Filtern
Erscheinungsjahr
- 2019 (4) (entfernen)
Dokumenttyp
- Vortrag (4) (entfernen)
Referierte Publikation
- nein (4)
Schlagworte
- Biodiesel (2)
- FAME (2)
- Heizöl (2)
- ACM (1)
- Beständigkeit (1)
- Beständigkeitsbewertung (1)
- Beständigkeitsbewertungen (1)
- Biogene Brennstoffe (1)
- Compatibility (1)
- Corrosion (1)
- Elastomere (1)
- FKM (1)
- HNBR (1)
- HVO (1)
- Heating oil (1)
- Heizöl mit 20 % Biodiesel (1)
- Heizöl-FAME-Blends (1)
- Metallene Werkstoffe (1)
- Metals (1)
- PUR (1)
- Polymere (1)
- RME (1)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (4)
Für Bauteile (Komponenten) von Versorgungsanlagen für flüssige Brenn- und Kraftstoffe muss die Beständigkeit der metallenen Werkstoffe und Polymere nachgewiesen werden. Im Anwendungsfall von Heizöl mit 20 % biogenen Anteilen in Form von Rapsölfettsäuremethylester (FAME, Biodiesel) ist es für eine konservative Beurteilung des Korrosionssystems Werkstoff/Medium/Umgebung wichtig, die Alterungseffekte des Mediums einzubeziehen.
Entwicklung eines Prüfverfahrens für die Untersuchung der Beständigkeit von metallenen Werkstoffen und Polymeren in Heizöl und Heizöl-FAME-Blends, das für eine Vorauswahl der Werkstoffe und zum Nachweis der Beständigkeit im Hinblick auf die bauaufsichtlichen Zulassungsverfahren geeignet ist. Ein Schwerpunkt wird bei den metallenen Werkstoffen auf der Erprobung von Messmethoden liegen, mit denen sich in kurzer Versuchszeit ein Korrosionsangriff detektieren lässt.
Metallene Werkstoffe:
Weder örtliche Korrosion noch erhöhte Flächenkorrosion (Korrosionsrate:< 0,1 m/Jahr) sind bei den bisher geprüften Werkstoffen: Aluminium,
C-Stahl 1.0037, austenitischer CrNi-Stahl 1.4301, Kupfer und Messing in Heizöl und B20 (Heizöl mit 20% Biodiesel) aufgetreten. Diese Werkstoffe sind in den Prüfmedien Heizöl und B20 als beständig zu bewerten.
Es wurde keine signifikante Veränderung des pH-Wertes der Prüfmedien gemessen.
Polymere:
Massebestimmung:
Die Prüfkörper der Elastomere ACM, HNBR und PUR sowie in geringerem Maße PE neigten zur Quellung in Heizöl und B20 nach 42 d und 84 d Auslagerung; für PA 6, POM und PVC wurde keine Masseänderung gemessen. Die Masseänderung der Prüfkörper in Heizöl und B20 ist mit Ausnahme von PUR vergleichbar. Bei PE traten Verfärbungen durch die Brennstoffe auf.
Zugeigenschaften:
ACM, HNBR, PE und PVC sind in Heizöl und B20 beständig, da die Änderung der Zugfestigkeit und der Reißdehnung < 15 % beträgt. PA und POM sind bedingt beständig, da die Änderung der Zugfestigkeit und der Reißdehnung < 30% beträgt.
Für Bauteile (Komponenten) von Versorgungsanlagen für flüssige Brenn- und Kraftstoffe muss die Beständigkeit der metallenen Werkstoffe und Polymere nachgewiesen werden. Im Anwendungsfall von Heizöl mit 20 % biogenen Anteilen in Form von Rapsölfettsäuremethylester (FAME, Biodiesel) ist es für eine konservative Beurteilung des Korrosionssystems Werkstoff/Medium/Umgebung wichtig, die Alterungseffekte des Mediums einzubeziehen.
Entwicklung eines Prüfverfahrens für die Untersuchung der Beständigkeit von metallenen Werkstoffen und Polymeren in Heizöl und Heizöl-FAME-Blends, das für eine Vorauswahl der Werkstoffe und zum Nachweis der Beständigkeit im Hinblick auf die bauaufsichtlichen Zulassungsverfahren geeignet ist.
In Europe biodiesel gained from rapeseeds are considered as an alternative to common fossil fuels due to its environmental performance and its independence from import of raw materials. Biodiesel is also suitable to serve as blending component to heating oil. In that case, it must be considered that changes of fuel composition might cause material degradation.
The objective of this research was to investigate the resistance of metallic materials exposed to heating oil, heating oil blend B20 with 20 % biodiesel and pure biodiesel. Furthermore, the resistance of metals to eight-year aged B10 and six-year aged pure biodiesel was evaluated. Ageing of biodiesel forms acids and water which might propagate metal corrosion. The investigated metals (aluminium, unalloyed steel, austenitic CrNi-steel, copper, die cast zinc and brass) are commonly used for components in middle distillate facilities.
According to DIN 50905-4 the immersed metals were exposed in a climate chamber at 50°C for 4 weeks. The metallic materials were evaluated as resistant if the annual corrosion rate due to uniform corrosion remained under 0.1 mm/year and no localized corrosion in the form of pitting occurred.
The corrosion rates of the exposed materials stayed far below the limit of 0.1 mm/year for all tested fuels. An exception was die cast zinc ZP0410 in eight-year aged B10; a corrosion rate up to 0.3 mm/year due to uniform corrosion was measured. In no case localized corrosion occurred. Copper and brass caused discolouration of biodiesel from yellow to green.
In conclusion, the tested metallic materials were resistant in heating oil, heating oil blend B20 and pure biodiesel at 50 °C. Even the metals exposed to six-year aged biodiesel and eight-year aged B10 showed no uniform or localized corrosion; except for zinc, which was not resistant in eight-year aged B10.
Aus Rapsöl gewonnener Biodiesel ist eine umweltfreundliche Alternative zu fossilen Energiequellen. In der Europäischen Union, in der 80 % der ölhaltigen Brennstoffe importiert werden müssen, besteht zudem ein Interesse, die Abhängigkeit von exter-nen Ölversorgern zu reduzieren.
Bei jeder Veränderung der Zusammensetzung eines Brennstoffs muss auch die Ma-terialverträglichkeit gewährleistet bleiben. Es stellt sich die Frage, ob Elastomere im Vergleich zu reinem Heizöl auch in Heizöl mit 20 % Biodiesel (B20) beständig sind.
Die Polarität des Biodiesels erhöht die Quellung und fördert die Permeation und Ex-traktion. Sowohl Quellung als auch Extraktion bedingen Änderungen der physikali-schen Eigenschaften der Elastomere. Extraktion verändert die chemische des Heiz-öls. Diese chemischen Veränderungen können auch den Abbau (Hydrolyse und Oxi-dation) der Polymere durch das Herauslösen von Additiven und Stabilisatoren be-schleunigen.
Ziel dieser Arbeit war die Bestimmung der Beständigkeit der Elastomere ACM (Poly-acrylatkautschuk), HNBR (Hydrierter Acrylnitrilbutadienkautschuk), FKM (Fluorkaut-schuk) und PUR (Polyurethan) in Heizöl und im Heizölgemisch B20.
Prüfkörper der Elastomere wurden für 42 Tage (Härteprüfung) und 84 Tage (Zugprü-fung) bei 40 °C ausgelagert. Anschließend wurde die Änderung der Masse, Shore Härte A, Zugfestigkeit, und Reißdehnung bezogen auf die Werte vor der Aus-lagerung bestimmt. Die weniger zur Quellung neigenden Elastomere FKM und HNBR wurden zusätzlich bei 70 °C ausgelagert.
Um die Elastomere im verpressten Zustand zu testen, wurde der Druckverformungs-rest nach DIN ISO 815 bestimmt. Hierzu wurden zylindrische Prüfkörper aus ACM, HNBR und FKM verpresst und in Heizöl und Heizöl mit 20 % FAME für 3, 7, 14, 28, 56 und 90 Tage bei 40 °C ausgelagert. Anschließend wurde über die Dickenmes-sung der Druckverformungsrest ermittelt. Zum Vergleich wurden Prüfkörper verpresst und ohne Medium bei 40 °C ausgelagert.
In den internationalen Normen wurde kein Grenzwert für die Veränderung der Zugei-genschaften und der Härte für eine positive Bewertung der Beständigkeit festgelegt. Deshalb wurde in der BAM ein Grenzwert von 15 % für die Beständigkeitsbewertung herangezogen.
Bei 40 °C lag die Änderung der Zugeigenschaften und der Shore Härte von ACM, HNBR und FKM in Heizöl und in B20 unter 15 %. Folglich sind ACM, HNBR und FKM bei 40 °C in Heizöl und in B20 beständig. PUR ist bei 40 °C in Heizöl beständig, je-doch nicht für eine Verwendung in B20 geeignet, da sich die Zugfestigkeit und Reiß-dehnung um 50 % vermindert haben.
Bei 70 °C ist FKM in Heizöl und B20 beständig, wohingegen HNBR an seine Einsatz-grenzen gelangt und unbeständig ist, in B20 haben sich die Zugfestigkeit um 40 % und die Reißdehnung um 50 % reduziert.