im derzeitigen Erkenntnisstand zum Materialverhalten des Betons gibt es gerade bei dessen Ermüdungsverhalten noch viele nicht oder nicht ausreichend geklärte Fragestellungen. Deshalb wurde in Laborversuchen das Ermüdungsverhalten von Beton unter Druckschwellbeanspruchungen untersucht. Im Fokus dieser Untersuchungen standen dabei die während der Lebensdauer im Materialgefüge ablaufenden Prozesse, die zur Schädigung des Gefüges und schließlich auch zum Ermüdungsversagen führen können.
In den Ermüdungsversuchen wurden versuchsbegleitend Dehnungsmessungen, Ultraschall-Laufzeitmessungen und Schallemissionsmessungen an den Proben zur Erfassung der Schädigungsevolution eingesetzt. Die Schallemissionsmessung ist dabei ein wichtiges Instrument, da sie die Rissentwicklungsprozesse detektiert, die die Ursache für die Materialschädigung sind. Mit ihr konnten die unterschiedlichen Phasen der Rissentwicklungen über die gesamte Lebensdauer der Betonproben festgestellt werden. Diese Phasen sind gekennzeichnet durch sich stabilisierende, stabile und instabile Rissprozesse, die entsprechende Auswirkungen auf das Materialverhalten haben. Ein Vergleich mit den Ergebnissen der anderen Messtechniken zeigt den entsprechenden Einfluss der Rissentwicklungen auf die Materialeigenschaften des Betons.
Fatigue is of relevance not only for metals but also for concrete. The current knowledge about fatigue behaviour of concrete is, however, incomplete. This concerns especially the progress of fatigue which precedes the fatigue failure. Some macroscopic effects of this process are well known but the governing material changes behind them are still less studied. The focus of the present contribution lay on a systematic and comprehensive investigation of the fatigue process under cyclic compressive loading. The aim was to obtain a deeper insight and to provide a better understanding of the damage process in the material. Cylindrical specimens were tested with a number of cycles to failure between 106 and 107. Various methods of non-destructive and destructive testing were used to investigate macroscopic and microscopic changes in the material. One main result was that the changes in the macroscopic material behaviour could not be explained only by the development of micro cracks. The results indicated that the related changes in the fatigue behaviour originate rather from viscous processes in the cement stone, similar to the process of creep. A sound description of the possible processes was derived from the obtained experimental results which concerns material structure during fatigue loading. It has been shown that in case of isotropic material behaviour a stiffness reduction related to a scalar value could not capture the damage effect on the stress-strain relationship caused by fatigue.
The current knowledge about fatigue behavior of concrete is still incomplete. This concerns especially the progress of fatigue which precedes the fatigue failure. Therefore, the process of fatigue itself under cyclic compressive loading was investigated in a systematic and comprehensive way. The aim of this investigation was to obtain a deeper insight and to provide a better understanding of the damage process occurring within the material during fatigue loading. Concrete cylinders were tested with a number of cycles to failure between 106 and 107. To investigate macroscopic and microscopic changes in the material, various methods of non-destructive and destructive testing were used. One main result was, in contrast to other authors, that the investigated changes in macroscopic material behavior could not be explained only by a development of micro-cracks. The results indicated rather, that the related changes in the fatigue behavior are mainly a result of viscous processes in the hardened cement paste, similar to the processes of creep. Based on the experimental results a description of the possible processes was derived which take place in the material structure during fatigue loading and also leads to the observed macroscopic changes in the material behavior. In this context, the results have shown that in case of isotropic material behavior a stiffness reduction related to a scalar value could not capture the damage effect on the stress-strain-relationship caused by fatigue.
The current knowledge about fatigue behavior of concrete is still incomplete. This concerns especially the progress of fatigue which precedes the fatigue failure. Therefore, the process of fatigue itself under cyclic compressive loading was investigated in a systematic and comprehensive way. The aim of this investigation was to obtain a deeper insight and to provide a better understanding of the damage process occurring within the material during fatigue loading. Concrete cylinders were tested with a number of cycles to failure between 106 and 107. To investigate macroscopic and microscopic changes in the material, various methods of non-destructive and destructive testing were used. One main result was, in contrast to other authors, that the investigated changes in macroscopic material behavior could not be explained only by a development of micro-cracks. The results indicated rather, that the related changes in the fatigue behavior are mainly a result of viscous processes in the hardened cement paste, similar to the processes of creep. Based on the experimental results a description of the possible processes was derived which take place in the material structure during fatigue loading and also leads to the observed macroscopic changes in the material behavior. In this context, the results have shown that in case of isotropic material behavior a stiffness reduction related to a scalar value could not capture the damage effect on the stress-strain-relationship caused by fatigue.
Unter zyklischen Belastungen findet im Beton, wie bei anderen Materialien auch, ein Ermüdungsprozess statt. Im derzeitigen Erkenntnisstand zum Materialverhalten des heterogenen Betons gibt es gerade bei dessen Ermüdungsverhalten momentan noch viele nicht oder nicht ausreichend geklärte Fragestellungen. Deshalb befasst sich der vorliegende Beitrag mit der experimentellen Untersuchung des Ermüdungsverhaltens von Beton, speziell unter hochzyklischen Druckschwellbelastungen. Im Fokus der Untersuchungen stehen dabei die während der gesamten Lebensdauer im Materialgefüge ablaufenden Prozesse, die zu Veränderungen im Materialverhalten und schließlich auch bis zum Ermüdungsversagen führen können. Ziel ist es, eine möglichst realitätsnahe Beschreibung des im Materialgefüge ablaufenden Ermüdungsprozesses zu entwickeln.
A novel method for risk-based optimization of inspection and repair strategies for deteriorating structural systems has recently been proposed. The method defines heuristics at the system level to reduce the number of possible strategies. For each defined strategy, it computes the updated system failure probability conditional on simulated inspection and repair histories, and evaluates the associated costs and risk. The expected total service life costs and risk for a strategy are finally determined using Monte Carlo simulation. The optimal strategy minimizes the expected total service life costs and risk. We intend to adopt this approach to optimize inspection, monitoring and repair activities for offshore wind park support structures. As a first step, we simulate – in analogy to an offshore wind park – the service life performance of an inspected group of jacket-type frames. The performance is quantified in terms of the group’s system failure probability conditional on simulated inspection and repair histories. The underlying system model accounts for the structural redundancy of the frames and the interdependence among their failure events due to similar loading conditions. The model also captures stochastic dependence among the deterioration states of the frames. As part of the simulation process the a-priori unknown outcome of any planned inspection is generated conditional on the outcome of all previous inspections.
Identifying optimal inspection and repair strategies for offshore jacket structures is a challenging task. We pre-sent an approach, which is based on recent developments in the field of risk-based operation and maintenance planning at the structural system level. The approach utilizes heuristics to define inspection and repair strate-gies at the system level and to reduce the search space of possible strategies. For each defined strategy, the expected service life cost of inspection, repair and failure is evaluated based on simulated inspection and re-pair histories. Subset simulation is applied to compute the conditional repair and failure probabilities required for this analysis. It also forms the basis for simulating inspection and repair histories. The strategy that mini-mizes the expected service life cost is the optimal one in the set of pre-selected strategies. The underlying condition and performance model accounts for the stochastic dependence among the deterioration states of the different structural elements and the structural redundancy. The approach is demonstrated in a case study considering a jacket-type frame. In this study, we essentially vary the inspection interval, the minimum num-ber of inspected components and the target reliability, and identify the combination that minimizes the ex-pected total service life cost.