The safety evaluation of cask components made of ductile cast iron includes investigations to prevent brittle fracture. Generally, ductile cast iron is endangered by brittle fracture especially at low temperatures (down to -40°C) and in combination with existing crack-like material defects. An applicable method is the assessment of fracture resistance using fracture mechanics according to the IAEA guidelines. The approach is based on the prevention of fracture initiation. For application of these principles for drop loads, account must be taken both of dynamic stresses within the component and dynamic material behavior. Basically, the dynamic stress intensity factor of postulated pre-existing crack-like defects is compared with the dynamic fracture toughness of the material. Applicable numerical and experimental methods for the safety assessment of cask components are demonstrated for the case of an artificially pre-cracked cylindrical cast iron cask which undergoes dynamic loading conditions as result of the hard impact between the cask and a concrete target. The proposed evaluation procedure is a combination of numerical and experimental steps. Exemplarily, the calculated stress intensity factor is compared with measured fracture toughness values from single edge notched bending specimens.
Compared with the original time-temperature superposition (TTS) principle, an extended non-linear time-temperature equivalent (TTE) principle is suggested in this work. Results shown us, all application of TTS and most of the TTE parameters, for example, the Orr-Sherby-Dorn, Manson-Succop, Larson-Müller, Manson-Haferd, Mendelson-Roberts-Manson parameters and the more general ‘single metamodel’ from Haque–Stewart are special cases of the new suggested principle. The merits of this new method are discussed.
The long-term sealing behavior of metal seals, assembled in the lid system of casks for transportation and storage of radioactive materials, has been investigated. For that purpose, phenomenological models describing the time- and temperature dependent behavior have been introduced by BAM since 2016, e.g. by using the time-temperature superposition principle. Results have shown that these models describe the relaxation behavior adequately and are suitable for extrapolations. In this work, the applicability of these models is checked by analyzing the necessary scope of tests, which must be carried out to get sufficient information about the long-term behavior of metal seals based on short-term tests.
Three-dimensional finite element analysis of O-ring metal seals considering manufacture tolerances
(2019)
Metal seals are widely used in various industrial branches with severe working conditions (e.g. high pressure, high temperature, corrosion, or radioactive radiation). For example, O-ring metal seals are applied in the closure lid system of transport and storage casks for radioactive materials to guarantee an approved specified leak-tightness and the safe enclosure of the radioactive inventory. Within safety assessments of those casks under normal or accident conditions during transport and long-term interim storage for several decades, numerical simulations of the thermo-mechanical behavior of metal seals by using finite element (FE) analyses are suitable and effective.
In general, finite element codes provide the possibility to construct a complex three-dimensional (3D) modelling of metal seals with solid elements, cf., where all components of the metal seals are modeled in detail. This modelling is complex but allows the consideration of underlying physical effects such as elastic-plastic deformation, thermal expansion, creep/relaxation, friction and possible local damage. Therefore, this approach permits the investigation and understanding of the complex behavior of metal seals in detail which can hardly be measured for all seal components.
In a prior work, the complex 3D modelling approach was applied to investigate the influence of each seal component on the global seal force by considering varying material properties and different seal diameters. In the present contribution, the influence of manufacturing tolerances is discussed. At first, the results of prior work are summarized. After that, the manufacturing tolerances of the studied O-ring metal seal types are described and the corresponding FE model with all individual components is introduced. Finally, the influence of varying manufacturing tolerances of each seal component on the global seal force is analyzed and discussed.