Schlagworte
- Inconel 718 (2)
- Lightweight concepts (2)
- Resistance spot welding (2)
- Ti-6Al-4V (2)
- Widerstandspunktschweißen (2)
- laser welding (2)
- 316L (1)
- 3D-FE-Simulation (1)
- 3DDruck (1)
- AHSS (1)
Eingeladener Vortrag
- nein (4)
Heat treated 9%Ni steel is considered the most suitable and economic material for construction of large-size liquefied natural gas (LNG) storage tanks which operate at cryogenic temperatures (-196°C). Strength above 700 MPa as well as a minimum impact value of 60 J are required to ensure reliable operation of the LNG tanks at operating temperature. Conventional arc welding processes, including shielded metal arc welding, gas metal arc welding, gas tungsten arc welding and submerged arc welding, are currently used in construction of LNG tanks. Ni based filler wire is the preferred filler metal of choice in LNG tank construction. The main problem with this choice is the lower mechanical properties, particularly tensile strength of the weld metal. To compensate, the wall thickness needs to be excessively thick to ensure the strength of the welded structures. Ni based filler material is expensive and a large quantity is needed to fill the multi-pass weld grooves. These factors significantly add to the cost in the fabrication of LNG storage tanks. For these reasons, exploration of new welding technologies is a priority. A big potential can be seen in laser based welding techniques. Laser beam welding results in much smaller fusion zone with chemical composition and mechanical properties similar to that of the base material. Laser welding is a much faster process and allows for a joint geometry which requires less filler material and fewer welding passes. The advantages of laser welding can help to overcome the problems pointed out above. Trials of autogenous laser welding, laser cold-wire welding and hybrid laser-arc welding conducted on the 9%Ni steel are presented in this paper. Chemical composition of the weld metal as well as effects of welding parameters on the weld formation, microstructure and tensile strength is discussed. Filler wire penetration depth as well as character of its distribution in the narrow laser welds was examined using EPMA - electron probe microanalysis.
Die stetig zunehmenden Anforderungen an Kraftstoffverbrauch, Schadstoffemission, sowie passive Sicherheit haben die Automobilindustrie vor Herausforderungen gestellt, die nur durch einen konsequenten Einsatz moderner hochfester Stahlwerkstoffe zu bewältigen sind. Obgleich eine generelle Eignung dieser Stähle für das Widerstandspunktschweißen (WPS) gegeben ist, kann es durch verschiedene externe Einflüsse im betrieblichen Umfeld zur Rissbildung in der Schweißverbindung kommen. Der Einfluss dieser Risse auf die mechanischen Eigenschaften ist derzeit nicht hinreichend genau erfasst, so dass häufig die Vorgabe einer rissfreien Schweißverbindung besteht. Die Kenntnis der Rissanfälligkeit der verarbeiteten Materialkombinationen sowie von ungünstigen Schweißparametern ist daher für viele Unternehmen von erheblicher wirtschaftlicher Bedeutung. Im Rahmen des FOSTA Projekts P921 „Entwicklung eines Verfahrens zur Bestimmung der Rissanfälligkeit von hochfesten Stählen beim Widerstandspunktschweißen“ wurde ein Ansatz zur Bestimmung der Rissanfälligkeit von WPS-Verbindungen hochfester Stähle entwickelt. Mittels einer hydraulischen Vorrichtung unter Zugbelastung wurden geschweißte, rissbehaftete Proben optisch ausgewertet. Das Verfahren ist geeignet, um ein Werkstoffranking bezüglich der Rissanfälligkeit beim Widerstandspunktschweißen für Werkstoffe aufzustellen.
The complex microstructure and the advanced mechanical properties of AHSS steel types lead to an increased susceptibility to weld cracking, especially during resistance spot welding under ‘rough’ manufacturing conditions.
Various activities have been conducted in recent years at the Federal Institute for Materials Research and Testing (BAM) and the Fraunhofer IPK on this matter. Understandings about the safe spot weldability and the process of crack-forming itself were gained, and solutions for handling this issue given.
The performed work includes investigations on the influence of initial gaps as well as restraint intensity. An experimental method for the determination of the general cracking susceptibility, i.e. a material ranking of AHSS in respective to current restraints was developed. Coupled mechanical and thermal simulations of the welding process show the present internal stress-strain-conditions and values responsible for the formation of cracks, deepening the understanding of the process.
By using this easy to perform and material-independent method for the determination of the cracking susceptibility in resistance spot welded joints, small and medium sized companies can profit by rapidly evaluating the joinability of their handled material combinations as well as OEMs.
Manganese alloyed stainless steels represent a cost-effective alternative to conventional CrNi- stainless steels due to strong fl uctuations of the market prices for nickel seen during the last years. In CrMnNi steels, nickel is partially replaced by lower-cost manganese and small amounts of nitrogen for stabilization of the austenitic phase. This also brings benefi ts regarding the mechanical properties, as it results in an increased material strength. Laser beam welding of such materials was investigated for direct comparison with Standard CrNi steels. Main emphasis was laid on fi nding adequate process parameters to achieve a stable welding process and obtain a good weld quality. Two different laser sources, a 4.4 kW Nd:YAG and a 5 kW CO2 laser, were used to weld 1.5 mm stainless steel sheets in continuous wave mode. A high-Mn austenitic (1.4376) and a lean duplex (1.4162) steel, as well as the standard austenitic (1.4301) and duplex (1.4362) grades were selected as test materials. Both butt and lap joint confi gurations were studied. Experiments were carried out systematically, varying the welding speed, laser power and focal point position in order to determine adequate process windows. The infl uence of the shielding gas type and fl ow rate on the process stability and the weld quality were investigated. The effects of weld edge preparation on the weld appearance and quality levels attained were also examined. The obtained welded joints were subjected to radiographic tests for detection of internal imperfections. Also a metallurgical characterization of the samples regarding the resulting phase composition or balance and hardness depending on the welding process parameters was conducted. Furthermore, tensile and potentiodynamic tests were performed to evaluate the mechanical and corrosion properties, respectively. The results provide an insight into the advantages and limitations of the laser beam welding process for joining high-manganese alloyed stainless steels. Conditions for the production of defect-free and corrosion-resistant welds having good mechanical properties could be determined.
Die in dieser Studie vorgestellte einfache Probengeometrie zeigt sich in Verbindung mit der
angewandten Versuchs- und Auswertemethodik geeignet, um den umwandlungsplastischen (TRIP)-Parameter K unter Verwendung des thermomechanischen Simulators Gleeble® 3500 experimentell zu bestimmen.
Der TRIP-Parameter K wurde für die Grundwerkstoffe S355J2+N und S960QL, sowie für den hochlegierten Zusatzwerkstoff CN13-4 -IG bestimmt.
Die numerische Einflussanalyse zeigt, dass bei der Berechnung von (Oberflächen-)Schweißeigen-spannungen die Vernachlässigung des TRIP-Effektes kaum einen Einfluss auf die Längseigenspannungen hat. Im Gegensatz da zu resultieren gegenüber dem Referenzfall signifikante Abweichungen der
Quereigenspannungen im und um den Schweißnahtbereich.
Die Verdopplung des TRIP-Parameters K gegenüber dem Referenzfall hat nur einen vernachlässigbaren Einfluss auf die Längs- sowie Quereigenspannungen auf der Oberfläche.
Für eine qualitative und quantitative numerische Nachbildung der experimentell bestimmten Längs- und Quereigenspannungen ist die Berücksichtigung der Größenordnung des material-abhängigen TRIP-Parameters K notwendig.
In dieser Studie wurde die Heißrissanfälligkeit beim Laserstrahlschweißen für die Werkstoffe 1.4376, 1.4301 und 1.4828 mit Hilfe des CTW Test quantifiziert. Bei den Versuchen konnten Erstarrungsrisse in den Proben generiert werden. Zusätzlich können mit der Bildkorrelations-Technik die lokalen Dehnungen und Dehnungsraten während des Heißrisstests gemessen wer den. In Verbindung mit einem externen Diodenlaser zum Beleuchten der zu messende Oberfläche und lnterferenzfiltern an den Kameras konnten die DIC Messungen ohne optische Störungen durchgeführt werden.
Die Ergebnisse zeigen, dass die Heißrissbildung bei einer externen Belastung von 3 % für die Stahlsorte 1.4376 zu erwarten ist. Für die Stahls orte 1.4301 beträgt dieser Grenzwert 2 % und 1,5 % für die Stahlgüte 1.4828. Außerdem ist zu beobachten, dass die Gesamtrisslänge mit zu nehmender äußerer Zugbeanspruchung steigt
•Main Welding Technologies in the Automotive: RSW and laserbeam welding
•Light Weight Design leads to increasing use of AHSS and UHSS which results in higher demands for the joining technology
•Joining Multi-Material Structures offers opportunities for “new” Thermal-Mechanical Joining Processes and Hybrid Processes
•In the coming years a trend towards sustainable manufacturing can be seen. Comparison between laserbeam and RSW will be a tight match!
High power laser welding technology has made a large progress in the last decade and established itself in different industrial applications;
Hybrid laser arc welding is one of the most prospective technologies for heavy components assembling;
Modern high speed video observation, in situ x-ray screening as well as simulation techniques contributed to better understanding of laser welding process;
New approaches e.g. application of electromagnetic fields for melt pool control and welding at reduced pressure ambient have significantly contributed to extending the process boundaries far beyond the known Limits.
The influence of two different weld imperfections (gap/crack) on the fatigue behaviour of spot welded joints was tested
Surface cracks have no influence on the fatigue life
Samples with cracks in the electrode indentation /HAZ where tested
Stiffness curves are not significantly influenced by surface cracks
3D FE-Simulation demonstrate no changes of stress due to surface imperfections
•
Welding under external forces was found suitable for characterizing AHSS materials
New quick and easy-to-perform procedure for establishing a material ranking regarding cracking susceptibility
Metal additive manufacturing is often based on laser beam processes like Laser Metal Fusion (LMF) or Laser Metal Deposition (LMD). The LMF process is in particular suitable for very complex geometries. However build rate, part volume and material flexibility are limited in LMF. In contrast, LMD achieves higher deposition rates, less restricted part sizes and the possibility to change the material composition during the build-up process. On the other hand, due to the lower spatial precision of the material deposition process, the complexity of geometries is limited. Therefore, combined manufacturing with both LMF and LMD has the potential to utilize the respective advantages of both technologies.
In this paper, combined additive manufacturing with LMF and LMD is described for Ti-6Al-4V and Inconel 718. First, lattice structures with different wall thickness and void sizes are built with LMF. The influence of LMD material deposition on these LMF-structures is examined regarding metallurgical impact and distortion. Cross-sections, x-ray computer tomography and 3D-scanning results are shown.
For the titanium alloy specimen, oxygen and Nitrogen content in the deposited material are analysed to evaluate the LMD shielding gas atmosphere. The results are used to develop guidelines for a LMD build-up strategy on LMF substrates. With these findings, a gas turbine burner is manufactured as reality test for the combined approach.